Hydrotalcites known as anionic clays are found in nature. Hydrotalcites, hydrotalcite-like compounds, and calcined hydrotalcites (as mixed or complex oxides) as highly active, selective catalysts play an important rol...Hydrotalcites known as anionic clays are found in nature. Hydrotalcites, hydrotalcite-like compounds, and calcined hydrotalcites (as mixed or complex oxides) as highly active, selective catalysts play an important role in many base/catalyzed reactions. Mg/Al hydrotalcite (MAH) as precursor was used to prepare Mg/Al metal complex oxides (MAO), used as epoxidation catalysts in the current research. In this paper, some primary physical and catalytic properties of MAH and MAO were investigated. The results indicated that the qualified MAH (Mg/Al mol ratio of 3) can be achieved when the suspension was crystallized under 80°C for 16h, and after being filtered, dried at 100 °C for 5h in a oven. MAO was prepared by calcining MAH for 4h in a muffle furnace, and calcination temperature was determined to be 500 °C by a differential scanning calorimeter (DSC). Crystal structure and parameters of MAH and MAO were characterized by X/ray diffraction (XRD), good crystal structure was observed and typical peaks of MAH were detected when 2θ was at 11.5 (003), 23.0 (006), 35.0 (009), and 61.0 (110), respectively. The morphology of calcined precursor, i.e. MAO, was investigated with scanning electron microscopy (SEM);the finer lamellar structure and smaller average size of 3μm was observed. Molding research was performed and confirmed by SEM, the results indicated that the surface bulge and cavity with size of several micrometers were increased, which simultaneously suggested the increasing of specific surface area. The catalytic activity of molding MAO was finally examined by using octanol as starting reagent and ethylene oxide as reactant, and narrower molecular distribution was observed comparing with the traditional catalyst-KOH.展开更多
SiCp/Al2O3-Al composites were synthesized by means of direct metal oxidation method. The composition and microstructures of the composites were investigated using X-ray diffraction （XRD）, scanning electron microsco...SiCp/Al2O3-Al composites were synthesized by means of direct metal oxidation method. The composition and microstructures of the composites were investigated using X-ray diffraction （XRD）, scanning electron microscopy （SEM） and metallurgical microscope. The effects of technical parameters on the properties of the product were analyzed. The results indicate that the composite possesses a dense microstructure, composed of three interpenetrated phases. Of them, SiO2 layer prohibits the powdering of the composites; Mg promotes the wetting and infiltration of the system and Si restricts the interfacial reaction while improving the wetting ability between reinforcement and matrix.展开更多
The one-pot synthesis of methyl isobutyl ketone(MIBK)from acetone using multifunctional catalysts is an important sustainable organic synthesis method with high atom and energy efficiency.Herein.we report a series of ...The one-pot synthesis of methyl isobutyl ketone(MIBK)from acetone using multifunctional catalysts is an important sustainable organic synthesis method with high atom and energy efficiency.Herein.we report a series of Pd supported on mixed metal oxide(MMO)catalysts with controllable acidic/basic/metallic sites on the surface.We study the relationship between the nature,synergy,and proximity of active sites and the catalytic performance of the multifunctional catalyst in the tandem reaction,in detail.In the existence of Lewis acid and base sites,the catalysts with medium-strength acidic/basic sites show preferred activity and/or MIBK selectivity.For multifunctional catalysts,the catalytic properties are more than just a collection of active sites,and the Pd/Mg_3Al-MMO catalyst possessing 0.1%Pd loading and~0.4 acid/base molar ratio exhibits the optimal 42.1%acetone conversion and 37.2%MIBK yield,which is among the best reported so far for this tandem reaction under similar conditions.Moreover,the proximity test indicates that the intimate distance between acidic/basic/metallic sites can greatly shorten the diffusion time of the intermediate species from each active site,leading to an enhancement in the catalytic performance.展开更多
This work reports the influence of alumina fiber reinforcement of an AZ91Nd MMC(metal matrix composite)on the PEO coating formation process in a sodium phosphate-based electrolyte.By comparison with the pure AZ91Nd,th...This work reports the influence of alumina fiber reinforcement of an AZ91Nd MMC(metal matrix composite)on the PEO coating formation process in a sodium phosphate-based electrolyte.By comparison with the pure AZ91Nd,the evolution of alumina fiber during the processing and the characteristics of the resultant PEO coating were investigated.The voltage response as a function of processing time was changed.Lower voltage in the presence of alumina fiber is responsible for the lower coating thickness.The morphology and phase composition of the coatings are also influenced by the incorporation of the fiber.Firstly,the fiber is embedded in the coating and interrupts the continuity of the coating.With increasing processing time,the fiber is found to be reactively incorporated in the coating.The intention to produce a MgAl_(2)O_(4)containing coating is achieved and it is mainly accumulated near the coating surface.However,due to the low number of fibers,the Al content is overall still low and only near to the fibers the MgAl_(2)O_(4)spinel phase can form.展开更多
研究了一种以玻碳为基底电极,掺杂钴—氧化钴的聚苯胺为中间体,层状镁铝复合金属氧化物PVC膜为敏感膜,具有双层膜结构的固态磷酸根离子选择电极。该电极的检测磷酸二氢根的线性范围在10^(-1)~10^(-4)mol/L之间,响应斜率为-32.3 m V/dec...研究了一种以玻碳为基底电极,掺杂钴—氧化钴的聚苯胺为中间体,层状镁铝复合金属氧化物PVC膜为敏感膜,具有双层膜结构的固态磷酸根离子选择电极。该电极的检测磷酸二氢根的线性范围在10^(-1)~10^(-4)mol/L之间,响应斜率为-32.3 m V/dec,检测下限为7.65×10^(-5)mol/L,电极响应时间较快,且具有较强的稳定性和抗干扰能力。展开更多
文摘Hydrotalcites known as anionic clays are found in nature. Hydrotalcites, hydrotalcite-like compounds, and calcined hydrotalcites (as mixed or complex oxides) as highly active, selective catalysts play an important role in many base/catalyzed reactions. Mg/Al hydrotalcite (MAH) as precursor was used to prepare Mg/Al metal complex oxides (MAO), used as epoxidation catalysts in the current research. In this paper, some primary physical and catalytic properties of MAH and MAO were investigated. The results indicated that the qualified MAH (Mg/Al mol ratio of 3) can be achieved when the suspension was crystallized under 80°C for 16h, and after being filtered, dried at 100 °C for 5h in a oven. MAO was prepared by calcining MAH for 4h in a muffle furnace, and calcination temperature was determined to be 500 °C by a differential scanning calorimeter (DSC). Crystal structure and parameters of MAH and MAO were characterized by X/ray diffraction (XRD), good crystal structure was observed and typical peaks of MAH were detected when 2θ was at 11.5 (003), 23.0 (006), 35.0 (009), and 61.0 (110), respectively. The morphology of calcined precursor, i.e. MAO, was investigated with scanning electron microscopy (SEM);the finer lamellar structure and smaller average size of 3μm was observed. Molding research was performed and confirmed by SEM, the results indicated that the surface bulge and cavity with size of several micrometers were increased, which simultaneously suggested the increasing of specific surface area. The catalytic activity of molding MAO was finally examined by using octanol as starting reagent and ethylene oxide as reactant, and narrower molecular distribution was observed comparing with the traditional catalyst-KOH.
基金National Natural Science Foundation of China (50372037)Scientific Research Foundations of Shaanxi University of Science and Technology (SUST-B14)
文摘SiCp/Al2O3-Al composites were synthesized by means of direct metal oxidation method. The composition and microstructures of the composites were investigated using X-ray diffraction （XRD）, scanning electron microscopy （SEM） and metallurgical microscope. The effects of technical parameters on the properties of the product were analyzed. The results indicate that the composite possesses a dense microstructure, composed of three interpenetrated phases. Of them, SiO2 layer prohibits the powdering of the composites; Mg promotes the wetting and infiltration of the system and Si restricts the interfacial reaction while improving the wetting ability between reinforcement and matrix.
文摘The one-pot synthesis of methyl isobutyl ketone(MIBK)from acetone using multifunctional catalysts is an important sustainable organic synthesis method with high atom and energy efficiency.Herein.we report a series of Pd supported on mixed metal oxide(MMO)catalysts with controllable acidic/basic/metallic sites on the surface.We study the relationship between the nature,synergy,and proximity of active sites and the catalytic performance of the multifunctional catalyst in the tandem reaction,in detail.In the existence of Lewis acid and base sites,the catalysts with medium-strength acidic/basic sites show preferred activity and/or MIBK selectivity.For multifunctional catalysts,the catalytic properties are more than just a collection of active sites,and the Pd/Mg_3Al-MMO catalyst possessing 0.1%Pd loading and~0.4 acid/base molar ratio exhibits the optimal 42.1%acetone conversion and 37.2%MIBK yield,which is among the best reported so far for this tandem reaction under similar conditions.Moreover,the proximity test indicates that the intimate distance between acidic/basic/metallic sites can greatly shorten the diffusion time of the intermediate species from each active site,leading to an enhancement in the catalytic performance.
基金China Scholarship Council for the award of fellowship and funding (No. 201708510113)。
文摘This work reports the influence of alumina fiber reinforcement of an AZ91Nd MMC(metal matrix composite)on the PEO coating formation process in a sodium phosphate-based electrolyte.By comparison with the pure AZ91Nd,the evolution of alumina fiber during the processing and the characteristics of the resultant PEO coating were investigated.The voltage response as a function of processing time was changed.Lower voltage in the presence of alumina fiber is responsible for the lower coating thickness.The morphology and phase composition of the coatings are also influenced by the incorporation of the fiber.Firstly,the fiber is embedded in the coating and interrupts the continuity of the coating.With increasing processing time,the fiber is found to be reactively incorporated in the coating.The intention to produce a MgAl_(2)O_(4)containing coating is achieved and it is mainly accumulated near the coating surface.However,due to the low number of fibers,the Al content is overall still low and only near to the fibers the MgAl_(2)O_(4)spinel phase can form.
基金This work was supported by the National Natural Science Foundation of China(Nos.51971040,52171101,52001036,51971044)the Natural Science Foundation of Chongqing,China(No.cstc2021jcyj-msxmX0613)the Independent Research Project of State Key Laboratory of Mechanical Transmissions,China(No.SKLMT-ZZKT-2022M12).
文摘研究了一种以玻碳为基底电极,掺杂钴—氧化钴的聚苯胺为中间体,层状镁铝复合金属氧化物PVC膜为敏感膜,具有双层膜结构的固态磷酸根离子选择电极。该电极的检测磷酸二氢根的线性范围在10^(-1)~10^(-4)mol/L之间,响应斜率为-32.3 m V/dec,检测下限为7.65×10^(-5)mol/L,电极响应时间较快,且具有较强的稳定性和抗干扰能力。