A new method was proposed for preparing AZ31/1060 composite plates with a corrugated interface,which involved cold-pressing a corrugated surface on the Al plate and then hot-pressing the assembled Mg/Al plate.The resu...A new method was proposed for preparing AZ31/1060 composite plates with a corrugated interface,which involved cold-pressing a corrugated surface on the Al plate and then hot-pressing the assembled Mg/Al plate.The results show that cold-pressing produces intense plastic deformation near the corrugated surface of the Al plate,which promotes dynamic recrystallization of the Al substrate near the interface during the subsequent hot-pressing.In addition,the initial corrugation on the surface of the Al plate also changes the local stress state near the interface during hot pressing,which has a large effect on the texture components of the substrates near the corrugated interface.The construction of the corrugated interface can greatly enhance the shear strength by 2−4 times due to the increased contact area and the strong“mechanical gearing”effect.Moreover,the mechanical properties are largely depended on the orientation relationship between corrugated direction and loading direction.展开更多
(NbZrHfTi)C high-entropy ceramics,as an emerging class of ultra-high-temperature materials,have garnered significant interest due to their unique multi-principal-element crystal structure and exceptional hightemperatu...(NbZrHfTi)C high-entropy ceramics,as an emerging class of ultra-high-temperature materials,have garnered significant interest due to their unique multi-principal-element crystal structure and exceptional hightemperature properties.This study systematically investigates the mechanical properties of(NbZrHfTi)C high-entropy ceramics by employing first-principles density functional theory,combined with the Debye-Grüneisen model,to explore the variations in their thermophysical properties with temperature(0–2000 K)and pressure(0–30 GPa).Thermodynamically,the calculated mixing enthalpy and Gibbs free energy confirm the feasibility of forming a stable single-phase solid solution in(NbZrHfTi)C.The calculated results of the elastic stiffness constant indicate that the material meets the mechanical stability criteria of the cubic crystal system,further confirming the structural stability.Through evaluation of key mechanical parameters—bulk modulus,shear modulus,Young’s modulus,and Poisson’s ratio—we provide comprehensive insight into the macro-mechanical behaviour of the material and its correlation with the underlying microstructure.Notably,compared to traditional binary carbides and their average properties,(NbZrHfTi)C exhibits higher Vickers hardness(Approximately 28.5 GPa)and fracture toughness(Approximately 3.4 MPa⋅m^(1/2)),which can be primarily attributed to the lattice distortion and solid-solution strengthening mechanism.The study also utilizes the quasi-harmonic approximation method to predict the material’s thermophysical properties,including Debye temperature(initial value around 563 K),thermal expansion coefficient(approximately 8.9×10^(−6) K−1 at 2000 K),and other key parameters such as heat capacity at constant volume.The results show that within the studied pressure and temperature ranges,(NbZrHfTi)C consistently maintains a stable phase structure and good thermomechanical properties.The thermal expansion coefficient increasing with temperature,while heat capacity approaches the Dulong-Petit limit at elevated temperatures.These findings underscore the potential of(NbZrHfTi)C applications in ultra-high temperature thermal protection systems,cutting tool coatings,and nuclear structural materials.展开更多
The composition−property relationship of 18 quaternary high entropy diborides(HEBs)consisting of boron and IVB,VB and VIB transition metals(TM)was investigated using first-principles calculations.A valence electron co...The composition−property relationship of 18 quaternary high entropy diborides(HEBs)consisting of boron and IVB,VB and VIB transition metals(TM)was investigated using first-principles calculations.A valence electron concentration−relative electronegativity(VEC−REN)composite descriptor was developed to effectively predict the mechanical properties of HEBs.The results demonstrate that with a fixed VEC,the rise of the REN makes HEBs harder but more brittle when the electronegativity of doped TM atoms is lower than that of boron atoms.However,HEBs become softer and more ductile as REN increases if the doped TM atoms have higher electronegativity than boron atoms.The VEC−REN composite descriptor can accurately classify and predict the mechanical properties of HEBs with different components,which provides important theoretical guidance for the rapid design and development of novel high-entropy ceramic materials.展开更多
The advancement of flexible memristors has significantly promoted the development of wearable electronic for emerging neuromorphic computing applications.Inspired by in-memory computing architecture of human brain,fle...The advancement of flexible memristors has significantly promoted the development of wearable electronic for emerging neuromorphic computing applications.Inspired by in-memory computing architecture of human brain,flexible memristors exhibit great application potential in emulating artificial synapses for highefficiency and low power consumption neuromorphic computing.This paper provides comprehensive overview of flexible memristors from perspectives of development history,material system,device structure,mechanical deformation method,device performance analysis,stress simulation during deformation,and neuromorphic computing applications.The recent advances in flexible electronics are summarized,including single device,device array and integration.The challenges and future perspectives of flexible memristor for neuromorphic computing are discussed deeply,paving the way for constructing wearable smart electronics and applications in large-scale neuromorphic computing and high-order intelligent robotics.展开更多
The microstructures and mechanical properties of Al-8.3Zn-3.3Cu-2.2Mg alloys prepared via hot extrusion and liquid forging methods were investigated.Results show that based on DEFORM simulation analysis,the optimal ho...The microstructures and mechanical properties of Al-8.3Zn-3.3Cu-2.2Mg alloys prepared via hot extrusion and liquid forging methods were investigated.Results show that based on DEFORM simulation analysis,the optimal hot extrusion parameters are determined as ingot initial temperature of 380°C and extrusion speed of 3 mm/s.The hot-extruded aluminum alloy after T6 heat treatment presents superior mechanical properties with yield strength of 519.6 MPa,ultimate tensile strength of 582.1 MPa,and elongation of 11.0%.Compared with the properties of gravity-cast and liquid-forged alloys,the yield strength of hot-extruded alloy increases by 30.8%and 4.9%,and the ultimate tensile strength improves by 43.5%and 10.2%,respectively.The significant improvement in tensile strength of the hot-extruded alloys is attributed to the elimination of casting defects and the refinement of matrix grain and eutectic phases.In addition,the hot-extruded alloy demonstrates superior plasticity compared with the liquid-forged alloy.This is because severe plastic deformation occurs during hot extrusion,which effectively breaks and disperses the eutectic phases,facilitating the dissolution and precipitation of the second phases and inhibiting the microcrack initiation.展开更多
Ag-Cu-In-Ti low-temperature filler was used to braze the diamond and copper,and the effects of brazing temperature and soaking time on the microstructure and mechanical properties of the joints were investigated.In ad...Ag-Cu-In-Ti low-temperature filler was used to braze the diamond and copper,and the effects of brazing temperature and soaking time on the microstructure and mechanical properties of the joints were investigated.In addition,the joint formation mechanism was discussed,and the correlation between joint microstructure and mechanical performance was established.Results show that adding appropriate amount of In into the filler can significantly reduce the filler melting point and enhance the wettability of filler on diamond.When the brazing temperature is 750°C and the soaking time is 10 min,a uniformly dense braze seam with excellent metallurgical bonding can be obtained,and its average joint shear strength reaches 322 MPa.The lower brazing temperature can mitigate the risk of diamond graphitization and also reduce the residual stresses during joining.展开更多
Modification of 6061 aluminum alloy was conducted through composite addition of cerium-rich rare earths and Al-Ti-B.Results show that the composite addition of Al-Ti-B and Ce/La element at a specific ratio notably pro...Modification of 6061 aluminum alloy was conducted through composite addition of cerium-rich rare earths and Al-Ti-B.Results show that the composite addition of Al-Ti-B and Ce/La element at a specific ratio notably promotes the refinement of the alloy's grains.Ce and La elements are combined with Si and other elements to form rare earth phases,improving the morphology and distribution of precipitates and mitigating the adverse effects ofβ-Fe phases on the microstructure and mechanical properties of alloy.However,excessive rare earth content poses challenges;it not only leads to a decrease in Mg-Si strengthening phase by binding with Si but also promotes the formation of larger or numerous rare earth phases that may act as initiation points for cracks,thereby impeding the improvement of the structure and performance of alloy.The composite addition of cerium-rich rare earths and Al-Ti-B not only preserves the strength of the alloy but also significantly enhances the plasticity of the 6061 as-cast alloy.At a composite addition ratio of Al-Ti-B:RE=2:1,the newly developed 6061-RE aluminum alloy exhibits increased average elongation by 50%and 45%in its as-cast and homogenized states,respectively,compared to the baseline 6061 alloy,facilitating subsequent deformation processing.After solution treatment at 540℃for 1 h and aging at 180℃for 5 h,the average ultimate tensile strength and yield strength of 6061-RE alloys reach 313.2 and 283.1 MPa,increased by 12.3%and 14.5%compared with those of the original alloy,respectively,and the average elongation is improved by 41%.展开更多
To enhance the mechanical properties of Mo alloys prepared through laser powder bed fusion(LPBF),a hot isostatic pressing(HIP)treatment was used.Results show that following HIP treatment,the porosity decreases from 0....To enhance the mechanical properties of Mo alloys prepared through laser powder bed fusion(LPBF),a hot isostatic pressing(HIP)treatment was used.Results show that following HIP treatment,the porosity decreases from 0.27%to 0.22%,enabling the elements Mo and Ti to diffuse fully and to distribute more uniformly,and to forming a substantial number of low-angle grain boundaries.The tensile strength soars from 286±32 MPa to 598±22 MPa,while the elongation increases from 0.08%±0.02%to 0.18%±0.02%,without notable alterations in grain morphology during the tensile deformation.HIP treatment eliminates the molten pool boundaries,which are the primary source for premature failure in LPBFed Mo alloys.Consequently,HIP treatment emerges as a novel and effective approach for strengthening the mechanical properties of LPBFed Mo alloys,offering a fresh perspective on producing high-performance Mo-based alloys.展开更多
The performances of magnesium alloys remain insufficient to further enhance the application potential of ultralight magnesium alloys.In this work,a Mg-8Li-3Y-2Zn alloy was prepared through vacuum melting and subsequent...The performances of magnesium alloys remain insufficient to further enhance the application potential of ultralight magnesium alloys.In this work,a Mg-8Li-3Y-2Zn alloy was prepared through vacuum melting and subsequent heat treatment at 300,450,and 500°C.The material properties of the resulting samples were assessed through microstructural observation,tensile testing,electrical conductivity measurements,and electromagnetic shielding effectiveness(EMI-SE)testing.The influence of the Mg-8Li-3Y-2Zn alloy microstructure on its mechanical and electromagnetic shielding properties in different states was investigated.It was found that the as-cast alloy containsα-Mg,β-Li,Mg_(3)Zn_(3)Y_(2),and Mg_(12)ZnY phases.Following heat treatment at 500℃(HT500),the blockα-Mg phase transformedfine needle-shapes,its tensile strength increased to 263.7 MPa,and its elongation reached 45.3%.The mechanical properties of the alloy were significantly improved by the synergistic effects imparted by the needle-shapedα-Mg phase,solid solution strengthening,and precipitation strengthening.The addition of Y and Zn improved the EMI-SE of Mg-8Li-1Zn alloy,wherein the HT500 sample exhibits the highest SE,maintaining a value of 106.7–76.9 dB in the frequency range of 30–4500 MHz;this performance has rarely been reported for electromagnetically shielded alloys.This effect was mainly attributed to the multiple reflections of electromagnetic waves caused by the severe impedance mismatch of the abundant phase boundaries,which were in turn provided by the dual-phase(α/β)and secondary phases.Furthermore,the presence of nano-precipitation was also believed to enhance the absorption of electromagnetic waves.展开更多
High-entropy materials possess high hardness and strong wear resistance,yet the key bottleneck for their practical applications is the poor corrosion resistance in harsh environments.In this work,the high-entropy nitr...High-entropy materials possess high hardness and strong wear resistance,yet the key bottleneck for their practical applications is the poor corrosion resistance in harsh environments.In this work,the high-entropy nitride(HEN)coatings of(MoNbTaTiZr)1-x Nx(x=0-0.47)were fabricated using a hybrid di-rect current magnetron sputtering technique.The research focus was dedicated to the effect of nitrogen content on the microstructure,mechanical and electrochemical properties.The results showed that the as-deposited coatings exhibited a typical body-centered cubic(BCC)structure without nitrogen,while the amorphous matrix with face-centered cubic(FCC)nanocrystalline grain was observed at x=0.17.Further increasing x in the range of 0.35-0.47 caused the appearance of polycrystalline FCC phase in structure.Compared with the MoNbTaTiZr metallic coating,the coating containing nitrogen favored the high hard-ness around 13.7-32.4 GPa,accompanied by excellent tolerance both against elastic and plastic deforma-tion.Furthermore,such N-containing coatings yielded a low corrosion current density of about 10−8-10−7 A/cm^(2) and high electrochemical impedance of 10^(6)Ωcm^(2) in 3.5 wt.%NaCl solution,indicating the supe-rior corrosion resistance.The reason for the enhanced electrochemical behavior could be ascribed to the spontaneous formation of protective passive layers over the coating surface,which consisted of the domi-nated multi-elemental oxides in chemical stability.Particularly,noted that the(MoNbTaTiZr)_(0.83) N0.17 coat-ing displayed the highest hardness of 32.4±2.6 GPa and H/E ratio at 0.09,together with remarkable cor-rosion resistance,proposing the strongest capability for harsh-environmental applications required both good anti-wear and anti-corrosion performance.展开更多
Hot isostatic pressing (HIP) temperature has a significant impact on the service performance of powder metallurgy titanium alloys. In this study, a high-temperature titanium alloy, Ti-6.5Al-3.5Mo-1.5Zr-0.3Si, was prep...Hot isostatic pressing (HIP) temperature has a significant impact on the service performance of powder metallurgy titanium alloys. In this study, a high-temperature titanium alloy, Ti-6.5Al-3.5Mo-1.5Zr-0.3Si, was prepared under different HIP temperatures (880–1000℃), and the microstructural evolution and mechanical properties were systematically investigated. The results demonstrated that the HIPed alloys were predominantly composed of more than 80 vol.% α phase and a small amount of β phase, and their phase compositions were basically unaffected by the HIP temperatures. Under the typical single-temperature-maintained HIP (STM-HIP) regime, the microstructure of alloy significantly coarsened as the HIP temperature increased, and the alloy strength exhibited an obvious linear negative correlation with the HIP temperature. On the basis of Hall–Petch relation, the prediction model of grain size was established, and the mathematical equation between HIP temperature and grain size (d=M(T_(HIP-N)^(-2))) was deduced. Furthermore, a possible evolution mechanism of microstructure was proposed, which could be divided into the decomposition of initial α′ martensite for as-received powder, formation of the globular α grains in prior particle boundaries (PPBs) region, and precipitation of the platelet α grains in non-PPBs region. For these alloys prepared by the dual-temperature-maintained HIP (DTM-HIP) regime, although their tensile properties were comparable to that of alloy prepared by STM-HIP regime with same high-temperature holding stage, higher proportion of globular α grains occurred due to more recrystallization nucleation during the low-temperature holding stage, which probably provided a solution for improving the dynamic service performance of HIPed alloys.展开更多
Irregular bone scaffolds fabricated using the Voronoi tessellation method resemble the morphology and properties of human cancellous bones.This has become a prominent topic in bone tissue engineering research in recen...Irregular bone scaffolds fabricated using the Voronoi tessellation method resemble the morphology and properties of human cancellous bones.This has become a prominent topic in bone tissue engineering research in recent years.However,studies on the radial-gradient design of irregular bionic scaffolds are limited.Therefore,this study aims to develop a radial-gradient structure similar to that of natural long bones,enhancing the development of bionic bone scaffolds.A novel gradient method was adopted to maintain constant porosity,control the seed site-specific distribution within the irregular porous structure,and vary the strut diameter to generate radial gradients.The irregular scaffolds were compared with four conventional scaffolds(cube,pillar BCC,vintiles,and diamond)in terms of permeability,stress concentration characteristics,and mechanical properties.The results indicate that the radial-gradient irregular porous structure boasts the widest permeability range and superior stress distribution compared to conventional scaffolds.With an elastic modulus ranging from 4.20 GPa to 22.96 GPa and a yield strength between 68.37 MPa and 149.40 MPa,it meets bone implant performance requirements and demonstrates significant application potential.展开更多
In cold regions,slope rocks are inevitably impacted by freeze-thaw,dry-wet cycles and their alternating actions,leading to strength weakening and pore degradation.In this study,the mechanical and microstructural prope...In cold regions,slope rocks are inevitably impacted by freeze-thaw,dry-wet cycles and their alternating actions,leading to strength weakening and pore degradation.In this study,the mechanical and microstructural properties of schist subjected to four conditions were investigated:freeze-thaw cycles in air(FTA),freeze-thaw cycles in water(FTW),dry-wet cycles(DW),and dry-wet-freeze-thaw cycles(DWFT).Uniaxial compressive strength(UCS),water absorption,ultrasonication,low-field nuclear magnetic resonance,and scanning electron microscopy analyses were conducted.The integrity attenuation characteristics of the longitudinal wave velocity,UCS,and elastic modulus were analyzed.The results showed that liquid water emerged as a critical factor in reducing the brittleness of schist.The attenuation function model accurately described the peak stress and static elastic modulus of schist in various media(R2>0.97).Different media affected the schist deterioration and half-life,with the FTW-immersed samples having a half-life of 28 cycles.Furthermore,the longitudinal wave velocity decreased as the number of cycles increased,with the FTW showing the most significant reduction and having the shortest half-life of 208 cycles.Moreover,the damage variables of compressive strength and elastic modulus increased with the number of cycles.After 40 cycles,the schist exposed to FTW exhibited the highest damage variables and saturated water content.展开更多
7039 Al alloys are widely used in armor vehicles,given the material’s high specific strength and fracture toughness.However,laminar tearing in the thickness plane of the base metal(BM),specifically in the normal dire...7039 Al alloys are widely used in armor vehicles,given the material’s high specific strength and fracture toughness.However,laminar tearing in the thickness plane of the base metal(BM),specifically in the normal direction(ND)and rolling direction(RD)plane,was occasionally observed after the welding of thick plates,resulting in premature material failure.A vertically metal-inert gas(MIG)-welded laminar tearing component of a 30 mm thick plate was analyzed to determine the factors associated with this phenomenon.The texture,residual stress,microhardness,and tensile properties were also investigated.The results indicated that the crack extended along the RD as a transcrystalline fracture and terminated at the BM.The grains near the crack grew preferentially in the(001)crystal direction.Furthermore,the tensile strength(83 MPa)and elongation(6.8%)in the RD were relatively higher than those in the ND.In particular,the primary factors for crack initiation include stronger texture,higher dislocation density,increased Al_(7)Cu_(2)Fe phases,lower proportion of small-angle grain boundaries,and varying grain sizes in different regions,leading to the fragile microstructure.The higher residual stress of the BM promotes the formation and extension of cracks.The restraining force due to fixation and welding shrinkage force transformed the crack into laminar tearing.Preventive measures of laminar tearing were also proposed.展开更多
To tackle the common issue of green defects in material extrusion(MEX)additive manufacturing(AM)cemented carbides,warm isostatic pressing(WIP)was introduced to eliminate defects of MEX WC-9Co cemented carbide greens,t...To tackle the common issue of green defects in material extrusion(MEX)additive manufacturing(AM)cemented carbides,warm isostatic pressing(WIP)was introduced to eliminate defects of MEX WC-9Co cemented carbide greens,thereby improving both microstructure uniformity and mechanical properties of sintered bodies.The results indicate that WIP reduces defects in MEX greens,thus decreasing the dimensions and numbers of defects,modifying shapes of pores within sintered bodies,while preserving surface quality and shape characteristics.Compared with WC-9Co prepared via MEX followed by debinding and sintering(DS),the hardness of WC-9Co prepared using MEX-WIP-DS does not change significantly,ranging HV_(30)1494-1508,the transverse rupture strength increases by up to 49.3%,reaching 2998-3514 MPa,and the fracture toughness remains high,ranging 14.8-17.0 MPa·m^(1/2).The mechanical properties surpass comparable cemented carbides fabricated through other AM methods and are comparable to those produced by powder metallurgy.The integration of green WIP into MEX-DS broadens the MEX processing window,and improves the overall mechanical properties of MEX AM WC-Co cemented carbides.展开更多
Electrolytic copper foil has gained significant attention as an essential component in lithium-ion batteries(LIBs),printed circuit boards(PCBs),and chip packaging substrates(CPSs)applications.With the advancement of L...Electrolytic copper foil has gained significant attention as an essential component in lithium-ion batteries(LIBs),printed circuit boards(PCBs),and chip packaging substrates(CPSs)applications.With the advancement of LIBs towards higher energy densities and the increasing density of electronic components on circuits,copper foil is required to have demanding properties,such as extremely thin thickness and extremely high tensile strength.This comprehensive review firstly summarizes recent progress on the fabrication of electrolytic copper foil,and the effects of process parameters,cathode substrate,and additives on the electrodeposition behavior,microstructure,and properties of copper foil are discussed in detail.Then the regulation strategies of mechanical properties of electrolytic copper foil are also summarized,including the formation of nanotwins and texture.Furthermore,the recent advances in novel electrolytic copper foils,such as composite foils and extra-thin copper foils,are also overviewed.Lastly,the remaining challenges and perspectives on the further development of electrolytic copper foils are presented.展开更多
The effect of Cr addition on nickel aluminium bronze(NAB)alloy microstructure,mechanical properties,and erosion-corrosion behaviour has been studied.The results show that Cr addition does not change the composition of...The effect of Cr addition on nickel aluminium bronze(NAB)alloy microstructure,mechanical properties,and erosion-corrosion behaviour has been studied.The results show that Cr addition does not change the composition of the precipitated phases,more Cr entered theκphase and a small amount of Cr solubilized in the matrix,which increase the hardness of theκand matrix and decrease the potential difference between theκand matrix.NAB alloy with Cr shows high erosion-corrosion resistance at high flow rate conditions,due to its lower phase potential difference and higher surface hardness.At the flow rate of 3 m·s^(-1),the corrosion rate is 0.076 mm·year^(-1),which is~20%lower than that of the unadded Cr sample.Moreover,the corrosion product film contains Cr_(2)O_(3)and Cr^(3+),which improves the densification of the film and raises alloy’s corrosion resistance with Cr addition.The combination of mechanical and corrosion resistant properties may qualify this alloy as a potential candidate material for sustainable and safe equipment.展开更多
Herein,cure characteristics,morphology,and mechanical properties of natural rubber filled with activated carbon-based materials were investigated.Carbon-based materials were prepared from bagasse,coffee grounds and pi...Herein,cure characteristics,morphology,and mechanical properties of natural rubber filled with activated carbon-based materials were investigated.Carbon-based materials were prepared from bagasse,coffee grounds and pineapple crowns by the pyrolysis method at temperatures in the range of 300℃.As-synthesized carbon materials were characterized by optical microscopy(OM),scanning electron microscopy(SEM),and Fourier-transform infrared spectroscopy(FTIR)to analyze size distribution,morphology,and functional groups,respectively.OM and SEM analysis revealed that particles,flakes,and a small quantity of fiber-like carbon were obtained using bagasse and pineapple crown as raw materials,while honeycomb-like carbon materials can be derived from coffee grounds.To investigate the mechanical properties,natural rubber was filled with carbon black and as-synthesized carbon materials by the internal mixing and compression molding process.Transmission electron microscopy(TEM)was utilized to characterize the dispersion of carbon materials in the rubber matrix.The results of tensile testing showed that the natural rubber mixed with as-synthesized carbon materials from pineapple crowns exhibited 54%and 74%improvement in the ultimate tensile strength and Young’s modulus,respectively,compared with natural rubber without filled carbon materials.The enhancement in mechanical properties by activated carbon materials derived from pineapple crowns can be attributed to the flake-and fiber-like structures and good dispersion of carbon materials in the rubber matrix.In addition,it is higher than that of rubber mixed with carbon black.The results demonstrated that as-synthesized carbon materials from pineapple crowns have the potential materials to substitute carbon black in the rubber compound industry.展开更多
Micrometer-sized,irregularly shaped Ti particles(0.5wt%and 1.0wt%)were mixed with an Al-Si-Mg-Zr matrix powder,and a novel Ti-modified Al-Si-Mg-Zr aluminum alloy was subsequently fabricated via laser-powder bed fusion...Micrometer-sized,irregularly shaped Ti particles(0.5wt%and 1.0wt%)were mixed with an Al-Si-Mg-Zr matrix powder,and a novel Ti-modified Al-Si-Mg-Zr aluminum alloy was subsequently fabricated via laser-powder bed fusion(L-PBF).The results demonstrated that the introduction of Ti particles promoted the formation of near-fully equiaxed grains in the alloy owing to the strong grain refinement of the primary(Al,Si)3(Ti,Zr)nanoparticles.Furthermore,the presence of(Al,Si)3(Ti,Zr)nanoparticles inhibited the decomposition of Si-rich cell boundaries and the precipitation of Si nanoparticles in theα-Al cells.The ultimate tensile strength(UTS),yield strength(YS),and elongation of the asbuilt 0.5wt%Ti(0.5Ti)alloy were(468±11),(350±1)MPa,and(10.0±1.4)%,respectively,which are comparable to those of the L-PBF Al-Si-Mg-Zr matrix alloy and significantly higher than those of traditional L-PBF Al-Si-Mg alloys.After direct aging treatment at 150°C,the precipitation of secondary nanoparticles notably enhanced the strength of the 0.5Ti alloy.Specifically,the 0.5Ti alloy achieved a maximum UTS of(479±11)MPa and YS of(376±10)MPa.At 250°C,the YS of the L-PBF Ti/Al-Si-Mg-Zr alloy was higher than that of the L-PBF Al-Si-Mg-Zr matrix alloy due to the retention of Si-rich cell boundaries,indicating a higher thermal stability.As the aging temperature was increased to 300°C,the dissolution of Si-rich cell boundaries,desolvation of solid-solution elements,and coarsening of nanoprecipitates led to a decrease in the UTS and YS of the alloy to below 300 and 200 MPa,respectively.However,the elongation increased significantly.展开更多
基金supported by Guangdong Major Project of Basic and Applied Basic Research, China (No. 2020B0301030006)Fundamental Research Funds for the Central Universities, China (No. SWU-XDJH202313)+1 种基金Chongqing Postdoctoral Science Foundation Funded Project, China (No. 2112012728014435)the Chongqing Postgraduate Research and Innovation Project, China (No. CYS23197)。
文摘A new method was proposed for preparing AZ31/1060 composite plates with a corrugated interface,which involved cold-pressing a corrugated surface on the Al plate and then hot-pressing the assembled Mg/Al plate.The results show that cold-pressing produces intense plastic deformation near the corrugated surface of the Al plate,which promotes dynamic recrystallization of the Al substrate near the interface during the subsequent hot-pressing.In addition,the initial corrugation on the surface of the Al plate also changes the local stress state near the interface during hot pressing,which has a large effect on the texture components of the substrates near the corrugated interface.The construction of the corrugated interface can greatly enhance the shear strength by 2−4 times due to the increased contact area and the strong“mechanical gearing”effect.Moreover,the mechanical properties are largely depended on the orientation relationship between corrugated direction and loading direction.
基金supported by the National Natural Science Foundation of China(Nos.92166105 and 52005053)High-Tech Industry Science and Technology Innovation Leading Program of Hunan Province(No.2020GK2085)the Science and Technology Innovation Program of Hunan Province(No.2021RC3096).
文摘(NbZrHfTi)C high-entropy ceramics,as an emerging class of ultra-high-temperature materials,have garnered significant interest due to their unique multi-principal-element crystal structure and exceptional hightemperature properties.This study systematically investigates the mechanical properties of(NbZrHfTi)C high-entropy ceramics by employing first-principles density functional theory,combined with the Debye-Grüneisen model,to explore the variations in their thermophysical properties with temperature(0–2000 K)and pressure(0–30 GPa).Thermodynamically,the calculated mixing enthalpy and Gibbs free energy confirm the feasibility of forming a stable single-phase solid solution in(NbZrHfTi)C.The calculated results of the elastic stiffness constant indicate that the material meets the mechanical stability criteria of the cubic crystal system,further confirming the structural stability.Through evaluation of key mechanical parameters—bulk modulus,shear modulus,Young’s modulus,and Poisson’s ratio—we provide comprehensive insight into the macro-mechanical behaviour of the material and its correlation with the underlying microstructure.Notably,compared to traditional binary carbides and their average properties,(NbZrHfTi)C exhibits higher Vickers hardness(Approximately 28.5 GPa)and fracture toughness(Approximately 3.4 MPa⋅m^(1/2)),which can be primarily attributed to the lattice distortion and solid-solution strengthening mechanism.The study also utilizes the quasi-harmonic approximation method to predict the material’s thermophysical properties,including Debye temperature(initial value around 563 K),thermal expansion coefficient(approximately 8.9×10^(−6) K−1 at 2000 K),and other key parameters such as heat capacity at constant volume.The results show that within the studied pressure and temperature ranges,(NbZrHfTi)C consistently maintains a stable phase structure and good thermomechanical properties.The thermal expansion coefficient increasing with temperature,while heat capacity approaches the Dulong-Petit limit at elevated temperatures.These findings underscore the potential of(NbZrHfTi)C applications in ultra-high temperature thermal protection systems,cutting tool coatings,and nuclear structural materials.
基金the National Natural Science Foundation of China (Nos. 52071179, 52271033)the Key Program of National Natural Science Foundation of China (No. 51931003)+2 种基金the Natural Science Foundation of Jiangsu Province, China (No. BK20221493)the Jiangsu Province Leading Edge Technology Basic Research Major Project, China (No. BK20222014)the Foundation of “Qinglan Project” for Colleges and Universities in Jiangsu Province, China。
文摘The composition−property relationship of 18 quaternary high entropy diborides(HEBs)consisting of boron and IVB,VB and VIB transition metals(TM)was investigated using first-principles calculations.A valence electron concentration−relative electronegativity(VEC−REN)composite descriptor was developed to effectively predict the mechanical properties of HEBs.The results demonstrate that with a fixed VEC,the rise of the REN makes HEBs harder but more brittle when the electronegativity of doped TM atoms is lower than that of boron atoms.However,HEBs become softer and more ductile as REN increases if the doped TM atoms have higher electronegativity than boron atoms.The VEC−REN composite descriptor can accurately classify and predict the mechanical properties of HEBs with different components,which provides important theoretical guidance for the rapid design and development of novel high-entropy ceramic materials.
基金supported by the NSFC(12474071)Natural Science Foundation of Shandong Province(ZR2024YQ051)+5 种基金Open Research Fund of State Key Laboratory of Materials for Integrated Circuits(SKLJC-K2024-12)the Shanghai Sailing Program(23YF1402200,23YF1402400)Natural Science Foundation of Jiangsu Province(BK20240424)Taishan Scholar Foundation of Shandong Province(tsqn202408006)Young Talent of Lifting engineering for Science and Technology in Shandong,China(SDAST2024QTB002)the Qilu Young Scholar Program of Shandong University.
文摘The advancement of flexible memristors has significantly promoted the development of wearable electronic for emerging neuromorphic computing applications.Inspired by in-memory computing architecture of human brain,flexible memristors exhibit great application potential in emulating artificial synapses for highefficiency and low power consumption neuromorphic computing.This paper provides comprehensive overview of flexible memristors from perspectives of development history,material system,device structure,mechanical deformation method,device performance analysis,stress simulation during deformation,and neuromorphic computing applications.The recent advances in flexible electronics are summarized,including single device,device array and integration.The challenges and future perspectives of flexible memristor for neuromorphic computing are discussed deeply,paving the way for constructing wearable smart electronics and applications in large-scale neuromorphic computing and high-order intelligent robotics.
基金Natural Science Foundation of Shandong Province of China(ZR2023QE193)。
文摘The microstructures and mechanical properties of Al-8.3Zn-3.3Cu-2.2Mg alloys prepared via hot extrusion and liquid forging methods were investigated.Results show that based on DEFORM simulation analysis,the optimal hot extrusion parameters are determined as ingot initial temperature of 380°C and extrusion speed of 3 mm/s.The hot-extruded aluminum alloy after T6 heat treatment presents superior mechanical properties with yield strength of 519.6 MPa,ultimate tensile strength of 582.1 MPa,and elongation of 11.0%.Compared with the properties of gravity-cast and liquid-forged alloys,the yield strength of hot-extruded alloy increases by 30.8%and 4.9%,and the ultimate tensile strength improves by 43.5%and 10.2%,respectively.The significant improvement in tensile strength of the hot-extruded alloys is attributed to the elimination of casting defects and the refinement of matrix grain and eutectic phases.In addition,the hot-extruded alloy demonstrates superior plasticity compared with the liquid-forged alloy.This is because severe plastic deformation occurs during hot extrusion,which effectively breaks and disperses the eutectic phases,facilitating the dissolution and precipitation of the second phases and inhibiting the microcrack initiation.
基金National MCF Energy R&D Program(2019YFE03100400)。
文摘Ag-Cu-In-Ti low-temperature filler was used to braze the diamond and copper,and the effects of brazing temperature and soaking time on the microstructure and mechanical properties of the joints were investigated.In addition,the joint formation mechanism was discussed,and the correlation between joint microstructure and mechanical performance was established.Results show that adding appropriate amount of In into the filler can significantly reduce the filler melting point and enhance the wettability of filler on diamond.When the brazing temperature is 750°C and the soaking time is 10 min,a uniformly dense braze seam with excellent metallurgical bonding can be obtained,and its average joint shear strength reaches 322 MPa.The lower brazing temperature can mitigate the risk of diamond graphitization and also reduce the residual stresses during joining.
基金Subproject of Inner Mongolia Autonomous Region Key Research and Development and Achievement Transformation Plan Project(2023YFDZ0064,2023KJHZ0020,2022YFDZ0097)Natural Science Foundation of Inner Mongolia Autonomous Region of China(2022QN05040)+1 种基金Basic Research Funds for Directly Affiliated Universities in Inner Mongolia Autonomous Region(JY20220093)Program for Young Talents of Science and Technology in Universities of Inner Mongolia Autonomous Region(NJYT24008)。
文摘Modification of 6061 aluminum alloy was conducted through composite addition of cerium-rich rare earths and Al-Ti-B.Results show that the composite addition of Al-Ti-B and Ce/La element at a specific ratio notably promotes the refinement of the alloy's grains.Ce and La elements are combined with Si and other elements to form rare earth phases,improving the morphology and distribution of precipitates and mitigating the adverse effects ofβ-Fe phases on the microstructure and mechanical properties of alloy.However,excessive rare earth content poses challenges;it not only leads to a decrease in Mg-Si strengthening phase by binding with Si but also promotes the formation of larger or numerous rare earth phases that may act as initiation points for cracks,thereby impeding the improvement of the structure and performance of alloy.The composite addition of cerium-rich rare earths and Al-Ti-B not only preserves the strength of the alloy but also significantly enhances the plasticity of the 6061 as-cast alloy.At a composite addition ratio of Al-Ti-B:RE=2:1,the newly developed 6061-RE aluminum alloy exhibits increased average elongation by 50%and 45%in its as-cast and homogenized states,respectively,compared to the baseline 6061 alloy,facilitating subsequent deformation processing.After solution treatment at 540℃for 1 h and aging at 180℃for 5 h,the average ultimate tensile strength and yield strength of 6061-RE alloys reach 313.2 and 283.1 MPa,increased by 12.3%and 14.5%compared with those of the original alloy,respectively,and the average elongation is improved by 41%.
基金National Natural Science Foundation of China(52105385)Stable Support Plan Program of Shenzhen Natural Science Fund(20220810132537001)+2 种基金Guangdong Basic and Applied Basic Research Foundation(2022A1515010781)Joint Fund of Henan Province Science and Technology R&D Program(225200810002)Fundamental Research Funds of Henan Academy of Sciences(240621041)。
文摘To enhance the mechanical properties of Mo alloys prepared through laser powder bed fusion(LPBF),a hot isostatic pressing(HIP)treatment was used.Results show that following HIP treatment,the porosity decreases from 0.27%to 0.22%,enabling the elements Mo and Ti to diffuse fully and to distribute more uniformly,and to forming a substantial number of low-angle grain boundaries.The tensile strength soars from 286±32 MPa to 598±22 MPa,while the elongation increases from 0.08%±0.02%to 0.18%±0.02%,without notable alterations in grain morphology during the tensile deformation.HIP treatment eliminates the molten pool boundaries,which are the primary source for premature failure in LPBFed Mo alloys.Consequently,HIP treatment emerges as a novel and effective approach for strengthening the mechanical properties of LPBFed Mo alloys,offering a fresh perspective on producing high-performance Mo-based alloys.
基金supported by the National Natural Sci-ence Foundation of China[No.51564032]Yunnan Provin-cial Department of Education Science Research Fund Project[KKPH202132005]the Analysis and Testing Founda-tion of Kunming University of Science and Technology[2022M20212130086].
文摘The performances of magnesium alloys remain insufficient to further enhance the application potential of ultralight magnesium alloys.In this work,a Mg-8Li-3Y-2Zn alloy was prepared through vacuum melting and subsequent heat treatment at 300,450,and 500°C.The material properties of the resulting samples were assessed through microstructural observation,tensile testing,electrical conductivity measurements,and electromagnetic shielding effectiveness(EMI-SE)testing.The influence of the Mg-8Li-3Y-2Zn alloy microstructure on its mechanical and electromagnetic shielding properties in different states was investigated.It was found that the as-cast alloy containsα-Mg,β-Li,Mg_(3)Zn_(3)Y_(2),and Mg_(12)ZnY phases.Following heat treatment at 500℃(HT500),the blockα-Mg phase transformedfine needle-shapes,its tensile strength increased to 263.7 MPa,and its elongation reached 45.3%.The mechanical properties of the alloy were significantly improved by the synergistic effects imparted by the needle-shapedα-Mg phase,solid solution strengthening,and precipitation strengthening.The addition of Y and Zn improved the EMI-SE of Mg-8Li-1Zn alloy,wherein the HT500 sample exhibits the highest SE,maintaining a value of 106.7–76.9 dB in the frequency range of 30–4500 MHz;this performance has rarely been reported for electromagnetically shielded alloys.This effect was mainly attributed to the multiple reflections of electromagnetic waves caused by the severe impedance mismatch of the abundant phase boundaries,which were in turn provided by the dual-phase(α/β)and secondary phases.Furthermore,the presence of nano-precipitation was also believed to enhance the absorption of electromagnetic waves.
基金supported by the National Science Fund for Distinguished Young Scholars of China(No.52025014)Zhejiang Provincial Natural Science Foundation of China(Nos.LZJWY23E090001 and LD24E010003)the Natural Science Foundation of Ningbo(No.2022J305).
文摘High-entropy materials possess high hardness and strong wear resistance,yet the key bottleneck for their practical applications is the poor corrosion resistance in harsh environments.In this work,the high-entropy nitride(HEN)coatings of(MoNbTaTiZr)1-x Nx(x=0-0.47)were fabricated using a hybrid di-rect current magnetron sputtering technique.The research focus was dedicated to the effect of nitrogen content on the microstructure,mechanical and electrochemical properties.The results showed that the as-deposited coatings exhibited a typical body-centered cubic(BCC)structure without nitrogen,while the amorphous matrix with face-centered cubic(FCC)nanocrystalline grain was observed at x=0.17.Further increasing x in the range of 0.35-0.47 caused the appearance of polycrystalline FCC phase in structure.Compared with the MoNbTaTiZr metallic coating,the coating containing nitrogen favored the high hard-ness around 13.7-32.4 GPa,accompanied by excellent tolerance both against elastic and plastic deforma-tion.Furthermore,such N-containing coatings yielded a low corrosion current density of about 10−8-10−7 A/cm^(2) and high electrochemical impedance of 10^(6)Ωcm^(2) in 3.5 wt.%NaCl solution,indicating the supe-rior corrosion resistance.The reason for the enhanced electrochemical behavior could be ascribed to the spontaneous formation of protective passive layers over the coating surface,which consisted of the domi-nated multi-elemental oxides in chemical stability.Particularly,noted that the(MoNbTaTiZr)_(0.83) N0.17 coat-ing displayed the highest hardness of 32.4±2.6 GPa and H/E ratio at 0.09,together with remarkable cor-rosion resistance,proposing the strongest capability for harsh-environmental applications required both good anti-wear and anti-corrosion performance.
基金support from CAS Project for Young Scientists in Basic Research(YSBR-025)and the Technology Innovation(RCJJ-145-24-39)R.P.Guo acknowledges the financial support from the National Natural Science Foundation of China(No.52401104)+1 种基金the Fundamental Research Program of Shanxi Province(No.202203021221072)the China Postdoctoral Science Foundation(No.2024M753298).
文摘Hot isostatic pressing (HIP) temperature has a significant impact on the service performance of powder metallurgy titanium alloys. In this study, a high-temperature titanium alloy, Ti-6.5Al-3.5Mo-1.5Zr-0.3Si, was prepared under different HIP temperatures (880–1000℃), and the microstructural evolution and mechanical properties were systematically investigated. The results demonstrated that the HIPed alloys were predominantly composed of more than 80 vol.% α phase and a small amount of β phase, and their phase compositions were basically unaffected by the HIP temperatures. Under the typical single-temperature-maintained HIP (STM-HIP) regime, the microstructure of alloy significantly coarsened as the HIP temperature increased, and the alloy strength exhibited an obvious linear negative correlation with the HIP temperature. On the basis of Hall–Petch relation, the prediction model of grain size was established, and the mathematical equation between HIP temperature and grain size (d=M(T_(HIP-N)^(-2))) was deduced. Furthermore, a possible evolution mechanism of microstructure was proposed, which could be divided into the decomposition of initial α′ martensite for as-received powder, formation of the globular α grains in prior particle boundaries (PPBs) region, and precipitation of the platelet α grains in non-PPBs region. For these alloys prepared by the dual-temperature-maintained HIP (DTM-HIP) regime, although their tensile properties were comparable to that of alloy prepared by STM-HIP regime with same high-temperature holding stage, higher proportion of globular α grains occurred due to more recrystallization nucleation during the low-temperature holding stage, which probably provided a solution for improving the dynamic service performance of HIPed alloys.
基金the National Natural Science Foundation of China(No.52165026)。
文摘Irregular bone scaffolds fabricated using the Voronoi tessellation method resemble the morphology and properties of human cancellous bones.This has become a prominent topic in bone tissue engineering research in recent years.However,studies on the radial-gradient design of irregular bionic scaffolds are limited.Therefore,this study aims to develop a radial-gradient structure similar to that of natural long bones,enhancing the development of bionic bone scaffolds.A novel gradient method was adopted to maintain constant porosity,control the seed site-specific distribution within the irregular porous structure,and vary the strut diameter to generate radial gradients.The irregular scaffolds were compared with four conventional scaffolds(cube,pillar BCC,vintiles,and diamond)in terms of permeability,stress concentration characteristics,and mechanical properties.The results indicate that the radial-gradient irregular porous structure boasts the widest permeability range and superior stress distribution compared to conventional scaffolds.With an elastic modulus ranging from 4.20 GPa to 22.96 GPa and a yield strength between 68.37 MPa and 149.40 MPa,it meets bone implant performance requirements and demonstrates significant application potential.
基金supported by the National Natural Science Foundation of China(Nos.42171108 and 42101136)Sichuan Science and Technology Program(Nos.2024NSFSC2007 and2025YFHZ0273)Natural Science Starting Project of SWPU(No.2024QHZ029)。
文摘In cold regions,slope rocks are inevitably impacted by freeze-thaw,dry-wet cycles and their alternating actions,leading to strength weakening and pore degradation.In this study,the mechanical and microstructural properties of schist subjected to four conditions were investigated:freeze-thaw cycles in air(FTA),freeze-thaw cycles in water(FTW),dry-wet cycles(DW),and dry-wet-freeze-thaw cycles(DWFT).Uniaxial compressive strength(UCS),water absorption,ultrasonication,low-field nuclear magnetic resonance,and scanning electron microscopy analyses were conducted.The integrity attenuation characteristics of the longitudinal wave velocity,UCS,and elastic modulus were analyzed.The results showed that liquid water emerged as a critical factor in reducing the brittleness of schist.The attenuation function model accurately described the peak stress and static elastic modulus of schist in various media(R2>0.97).Different media affected the schist deterioration and half-life,with the FTW-immersed samples having a half-life of 28 cycles.Furthermore,the longitudinal wave velocity decreased as the number of cycles increased,with the FTW showing the most significant reduction and having the shortest half-life of 208 cycles.Moreover,the damage variables of compressive strength and elastic modulus increased with the number of cycles.After 40 cycles,the schist exposed to FTW exhibited the highest damage variables and saturated water content.
基金supported by the National Key Research and Development Program of China(No.SQ2021YFF 0600011).
文摘7039 Al alloys are widely used in armor vehicles,given the material’s high specific strength and fracture toughness.However,laminar tearing in the thickness plane of the base metal(BM),specifically in the normal direction(ND)and rolling direction(RD)plane,was occasionally observed after the welding of thick plates,resulting in premature material failure.A vertically metal-inert gas(MIG)-welded laminar tearing component of a 30 mm thick plate was analyzed to determine the factors associated with this phenomenon.The texture,residual stress,microhardness,and tensile properties were also investigated.The results indicated that the crack extended along the RD as a transcrystalline fracture and terminated at the BM.The grains near the crack grew preferentially in the(001)crystal direction.Furthermore,the tensile strength(83 MPa)and elongation(6.8%)in the RD were relatively higher than those in the ND.In particular,the primary factors for crack initiation include stronger texture,higher dislocation density,increased Al_(7)Cu_(2)Fe phases,lower proportion of small-angle grain boundaries,and varying grain sizes in different regions,leading to the fragile microstructure.The higher residual stress of the BM promotes the formation and extension of cracks.The restraining force due to fixation and welding shrinkage force transformed the crack into laminar tearing.Preventive measures of laminar tearing were also proposed.
基金supported by the Key Project of Chinese Academy of Engineering(No.2019-XZ-11)the General Project of Chinese Academy of Engineering(No.2023-XY-18)+1 种基金the Open Fund of National Joint Engineering Research Center for Abrasion Control and Molding of Metal Materials of China(No.HKDNM201907)the Independent Project of State Key Laboratory of Powder Metallurgy,China。
文摘To tackle the common issue of green defects in material extrusion(MEX)additive manufacturing(AM)cemented carbides,warm isostatic pressing(WIP)was introduced to eliminate defects of MEX WC-9Co cemented carbide greens,thereby improving both microstructure uniformity and mechanical properties of sintered bodies.The results indicate that WIP reduces defects in MEX greens,thus decreasing the dimensions and numbers of defects,modifying shapes of pores within sintered bodies,while preserving surface quality and shape characteristics.Compared with WC-9Co prepared via MEX followed by debinding and sintering(DS),the hardness of WC-9Co prepared using MEX-WIP-DS does not change significantly,ranging HV_(30)1494-1508,the transverse rupture strength increases by up to 49.3%,reaching 2998-3514 MPa,and the fracture toughness remains high,ranging 14.8-17.0 MPa·m^(1/2).The mechanical properties surpass comparable cemented carbides fabricated through other AM methods and are comparable to those produced by powder metallurgy.The integration of green WIP into MEX-DS broadens the MEX processing window,and improves the overall mechanical properties of MEX AM WC-Co cemented carbides.
基金supported by the National Key R&D Plan Program of China(No.2021YFB3400800)Henan Key Research and Development Program(No.231111241000)+1 种基金the Joint Fund of Henan Province Science and Technology R&D Program(No.225200810026)Zhongyuan Scholar Workstation Funded Program(No.224400510025).
文摘Electrolytic copper foil has gained significant attention as an essential component in lithium-ion batteries(LIBs),printed circuit boards(PCBs),and chip packaging substrates(CPSs)applications.With the advancement of LIBs towards higher energy densities and the increasing density of electronic components on circuits,copper foil is required to have demanding properties,such as extremely thin thickness and extremely high tensile strength.This comprehensive review firstly summarizes recent progress on the fabrication of electrolytic copper foil,and the effects of process parameters,cathode substrate,and additives on the electrodeposition behavior,microstructure,and properties of copper foil are discussed in detail.Then the regulation strategies of mechanical properties of electrolytic copper foil are also summarized,including the formation of nanotwins and texture.Furthermore,the recent advances in novel electrolytic copper foils,such as composite foils and extra-thin copper foils,are also overviewed.Lastly,the remaining challenges and perspectives on the further development of electrolytic copper foils are presented.
基金supported by Beijing Nova Program(No.20230484371)the National Key Research and Development Program of China(No.2021YFB3700700).
文摘The effect of Cr addition on nickel aluminium bronze(NAB)alloy microstructure,mechanical properties,and erosion-corrosion behaviour has been studied.The results show that Cr addition does not change the composition of the precipitated phases,more Cr entered theκphase and a small amount of Cr solubilized in the matrix,which increase the hardness of theκand matrix and decrease the potential difference between theκand matrix.NAB alloy with Cr shows high erosion-corrosion resistance at high flow rate conditions,due to its lower phase potential difference and higher surface hardness.At the flow rate of 3 m·s^(-1),the corrosion rate is 0.076 mm·year^(-1),which is~20%lower than that of the unadded Cr sample.Moreover,the corrosion product film contains Cr_(2)O_(3)and Cr^(3+),which improves the densification of the film and raises alloy’s corrosion resistance with Cr addition.The combination of mechanical and corrosion resistant properties may qualify this alloy as a potential candidate material for sustainable and safe equipment.
基金funded by Faculty of Engineering,Burapha University,grant number 003/2567.
文摘Herein,cure characteristics,morphology,and mechanical properties of natural rubber filled with activated carbon-based materials were investigated.Carbon-based materials were prepared from bagasse,coffee grounds and pineapple crowns by the pyrolysis method at temperatures in the range of 300℃.As-synthesized carbon materials were characterized by optical microscopy(OM),scanning electron microscopy(SEM),and Fourier-transform infrared spectroscopy(FTIR)to analyze size distribution,morphology,and functional groups,respectively.OM and SEM analysis revealed that particles,flakes,and a small quantity of fiber-like carbon were obtained using bagasse and pineapple crown as raw materials,while honeycomb-like carbon materials can be derived from coffee grounds.To investigate the mechanical properties,natural rubber was filled with carbon black and as-synthesized carbon materials by the internal mixing and compression molding process.Transmission electron microscopy(TEM)was utilized to characterize the dispersion of carbon materials in the rubber matrix.The results of tensile testing showed that the natural rubber mixed with as-synthesized carbon materials from pineapple crowns exhibited 54%and 74%improvement in the ultimate tensile strength and Young’s modulus,respectively,compared with natural rubber without filled carbon materials.The enhancement in mechanical properties by activated carbon materials derived from pineapple crowns can be attributed to the flake-and fiber-like structures and good dispersion of carbon materials in the rubber matrix.In addition,it is higher than that of rubber mixed with carbon black.The results demonstrated that as-synthesized carbon materials from pineapple crowns have the potential materials to substitute carbon black in the rubber compound industry.
基金supported by the National Natural Science Foundation of China(Nos.52001140 and 52475361).
文摘Micrometer-sized,irregularly shaped Ti particles(0.5wt%and 1.0wt%)were mixed with an Al-Si-Mg-Zr matrix powder,and a novel Ti-modified Al-Si-Mg-Zr aluminum alloy was subsequently fabricated via laser-powder bed fusion(L-PBF).The results demonstrated that the introduction of Ti particles promoted the formation of near-fully equiaxed grains in the alloy owing to the strong grain refinement of the primary(Al,Si)3(Ti,Zr)nanoparticles.Furthermore,the presence of(Al,Si)3(Ti,Zr)nanoparticles inhibited the decomposition of Si-rich cell boundaries and the precipitation of Si nanoparticles in theα-Al cells.The ultimate tensile strength(UTS),yield strength(YS),and elongation of the asbuilt 0.5wt%Ti(0.5Ti)alloy were(468±11),(350±1)MPa,and(10.0±1.4)%,respectively,which are comparable to those of the L-PBF Al-Si-Mg-Zr matrix alloy and significantly higher than those of traditional L-PBF Al-Si-Mg alloys.After direct aging treatment at 150°C,the precipitation of secondary nanoparticles notably enhanced the strength of the 0.5Ti alloy.Specifically,the 0.5Ti alloy achieved a maximum UTS of(479±11)MPa and YS of(376±10)MPa.At 250°C,the YS of the L-PBF Ti/Al-Si-Mg-Zr alloy was higher than that of the L-PBF Al-Si-Mg-Zr matrix alloy due to the retention of Si-rich cell boundaries,indicating a higher thermal stability.As the aging temperature was increased to 300°C,the dissolution of Si-rich cell boundaries,desolvation of solid-solution elements,and coarsening of nanoprecipitates led to a decrease in the UTS and YS of the alloy to below 300 and 200 MPa,respectively.However,the elongation increased significantly.