A new method was proposed for preparing AZ31/1060 composite plates with a corrugated interface,which involved cold-pressing a corrugated surface on the Al plate and then hot-pressing the assembled Mg/Al plate.The resu...A new method was proposed for preparing AZ31/1060 composite plates with a corrugated interface,which involved cold-pressing a corrugated surface on the Al plate and then hot-pressing the assembled Mg/Al plate.The results show that cold-pressing produces intense plastic deformation near the corrugated surface of the Al plate,which promotes dynamic recrystallization of the Al substrate near the interface during the subsequent hot-pressing.In addition,the initial corrugation on the surface of the Al plate also changes the local stress state near the interface during hot pressing,which has a large effect on the texture components of the substrates near the corrugated interface.The construction of the corrugated interface can greatly enhance the shear strength by 2−4 times due to the increased contact area and the strong“mechanical gearing”effect.Moreover,the mechanical properties are largely depended on the orientation relationship between corrugated direction and loading direction.展开更多
Thickness of the intermetallic compounds(IMC)layer at the interface has a significant effect on the mechanical properties of Mg/Al dissimilar joints.However,the thickness of IMC layer can be only obtained by metallurg...Thickness of the intermetallic compounds(IMC)layer at the interface has a significant effect on the mechanical properties of Mg/Al dissimilar joints.However,the thickness of IMC layer can be only obtained by metallurgical microscopy,which is destructive and has to break down the weld.Therefore,it is crucial to find a reliable approach that can non-destructively predict the thickness of IMC layer in practical application.In the current study,Mg alloy and Al alloy were friction stir butt welded(FSW)under different tool rotation speeds(TRS)to obtain different thicknesses of IMC layers.As the TRS increased from 400 rpm to 1000 rpm,thickness of the IMC layer increased from 0.4μm to 1.3μm,the peak welding temperatures increased from 259℃to 402℃,and the Z-axis downforces decreased from10.5 kN to 3.2 k N during welding process.Higher TRS would generally induce higher welding heat input,which promotes the growth of the IMC layer and the softening of base materials.The IMC layer formed through solid-state diffusion and transformation instead of eutectic reaction according to the welding temperature history and interfacial microstructure,and its evolution process was clearly observed by plan view.In order to incorporate the effect of dramatic change of welding temperature which is the characteristic feature of FSW,Psd Voigt function was used to fit the welding temperature histories.A new prediction formula was then established to predict thicknesses of IMC layers with considering sharp welding temperature change.Predicted thicknesses gave good agreement with measured thicknesses obtained experimentally under different welding parameters,which confirmed the accuracy and reliability of the new prediction formula.Based on this prediction formula,the time period of temperature higher than 200℃during welding was found critical for the thickening of interfacial IMC layers.展开更多
Fabricating Mg/Al laminate is an effective strategy to circumvent the inherently low formability and poor corrosion resistance of Mg alloys.Here,Mg/Al laminate with good bonding quality and mechanical properties was s...Fabricating Mg/Al laminate is an effective strategy to circumvent the inherently low formability and poor corrosion resistance of Mg alloys.Here,Mg/Al laminate with good bonding quality and mechanical properties was successfully fabricated via porthole die co-extrusion process using ZK60 Mg and TiB_(2)/6061Al composite as constituted layers.Integrating the results from microstructural characterization and mechanical testing,the effects of extrusion temperature on microstructure,interfacial structure,element diffusion,and mechanical properties were investigated.The results show that Mg/Al laminate achieves a sound welding quality by mechanical bonding and diffusion bonding.The obvious intermetallic compounds(βandγ)layer forms at Mg/Al interface,and its thickness increases to 8.3μm as the extrusion temperature reaches 400℃.High extrusion temperature promotes the dynamic recrystallization and grain growth of Mg and Al layers,while the dislocation density decreases.β/γinterface shows a coherent feature,whileγ/Mg interface is semi-coherent with a locally ordered transition zone of 4.5 nm.The rich Mg and Cr layers are found at TiB_(2)/6061 interface,which is conducive to improving the bonding quality.When the extrusion temperature is 370℃,the thickness of diffusion layer is around 5.0μm,and the bonding strength reaches 18.68 MPa,resulting in the best comprehensive mechanical properties.This work provides a new direction for the development of Mg/Al laminate with excellent strength and ductility.展开更多
In this study,microstructure and mechanical behavior of Mg/Al composite plates with Ti foil interlayer were systematically studied,with a great emphasis on the effect of different thicknesses of Ti foil interlayer.The...In this study,microstructure and mechanical behavior of Mg/Al composite plates with Ti foil interlayer were systematically studied,with a great emphasis on the effect of different thicknesses of Ti foil interlayer.The results show that compared to 100μm thick Ti foil,10μm thick Ti foil is more prone to fracture and is evenly distributed in fragments at the interface.The introduction of Ti foil can effectively refine the grain size of Mg layers of as-rolled Mg/Al composite plates,10μm thick Ti foil has a better refining effect than 100μm thick Ti foil.Ti foil can effectively increase the yield strength(YS)and ultimate strength(UTS)of as-rolled Mg/Al composite plates,10μm thick Ti foil significantly improves the elongation(El)of Mg/Al composite plate,while 100μm thick Ti foil slightly weakens the El.After annealing at 420℃ for 0.5 h and 4 h,Ti foil can inhibit the formation of intermetallic compounds(IMCs)at the interface of Mg/Al composite plates,which effectively improves the YS,UTS and El of Mg/Al composite plates.In addition,Ti foil can also significantly enhance the interfacial shear strength(SS)of Mg/Al composite plates before and after annealing.展开更多
Edge defects significantly impact the forming quality of Mg/Al composite plates during the rolling process.This study aims to develop an effective rolling technique to suppress these defects.First,an enhanced Lemaitre...Edge defects significantly impact the forming quality of Mg/Al composite plates during the rolling process.This study aims to develop an effective rolling technique to suppress these defects.First,an enhanced Lemaitre damage model with a generalized stress state damage prediction mechanism was used to evaluate the key mechanical factors contributing to defect formation.Based on this evaluation,an embedded composite rolling technique was proposed.Subsequently,comparative validation was conducted at 350℃ with a 50% reduction ratio.Results showed that the plates rolled using the embedded composite rolling technique had smooth surfaces and edges,with no macroscopic cracks observed.Numerical simulation indicated that,compared to conventional processes,the proposed technique reduced the maximum edge stress triaxiality of the plates from-0.02 to-1.56,significantly enhancing the triaxial compressive stress effect at the edges,which suppressed void nucleation and growth,leading to a 96%reduction in damage values.Mechanical property evaluations demonstrated that,compared to the conventional rolling process,the proposed technique improved edge bonding strength and tensile strength by approximately 67.7%and 118%,respectively.Further microstructural characterization revealed that the proposed technique,influenced by the restriction of deformation along the transverse direction(TD),weakened the plastic flow in the TD and enhanced plastic flow along the rolling direction(RD),resulting in higher grain boundary density and stronger basal texture.This,in turn,improved the toughness and transverse homogeneity of the plates.In summary,the embedded composite rolling technique provides crucial technical guidance for the preparation of Mg-based composite plates.展开更多
Mg/Al laminate with ZK60Mg and TiB2/6061Al as constitute layers was fabricated through the porthole die co-extrusion and hot rolling.The effects of rolling and roll temperatures on the microstructure,interfacial struc...Mg/Al laminate with ZK60Mg and TiB2/6061Al as constitute layers was fabricated through the porthole die co-extrusion and hot rolling.The effects of rolling and roll temperatures on the microstructure,interfacial structure,mechanical properties,and crack propagation paths were studied.The results show that the intermetallic compounds layer shows an intermittent form.The strong strain/dislocation hardening ability of Mg/Al laminate is attributed to the coupled effects of interlocking Al/βinterface,strain gradient,andβlayer with nanotwins and stacking faults.The complex dislocation structures such as network,loop,and array are found in the Al layer.Dislocation slip is the main deformation mode of the Al layer,while dislocation slip and dynamic recrystallization are the main deformation modes of the Mg layer.As roll temperature increases,prismatic〈a〉slip replaces the basal〈a〉slip as the most important slip mode.At a rolling temperature of 400℃ and a roll temperature of 150℃,an optimal synergy of mechanical properties is achieved,with ultimate tensile strength,shear strength,and elongation of 262.1 MPa,36.4 MPa,and 18.1%,respectively.As the rolling temperature increases,the fracture mode of Mg/Al laminate changes from discontinuous plastic shrinkage to transverse and longitudinal cracks.With increasing the roll temperature,the through cracks tend to form,indicating the plasticity and bonding quality of Mg/Al laminate are effectively enhanced.展开更多
文章研究了Mg/Al水滑石焙烧产物(LDO)对酸性红88(AR88)的吸附性能及其机理.考察了温度对其吸附性能的影响,探讨了吸附过程的动力学和热力学规律.热力学研究表明:LDO对AR88的吸附过程稍符合Langmuir等温吸附.从Langmuir等温式计算的ΔH,...文章研究了Mg/Al水滑石焙烧产物(LDO)对酸性红88(AR88)的吸附性能及其机理.考察了温度对其吸附性能的影响,探讨了吸附过程的动力学和热力学规律.热力学研究表明:LDO对AR88的吸附过程稍符合Langmuir等温吸附.从Langmuir等温式计算的ΔH,ΔS为负值,表明吸附过程为放热、熵减小的过程,这是因为LDO在吸附酸性染料后恢复了层状结构;不同温度下ΔG均为负值,表明吸附过程是自发进行的.动力学研究表明:吸附动力学符合准二级动力学模型,动力学计算吸附过程的活化能Ea=54.53 kJ·mol-1.利用Materials Studio 4.3软件中的CASTEP程序模块和Focite模块模拟了AR88染料分子在Mg/Al水滑石(LDHs)的尺寸大小和排列方式,推测吸附机理是以表面吸附占主要优势并伴有少部分插层.展开更多
基金supported by Guangdong Major Project of Basic and Applied Basic Research, China (No. 2020B0301030006)Fundamental Research Funds for the Central Universities, China (No. SWU-XDJH202313)+1 种基金Chongqing Postdoctoral Science Foundation Funded Project, China (No. 2112012728014435)the Chongqing Postgraduate Research and Innovation Project, China (No. CYS23197)。
文摘A new method was proposed for preparing AZ31/1060 composite plates with a corrugated interface,which involved cold-pressing a corrugated surface on the Al plate and then hot-pressing the assembled Mg/Al plate.The results show that cold-pressing produces intense plastic deformation near the corrugated surface of the Al plate,which promotes dynamic recrystallization of the Al substrate near the interface during the subsequent hot-pressing.In addition,the initial corrugation on the surface of the Al plate also changes the local stress state near the interface during hot pressing,which has a large effect on the texture components of the substrates near the corrugated interface.The construction of the corrugated interface can greatly enhance the shear strength by 2−4 times due to the increased contact area and the strong“mechanical gearing”effect.Moreover,the mechanical properties are largely depended on the orientation relationship between corrugated direction and loading direction.
基金supported by the National Natural Science Foundation of China(No.52075330)the Interdisciplinary Program of Shanghai Jiao Tong University(No.YG2019QNA15)the Foundation of National Facility for Translational Medicine(Shanghai)(No.TMSK-2020-107)。
文摘Thickness of the intermetallic compounds(IMC)layer at the interface has a significant effect on the mechanical properties of Mg/Al dissimilar joints.However,the thickness of IMC layer can be only obtained by metallurgical microscopy,which is destructive and has to break down the weld.Therefore,it is crucial to find a reliable approach that can non-destructively predict the thickness of IMC layer in practical application.In the current study,Mg alloy and Al alloy were friction stir butt welded(FSW)under different tool rotation speeds(TRS)to obtain different thicknesses of IMC layers.As the TRS increased from 400 rpm to 1000 rpm,thickness of the IMC layer increased from 0.4μm to 1.3μm,the peak welding temperatures increased from 259℃to 402℃,and the Z-axis downforces decreased from10.5 kN to 3.2 k N during welding process.Higher TRS would generally induce higher welding heat input,which promotes the growth of the IMC layer and the softening of base materials.The IMC layer formed through solid-state diffusion and transformation instead of eutectic reaction according to the welding temperature history and interfacial microstructure,and its evolution process was clearly observed by plan view.In order to incorporate the effect of dramatic change of welding temperature which is the characteristic feature of FSW,Psd Voigt function was used to fit the welding temperature histories.A new prediction formula was then established to predict thicknesses of IMC layers with considering sharp welding temperature change.Predicted thicknesses gave good agreement with measured thicknesses obtained experimentally under different welding parameters,which confirmed the accuracy and reliability of the new prediction formula.Based on this prediction formula,the time period of temperature higher than 200℃during welding was found critical for the thickening of interfacial IMC layers.
基金supports from the National Natural Science Foundation of China(52175338 and 52222510)Science Fund for Distinguished Young Scholars of Shandong Province(ZR2021JQ21)Key Research and Development Program of Shandong Province(2021ZLGX01).
文摘Fabricating Mg/Al laminate is an effective strategy to circumvent the inherently low formability and poor corrosion resistance of Mg alloys.Here,Mg/Al laminate with good bonding quality and mechanical properties was successfully fabricated via porthole die co-extrusion process using ZK60 Mg and TiB_(2)/6061Al composite as constituted layers.Integrating the results from microstructural characterization and mechanical testing,the effects of extrusion temperature on microstructure,interfacial structure,element diffusion,and mechanical properties were investigated.The results show that Mg/Al laminate achieves a sound welding quality by mechanical bonding and diffusion bonding.The obvious intermetallic compounds(βandγ)layer forms at Mg/Al interface,and its thickness increases to 8.3μm as the extrusion temperature reaches 400℃.High extrusion temperature promotes the dynamic recrystallization and grain growth of Mg and Al layers,while the dislocation density decreases.β/γinterface shows a coherent feature,whileγ/Mg interface is semi-coherent with a locally ordered transition zone of 4.5 nm.The rich Mg and Cr layers are found at TiB_(2)/6061 interface,which is conducive to improving the bonding quality.When the extrusion temperature is 370℃,the thickness of diffusion layer is around 5.0μm,and the bonding strength reaches 18.68 MPa,resulting in the best comprehensive mechanical properties.This work provides a new direction for the development of Mg/Al laminate with excellent strength and ductility.
基金supported by the National Key Research and Development Program of China(2022YFB3708400)the Guangdong Major Project of Basic and Applied Basic Research(2020B0301030006)+4 种基金the Youth Talent Support Programme of Guangdong Provincial Association for Science and Technology(SKXRC202301)the Guangdong Academy of Science Fund(2020GDASYL-20200101001,2023GDASQNRC-0210,2023GDASQNRC-0321)the Guangdong Science and Technology plan project(2023A0505030002)the GINM’Special Project of Science and Technology Development(2023GINMZX-202301020108)Evaluation Project of Guangdong Provincial Key Laboratory(2023B1212060043).
文摘In this study,microstructure and mechanical behavior of Mg/Al composite plates with Ti foil interlayer were systematically studied,with a great emphasis on the effect of different thicknesses of Ti foil interlayer.The results show that compared to 100μm thick Ti foil,10μm thick Ti foil is more prone to fracture and is evenly distributed in fragments at the interface.The introduction of Ti foil can effectively refine the grain size of Mg layers of as-rolled Mg/Al composite plates,10μm thick Ti foil has a better refining effect than 100μm thick Ti foil.Ti foil can effectively increase the yield strength(YS)and ultimate strength(UTS)of as-rolled Mg/Al composite plates,10μm thick Ti foil significantly improves the elongation(El)of Mg/Al composite plate,while 100μm thick Ti foil slightly weakens the El.After annealing at 420℃ for 0.5 h and 4 h,Ti foil can inhibit the formation of intermetallic compounds(IMCs)at the interface of Mg/Al composite plates,which effectively improves the YS,UTS and El of Mg/Al composite plates.In addition,Ti foil can also significantly enhance the interfacial shear strength(SS)of Mg/Al composite plates before and after annealing.
基金supported by National Key Research and Development Program(2018YFA0707300)Major Program of National Natural Science Foundation of China(U22A20188).
文摘Edge defects significantly impact the forming quality of Mg/Al composite plates during the rolling process.This study aims to develop an effective rolling technique to suppress these defects.First,an enhanced Lemaitre damage model with a generalized stress state damage prediction mechanism was used to evaluate the key mechanical factors contributing to defect formation.Based on this evaluation,an embedded composite rolling technique was proposed.Subsequently,comparative validation was conducted at 350℃ with a 50% reduction ratio.Results showed that the plates rolled using the embedded composite rolling technique had smooth surfaces and edges,with no macroscopic cracks observed.Numerical simulation indicated that,compared to conventional processes,the proposed technique reduced the maximum edge stress triaxiality of the plates from-0.02 to-1.56,significantly enhancing the triaxial compressive stress effect at the edges,which suppressed void nucleation and growth,leading to a 96%reduction in damage values.Mechanical property evaluations demonstrated that,compared to the conventional rolling process,the proposed technique improved edge bonding strength and tensile strength by approximately 67.7%and 118%,respectively.Further microstructural characterization revealed that the proposed technique,influenced by the restriction of deformation along the transverse direction(TD),weakened the plastic flow in the TD and enhanced plastic flow along the rolling direction(RD),resulting in higher grain boundary density and stronger basal texture.This,in turn,improved the toughness and transverse homogeneity of the plates.In summary,the embedded composite rolling technique provides crucial technical guidance for the preparation of Mg-based composite plates.
基金supported by the National Natural Science Foundation of China(Nos.52175338 and 52222510)Science Fund for Distinguished Young Scholars of Shandong Province(No.ZR2021JQ21)+1 种基金Key Research and Development Program of Shandong Province(No.2021ZLGX01)The Excellent Young Team Project of Central Universities(No.2023QNTD002).
文摘Mg/Al laminate with ZK60Mg and TiB2/6061Al as constitute layers was fabricated through the porthole die co-extrusion and hot rolling.The effects of rolling and roll temperatures on the microstructure,interfacial structure,mechanical properties,and crack propagation paths were studied.The results show that the intermetallic compounds layer shows an intermittent form.The strong strain/dislocation hardening ability of Mg/Al laminate is attributed to the coupled effects of interlocking Al/βinterface,strain gradient,andβlayer with nanotwins and stacking faults.The complex dislocation structures such as network,loop,and array are found in the Al layer.Dislocation slip is the main deformation mode of the Al layer,while dislocation slip and dynamic recrystallization are the main deformation modes of the Mg layer.As roll temperature increases,prismatic〈a〉slip replaces the basal〈a〉slip as the most important slip mode.At a rolling temperature of 400℃ and a roll temperature of 150℃,an optimal synergy of mechanical properties is achieved,with ultimate tensile strength,shear strength,and elongation of 262.1 MPa,36.4 MPa,and 18.1%,respectively.As the rolling temperature increases,the fracture mode of Mg/Al laminate changes from discontinuous plastic shrinkage to transverse and longitudinal cracks.With increasing the roll temperature,the through cracks tend to form,indicating the plasticity and bonding quality of Mg/Al laminate are effectively enhanced.
文摘文章研究了Mg/Al水滑石焙烧产物(LDO)对酸性红88(AR88)的吸附性能及其机理.考察了温度对其吸附性能的影响,探讨了吸附过程的动力学和热力学规律.热力学研究表明:LDO对AR88的吸附过程稍符合Langmuir等温吸附.从Langmuir等温式计算的ΔH,ΔS为负值,表明吸附过程为放热、熵减小的过程,这是因为LDO在吸附酸性染料后恢复了层状结构;不同温度下ΔG均为负值,表明吸附过程是自发进行的.动力学研究表明:吸附动力学符合准二级动力学模型,动力学计算吸附过程的活化能Ea=54.53 kJ·mol-1.利用Materials Studio 4.3软件中的CASTEP程序模块和Focite模块模拟了AR88染料分子在Mg/Al水滑石(LDHs)的尺寸大小和排列方式,推测吸附机理是以表面吸附占主要优势并伴有少部分插层.