Electrocodeposition of Mg-Li-Sm alloys was investigated in molten KCl-LiCl-MgCl2-SmCl3-KF system.The effects of electrolytic temperature and cathodic current density on current efficiency were studied and optimal elec...Electrocodeposition of Mg-Li-Sm alloys was investigated in molten KCl-LiCl-MgCl2-SmCl3-KF system.The effects of electrolytic temperature and cathodic current density on current efficiency were studied and optimal electrolysis parameters were obtained.The optimum electrolysis condition was a molten salt mixture of LiCl:KCl =50:50(wt.%),electrolytic temperature:660 oC,cathode current density:9.5 A/cm2 and electrolysis time of 40 min.The current efficiency reached 77.3%.X-ray diffraction(XRD) and scanning elec...展开更多
Different phases of Mg-Li-Sm alloys were prepared by galvanostatic electrolysis in LiCl-KCl-MgCl2-SmCl3 melts at 670 °C.The electrolysis process and phase control of Mg-Li-Sm alloys were studied.The microstructur...Different phases of Mg-Li-Sm alloys were prepared by galvanostatic electrolysis in LiCl-KCl-MgCl2-SmCl3 melts at 670 °C.The electrolysis process and phase control of Mg-Li-Sm alloys were studied.The microstructures of α,α+β,β phases of Mg-Li-Sm alloys were characterized by X-ray diffraction(XRD) and optical microscope(OM).Analysis of scanning electron microscopy(SEM) and EDS mapping analysis showed that Mg distributed homogeneously in Mg-Li-Sm alloys.EDS result showed that the distribution of Sm was more at...展开更多
基金supported by 863 project of Ministry of Science and Technology of China (2006AA03Z510)the National Natural Science Foundation of China (50871033)
文摘Electrocodeposition of Mg-Li-Sm alloys was investigated in molten KCl-LiCl-MgCl2-SmCl3-KF system.The effects of electrolytic temperature and cathodic current density on current efficiency were studied and optimal electrolysis parameters were obtained.The optimum electrolysis condition was a molten salt mixture of LiCl:KCl =50:50(wt.%),electrolytic temperature:660 oC,cathode current density:9.5 A/cm2 and electrolysis time of 40 min.The current efficiency reached 77.3%.X-ray diffraction(XRD) and scanning elec...
基金supported by 863 project of Ministry of Science and Technology of China (2006AA03Z510)the National Natural Science Foundation of China (50871033)
文摘Different phases of Mg-Li-Sm alloys were prepared by galvanostatic electrolysis in LiCl-KCl-MgCl2-SmCl3 melts at 670 °C.The electrolysis process and phase control of Mg-Li-Sm alloys were studied.The microstructures of α,α+β,β phases of Mg-Li-Sm alloys were characterized by X-ray diffraction(XRD) and optical microscope(OM).Analysis of scanning electron microscopy(SEM) and EDS mapping analysis showed that Mg distributed homogeneously in Mg-Li-Sm alloys.EDS result showed that the distribution of Sm was more at...