A novel core-shell structured Al_(8)Mn_(4)Y-Al_(2)Ca phase and controllable solute-segregation are elaborately designed in dilute Mg-0.6Al-0.5Mn-0.1Ca-0.1Y alloy(wt.%),via incomplete peritectic transformation during t...A novel core-shell structured Al_(8)Mn_(4)Y-Al_(2)Ca phase and controllable solute-segregation are elaborately designed in dilute Mg-0.6Al-0.5Mn-0.1Ca-0.1Y alloy(wt.%),via incomplete peritectic transformation during twin-roll casting.When soaked in 3.5 wt.%NaCl solution,Al_(2)Ca shell with a low electrochemical potential prevents direct contact of noble Al_(8)Mn_(4)Y with Mg matrix,mitigating the micro-galvanic corrosion and meanwhile accelerating the formation of uniform corrosion film.Thereafter,solute(Al,Ca)-segregation motivates the formation of heterogeneous multilayered corrosion product films,enhancing corrosion resistance and even achieving self-healing upon long-term corrosion.Notably,the dilute Mg alloy exhibits a corrosion rate as low as 0.22±0.05 mm·y^(−1).展开更多
基金supported by National Natural Science Foundation of China under Grant Nos.52234009 and 52274383Partial financial support came from the Fundamental Research Funds for the Central Universities,JLU,Program for JLU Science and Technology Innovative Research Team(JLUSTIRT,2017TD-09)Program for the Central University Youth Innovation Team.
文摘A novel core-shell structured Al_(8)Mn_(4)Y-Al_(2)Ca phase and controllable solute-segregation are elaborately designed in dilute Mg-0.6Al-0.5Mn-0.1Ca-0.1Y alloy(wt.%),via incomplete peritectic transformation during twin-roll casting.When soaked in 3.5 wt.%NaCl solution,Al_(2)Ca shell with a low electrochemical potential prevents direct contact of noble Al_(8)Mn_(4)Y with Mg matrix,mitigating the micro-galvanic corrosion and meanwhile accelerating the formation of uniform corrosion film.Thereafter,solute(Al,Ca)-segregation motivates the formation of heterogeneous multilayered corrosion product films,enhancing corrosion resistance and even achieving self-healing upon long-term corrosion.Notably,the dilute Mg alloy exhibits a corrosion rate as low as 0.22±0.05 mm·y^(−1).