Mge3Lie0.4Zr alloys containing RE elements(Gd,La,Nd)(Mge3LieREe0.4Zr alloys)are investigated to reveal the influence of homogenization treatment on microstructures and distributions of RE,Zr elements.It is found that...Mge3Lie0.4Zr alloys containing RE elements(Gd,La,Nd)(Mge3LieREe0.4Zr alloys)are investigated to reveal the influence of homogenization treatment on microstructures and distributions of RE,Zr elements.It is found that 300C24 h homogenization treatment shows better improvement on the microstructure including the refinement of grain size,the dispersion of cellular dendrite and low melting point particles.Before treatment,La and Nd segregate effectively at grain boundary and Zr segregates in the form of precipitates.Homogenization treatment induces the reduction of RE segregation.However,the segregation of Zr in precipitates cannot be abated due to the relatively low diffusion rate compared with RE elements.展开更多
基金This work was supported by the Major State Basic Research Development Program of China(No.2013CB632203)National Key Technology R&D Program of China(2011BAE22B03)+3 种基金(2012BAF09B01)National Natural Science Foundation of China(51074207)Chinese Postdoctoral Science Foundation(2012M520634)the Fundamental Research Foundation of Central Universities(Grant Nos.N120509002 and N120309003).
文摘Mge3Lie0.4Zr alloys containing RE elements(Gd,La,Nd)(Mge3LieREe0.4Zr alloys)are investigated to reveal the influence of homogenization treatment on microstructures and distributions of RE,Zr elements.It is found that 300C24 h homogenization treatment shows better improvement on the microstructure including the refinement of grain size,the dispersion of cellular dendrite and low melting point particles.Before treatment,La and Nd segregate effectively at grain boundary and Zr segregates in the form of precipitates.Homogenization treatment induces the reduction of RE segregation.However,the segregation of Zr in precipitates cannot be abated due to the relatively low diffusion rate compared with RE elements.