In recent years, more and more high Al2O3 iron ores were used in East Asia, especially in China, which increased the Al2O3 content in blast furnace (BF) slag and resulted in poor metallurgical properties of slag. Addi...In recent years, more and more high Al2O3 iron ores were used in East Asia, especially in China, which increased the Al2O3 content in blast furnace (BF) slag and resulted in poor metallurgical properties of slag. Adding MgO-bearing flux is one of the methods to improve the metallurgical properties of slag with high Al2O3. However, there is lack of theoretical basis for the proper MgO/Al2O3 ratio. Therefore, the properties of slag in SiO2-CaO-MgO-Al2O3 system were investigated based on viscosity experiments and phase diagram analyses at 1500℃, and the proper MgO/Al2O3 ratio was explored according to the Al2O3 content in slag. The experimental results show that: (1) in the case of Al2O3 content less than 14mass%, there is no limitation of the MgO/Al2O3 ratio, and the amount of MgO in slag can be determined according to the hearth tempera-ture and desulfurization;(2) in the case of Al2O3 content between 15 and 17mass%, the proper MgO/Al2O3 ratio should be 0.40-0.50;(3) in the case of Al2O3 content between 18 and 20mass%, the proper MgO/Al2O3 ratio should be 0.45-0.55. Consequently, the three-segment control theory of MgO/Al2O3 for BF slag was built, and the actual BF performances proved the validity and applicability of this theory. The research contents and results can give theoretical guidelines for stable BF operation in a wide range of Al2O3 content of 12-20mass%.展开更多
The supersaturated solution of MgO· 3B2O3 18% MgSO4 H2O was prepared and then reacted under hydrothermal condition at 120℃ . The solid phases of the different time were identified by means of chemical analysis, ...The supersaturated solution of MgO· 3B2O3 18% MgSO4 H2O was prepared and then reacted under hydrothermal condition at 120℃ . The solid phases of the different time were identified by means of chemical analysis, XRD, FT IR, SEM. The results show that the solid phases are spherical and sheet szaibelyite, which is different from those of non hydrothermal condition. On these grounds we suggested the crystallization mechanism of szaibelyite under the hydrothermal condition and then discussed the effects of hydrothermal properties on the crystallization mechanism.展开更多
基金The financial supports of National Natural Science Foundation of China(NSFC 51874080,NSFC 51774071,and NSFC 51974073)Natural Science Foundation of Liaoning(2019-MS-132)are much appreciated.
文摘In recent years, more and more high Al2O3 iron ores were used in East Asia, especially in China, which increased the Al2O3 content in blast furnace (BF) slag and resulted in poor metallurgical properties of slag. Adding MgO-bearing flux is one of the methods to improve the metallurgical properties of slag with high Al2O3. However, there is lack of theoretical basis for the proper MgO/Al2O3 ratio. Therefore, the properties of slag in SiO2-CaO-MgO-Al2O3 system were investigated based on viscosity experiments and phase diagram analyses at 1500℃, and the proper MgO/Al2O3 ratio was explored according to the Al2O3 content in slag. The experimental results show that: (1) in the case of Al2O3 content less than 14mass%, there is no limitation of the MgO/Al2O3 ratio, and the amount of MgO in slag can be determined according to the hearth tempera-ture and desulfurization;(2) in the case of Al2O3 content between 15 and 17mass%, the proper MgO/Al2O3 ratio should be 0.40-0.50;(3) in the case of Al2O3 content between 18 and 20mass%, the proper MgO/Al2O3 ratio should be 0.45-0.55. Consequently, the three-segment control theory of MgO/Al2O3 for BF slag was built, and the actual BF performances proved the validity and applicability of this theory. The research contents and results can give theoretical guidelines for stable BF operation in a wide range of Al2O3 content of 12-20mass%.
文摘The supersaturated solution of MgO· 3B2O3 18% MgSO4 H2O was prepared and then reacted under hydrothermal condition at 120℃ . The solid phases of the different time were identified by means of chemical analysis, XRD, FT IR, SEM. The results show that the solid phases are spherical and sheet szaibelyite, which is different from those of non hydrothermal condition. On these grounds we suggested the crystallization mechanism of szaibelyite under the hydrothermal condition and then discussed the effects of hydrothermal properties on the crystallization mechanism.