Surface tension of calcium aluminate refining slag was measured by the Slide method at 1823 K.Based on different levels of the MgO content and the mass ratio of CaO to Al_2O_3,the effects of MgO content and the mass r...Surface tension of calcium aluminate refining slag was measured by the Slide method at 1823 K.Based on different levels of the MgO content and the mass ratio of CaO to Al_2O_3,the effects of MgO content and the mass ratio of CaO to Al_2O_3 on surface tension were investigated.The results indicate that surface tension decreased with increasing MgO content(from 0 to 4.86%),followed by an increase with further increasing MgO content up to 11.33%.The trend that surface tension changed with the mass ratio of CaO to Al_2O_3 was the same as the trend that surface tension changed with the MgO content.The surface tension was varied from 0.617 N/m to 0.710 N/m,for the mass ratio of CaO to Al_2O_3 varying between 0.60 and 1.28.An attempt was made to estimate surface tension of CaO-Al_2O_3-MgO slag and its sub-system,and the application showed that the model worked well.展开更多
The influence of MgO content in slag on wetting and corrosion behavior between slag and MgO–C refractory was investigated.It can be known from the high-temperature wetting experiment that as the MgO content in the sl...The influence of MgO content in slag on wetting and corrosion behavior between slag and MgO–C refractory was investigated.It can be known from the high-temperature wetting experiment that as the MgO content in the slag increases,the final contact angle between the slag and the MgO–C refractory gradually increases and the penetration depth of the slag into the refractory gradually decreases from 60.54μm(when the MgO content is 8%)to 28.11μm(when the MgO content is 12%).The CaO and SiO_(2)in the slag penetrate into the MgO–C refractory along the pores or surface cracks formed by carbon oxidation and react with MgO to generate a large amount of low-melting compound CaO–MgO–SiO_(2),which accelerates the corrosion of the refractory.As the MgO content in slag increases,the viscosity of the slag increases and the fluidity becomes worse,so that the mass transfer and diffusion of molecules or ions in the slag are weakened.In addition,the increase in MgO reduces the activity of FeO in the slag,which inhibits the interfacial chemical reaction,thereby weakening the wetting effect caused by the reaction.展开更多
1 Scope This standard specifies the classification, technical requirements, test methods, inspection rules, marking, packing, transportation, and storage of magnesia bricks for glass furnace.
Activities of FeO in CaO-SiO2-Al2O3-MgO-FeO slags were determined at 1673 K by electrochemical of the solid electrolyte cell： Mo [Mo＋MoOu[ZrO2（MgO）[Fe＋（CaO-SiO2-Al2O3-MgO-FeO）＋Ag[Fe. The influences of slag com...Activities of FeO in CaO-SiO2-Al2O3-MgO-FeO slags were determined at 1673 K by electrochemical of the solid electrolyte cell： Mo [Mo＋MoOu[ZrO2（MgO）[Fe＋（CaO-SiO2-Al2O3-MgO-FeO）＋Ag[Fe. The influences of slag compositions and basicity on FeO activities were analyzed. The results reveal that, for slags of fixed （%CaO）/（%SiO2） ratio, MgO and Al2O3 content, there was an increase of FeO activities with increase of FeO content. For slags with constant {（%CaO）＋ （%MgO）}/（%SiO2） ratio, fixed FeO and A1203 content, FeO activities decreased when MgO content increased from 5% to 10%, and increased with the increase of MgO content when it was over 10%. The FeO activities increased when （%CaO）/（%SiO2） ratio changed from 1.03 to 1.30 in the slags of constant MgO, FeO and Al2O3 content.展开更多
基金Project(51204115)supported by the National Natural Science Foundation of ChinaProject(BK20130308)supported by the Basic Research Program of Jiangsu Province,ChinaProject(2014M561710)supported by China Postdoctoral Science Foundation
文摘Surface tension of calcium aluminate refining slag was measured by the Slide method at 1823 K.Based on different levels of the MgO content and the mass ratio of CaO to Al_2O_3,the effects of MgO content and the mass ratio of CaO to Al_2O_3 on surface tension were investigated.The results indicate that surface tension decreased with increasing MgO content(from 0 to 4.86%),followed by an increase with further increasing MgO content up to 11.33%.The trend that surface tension changed with the mass ratio of CaO to Al_2O_3 was the same as the trend that surface tension changed with the MgO content.The surface tension was varied from 0.617 N/m to 0.710 N/m,for the mass ratio of CaO to Al_2O_3 varying between 0.60 and 1.28.An attempt was made to estimate surface tension of CaO-Al_2O_3-MgO slag and its sub-system,and the application showed that the model worked well.
基金This work was financially supported by the National Natural Science Foundation of China(Grant Nos.51874171 and 51974154)supported by University of Science and Technology Liaoning talents program(601009840-09).
文摘The influence of MgO content in slag on wetting and corrosion behavior between slag and MgO–C refractory was investigated.It can be known from the high-temperature wetting experiment that as the MgO content in the slag increases,the final contact angle between the slag and the MgO–C refractory gradually increases and the penetration depth of the slag into the refractory gradually decreases from 60.54μm(when the MgO content is 8%)to 28.11μm(when the MgO content is 12%).The CaO and SiO_(2)in the slag penetrate into the MgO–C refractory along the pores or surface cracks formed by carbon oxidation and react with MgO to generate a large amount of low-melting compound CaO–MgO–SiO_(2),which accelerates the corrosion of the refractory.As the MgO content in slag increases,the viscosity of the slag increases and the fluidity becomes worse,so that the mass transfer and diffusion of molecules or ions in the slag are weakened.In addition,the increase in MgO reduces the activity of FeO in the slag,which inhibits the interfacial chemical reaction,thereby weakening the wetting effect caused by the reaction.
文摘1 Scope This standard specifies the classification, technical requirements, test methods, inspection rules, marking, packing, transportation, and storage of magnesia bricks for glass furnace.
基金Project supported by the National Natural Science Foundation of China （Grant No.50574036）
文摘Activities of FeO in CaO-SiO2-Al2O3-MgO-FeO slags were determined at 1673 K by electrochemical of the solid electrolyte cell： Mo [Mo＋MoOu[ZrO2（MgO）[Fe＋（CaO-SiO2-Al2O3-MgO-FeO）＋Ag[Fe. The influences of slag compositions and basicity on FeO activities were analyzed. The results reveal that, for slags of fixed （%CaO）/（%SiO2） ratio, MgO and Al2O3 content, there was an increase of FeO activities with increase of FeO content. For slags with constant {（%CaO）＋ （%MgO）}/（%SiO2） ratio, fixed FeO and A1203 content, FeO activities decreased when MgO content increased from 5% to 10%, and increased with the increase of MgO content when it was over 10%. The FeO activities increased when （%CaO）/（%SiO2） ratio changed from 1.03 to 1.30 in the slags of constant MgO, FeO and Al2O3 content.