RE-containing Mg alloys used as biodegradable medical implants exhibit good promising application due to their good mechanical properties and degradation resistance. In this work, effect of Gd on the microstructure, m...RE-containing Mg alloys used as biodegradable medical implants exhibit good promising application due to their good mechanical properties and degradation resistance. In this work, effect of Gd on the microstructure, mechanical properties and biodegradation of as-cast Mg-2Zn-xGd-0.5Zr alloys was investigated. The results showed that there were mainly α-Mg, I-phase, W-phase and MgZn2 phase in Mg-Zn-Gd-Zr alloys. With increase of the Gd content, the strength of the alloys was enhanced due to the second phase strengthening and grain refinement. The degradation resistance of Mg-2Zn-0.5Zr alloy was increased by adding 0.5%–1% Gd due to the uniformly distributed second phases which acted as a barrier to prevent the pitting corrosion. However, increasing Gd content to 2% reduced the degradation resistance of the alloy due to the galvanic corrosion between the matrix and the second phases.The good degradation resistance and mechanical properties of as-cast Mg-2Zn-1Gd-0.5Zr alloy makes it outstanding for biomaterial application.展开更多
Multi-pass hot processing methods are commonly used in magnesium(Mg)alloys to overcome the poor workability due to limited slip systems,which generally involve complicated post-deformation softening and hardening beha...Multi-pass hot processing methods are commonly used in magnesium(Mg)alloys to overcome the poor workability due to limited slip systems,which generally involve complicated post-deformation softening and hardening behaviors.In this work,to reveal post-deformation softening and hardening mechanisms of a Mg-2Y-1Zn alloy,double-stage hot compression tests and microstructural observations were conducted.The results showed that the softening fraction of Mg-2Y-1Zn alloy showed a non-linear dependence on deformation conditions and could be general coupled by Z parameter.Due to the formation and cross-overlapping of twins and kinks,only static recovery(SRV)occurred during holding process at 300℃/0.001 s^(-1) which led to the least static softening:5.52% after 10 s of holding.For samples at 400℃/0.001s^(-1),the enhanced post-deformation softening,which is 11.93% after 10 s of holding,was attributed to static recrystallization(SRX)followed continuous dynamic recrystallization(CDRX)happened during first deformation stage as well as SRV influenced by the LPSO phases.Under deformation condition of 400℃/0.1 s^(-1),the coupled meta-dynamic recrystallization(MDRX)and SRX resulted in serious stress relaxation,which is 42.83% after 10 s of holding,and caused hardening phenomenon at reloading stage.The 18R-LPSO and 14H-LPSO phases synchronously worked on deformation behaviors and limited the growth of recrystallized grains.Further,a simplified static softening kinetics model was established based on Johnson-Mehl-Avrami-Kolmogorov equation and employed to rationalize experimental data.展开更多
基金supported by the Key Program of China on Biomedical Materials Research and Tissue and Organ Replacement (Nos.2016YFC1101804,2016YFC1100604)Institute of Metal Research,Chinese Academy of Sciences (No.2015-ZD01)the Foundation of Jiangsu Collaborative Innovation Center of Biomedical Functional Materials
文摘RE-containing Mg alloys used as biodegradable medical implants exhibit good promising application due to their good mechanical properties and degradation resistance. In this work, effect of Gd on the microstructure, mechanical properties and biodegradation of as-cast Mg-2Zn-xGd-0.5Zr alloys was investigated. The results showed that there were mainly α-Mg, I-phase, W-phase and MgZn2 phase in Mg-Zn-Gd-Zr alloys. With increase of the Gd content, the strength of the alloys was enhanced due to the second phase strengthening and grain refinement. The degradation resistance of Mg-2Zn-0.5Zr alloy was increased by adding 0.5%–1% Gd due to the uniformly distributed second phases which acted as a barrier to prevent the pitting corrosion. However, increasing Gd content to 2% reduced the degradation resistance of the alloy due to the galvanic corrosion between the matrix and the second phases.The good degradation resistance and mechanical properties of as-cast Mg-2Zn-1Gd-0.5Zr alloy makes it outstanding for biomaterial application.
基金supported by the National Natural Science Foundation of China(52174361,52074114)Science and Technology Innovation Program of Hunan Province(2023RC3106)+2 种基金Open Fund of the China Spallation Neutron Source Songshan Lake Science City(KFKT2023B13)Graduate Training and Innovation Practice Base of Hunan Province,China Scholarship Council(202106130051)Postgraduate Scientific Research Innovation Project of Hunan Province(QL20220100,QL20230094).
文摘Multi-pass hot processing methods are commonly used in magnesium(Mg)alloys to overcome the poor workability due to limited slip systems,which generally involve complicated post-deformation softening and hardening behaviors.In this work,to reveal post-deformation softening and hardening mechanisms of a Mg-2Y-1Zn alloy,double-stage hot compression tests and microstructural observations were conducted.The results showed that the softening fraction of Mg-2Y-1Zn alloy showed a non-linear dependence on deformation conditions and could be general coupled by Z parameter.Due to the formation and cross-overlapping of twins and kinks,only static recovery(SRV)occurred during holding process at 300℃/0.001 s^(-1) which led to the least static softening:5.52% after 10 s of holding.For samples at 400℃/0.001s^(-1),the enhanced post-deformation softening,which is 11.93% after 10 s of holding,was attributed to static recrystallization(SRX)followed continuous dynamic recrystallization(CDRX)happened during first deformation stage as well as SRV influenced by the LPSO phases.Under deformation condition of 400℃/0.1 s^(-1),the coupled meta-dynamic recrystallization(MDRX)and SRX resulted in serious stress relaxation,which is 42.83% after 10 s of holding,and caused hardening phenomenon at reloading stage.The 18R-LPSO and 14H-LPSO phases synchronously worked on deformation behaviors and limited the growth of recrystallized grains.Further,a simplified static softening kinetics model was established based on Johnson-Mehl-Avrami-Kolmogorov equation and employed to rationalize experimental data.