Dual-layer thermal barrier coatings(TBCs)with ultrahigh temperature resistance were prepared on the surface of molybdenum-rhenium alloy hot-end components.The preparation of the MoSi_(2)-Gd_(2)Zr_(2)O_(7)dual-layer TB...Dual-layer thermal barrier coatings(TBCs)with ultrahigh temperature resistance were prepared on the surface of molybdenum-rhenium alloy hot-end components.The preparation of the MoSi_(2)-Gd_(2)Zr_(2)O_(7)dual-layer TBCs was designed based on the coefficient of thermal expansion and the coating functionality,and it was completed using atmospheric plasma spraying technique.The microstructure,mechanical properties,and thermal properties were analyzed.Results indicate that the adhesion of the prepared dual-layer composite TBCs is excellent,and no noticeable cracks appear at the interface.Compared with the MoSi_(2)coating with a low fracture toughness(0.88 MPa·m^(1/2)),the Gd_(2)Zr_(2)O_(7)coating exhibits higher fracture toughness(1.74 MPa·m^(1/2))and stronger resistance to crack propagation.The prepared MoSi_(2)-Gd_(2)Zr_(2)O_(7)composite coatings have a high porosity(39%),low thermal conductivity(1.020 W·(m·K)^(−1),1200℃),and low thermal diffusivity(0.249 mm^(2)/s,1200℃).Additionally,they possess a high oxygen-vacancy concentration,which ensures excellent insulation performance.展开更多
TiB_(2)coatings can significantly enhance the high-temperature oxidation resistance of molybdenum,which would broaden the application range of molybdenum and alloys thereof.However,traditional methods for preparing Ti...TiB_(2)coatings can significantly enhance the high-temperature oxidation resistance of molybdenum,which would broaden the application range of molybdenum and alloys thereof.However,traditional methods for preparing TiB_(2)coatings have disadvantages such as high equipment costs,complicated processes,and highly toxic gas emissions.This paper proposes an environmentally friendly method,which requires inexpensive equipment and simple processing,for preparing TiB_(2)coating on molybdenum via electrophoretic deposition within Na3AlF6-based molten salts.The produced TiB_(2)layer had an approximate thickness of 60μm and exhibited high density,outstanding hardness(38.2 GPa)and robust adhesion strength(51 N).Additionally,high-temperature oxidation experiments revealed that,at900℃,the TiB_(2)coating provided effective protection to the molybdenum substrate against oxidation for 3 h.This result indicates that the TiB_(2)coating prepared on molybdenum using molten salt electrophoretic deposition possesses good high-temperature oxidation resistance.展开更多
基金Supported by Scientific and Technological Innovation of Shaanxi Provincial State-Owned Capital Operation Budget(2022-056)Institute's Self-Developed Technology Program(0801YK2317)+4 种基金Qin Chuangyuan Cites High-Level Innovation and Entrepreneurship Talent Program(QCYRCXM-2023-120)Qin Chuangyuan Industry Cluster Zone“Four Chains”Integration Program(2024CY-JJQ-46)National Natural Science Foundation of China(52071274)Key Research and Development Projects of Shaanxi Province(2023-YBGY-442)Science and Technology Nova Project-Innovative Talent Promotion Program of Shaanxi Province(2020KJXX-062)。
文摘Dual-layer thermal barrier coatings(TBCs)with ultrahigh temperature resistance were prepared on the surface of molybdenum-rhenium alloy hot-end components.The preparation of the MoSi_(2)-Gd_(2)Zr_(2)O_(7)dual-layer TBCs was designed based on the coefficient of thermal expansion and the coating functionality,and it was completed using atmospheric plasma spraying technique.The microstructure,mechanical properties,and thermal properties were analyzed.Results indicate that the adhesion of the prepared dual-layer composite TBCs is excellent,and no noticeable cracks appear at the interface.Compared with the MoSi_(2)coating with a low fracture toughness(0.88 MPa·m^(1/2)),the Gd_(2)Zr_(2)O_(7)coating exhibits higher fracture toughness(1.74 MPa·m^(1/2))and stronger resistance to crack propagation.The prepared MoSi_(2)-Gd_(2)Zr_(2)O_(7)composite coatings have a high porosity(39%),low thermal conductivity(1.020 W·(m·K)^(−1),1200℃),and low thermal diffusivity(0.249 mm^(2)/s,1200℃).Additionally,they possess a high oxygen-vacancy concentration,which ensures excellent insulation performance.
基金supported by the Original Exploratory Program of the National Natural Science Foundation of China(No.52450012)。
文摘TiB_(2)coatings can significantly enhance the high-temperature oxidation resistance of molybdenum,which would broaden the application range of molybdenum and alloys thereof.However,traditional methods for preparing TiB_(2)coatings have disadvantages such as high equipment costs,complicated processes,and highly toxic gas emissions.This paper proposes an environmentally friendly method,which requires inexpensive equipment and simple processing,for preparing TiB_(2)coating on molybdenum via electrophoretic deposition within Na3AlF6-based molten salts.The produced TiB_(2)layer had an approximate thickness of 60μm and exhibited high density,outstanding hardness(38.2 GPa)and robust adhesion strength(51 N).Additionally,high-temperature oxidation experiments revealed that,at900℃,the TiB_(2)coating provided effective protection to the molybdenum substrate against oxidation for 3 h.This result indicates that the TiB_(2)coating prepared on molybdenum using molten salt electrophoretic deposition possesses good high-temperature oxidation resistance.