Chemical vapor deposition(CVD) of SiC from methyltrichlorosilane(MTS) was studied at two different molar ratios of H2 to MTS(n(H2) /n(MTS) ) . The total pressure was kept as 100 kPa and the temperature was varied from...Chemical vapor deposition(CVD) of SiC from methyltrichlorosilane(MTS) was studied at two different molar ratios of H2 to MTS(n(H2) /n(MTS) ) . The total pressure was kept as 100 kPa and the temperature was varied from 850 to 1 100 ℃ at a total residence time of 1 s. Steady-state deposition rates as functions of reactor length and of temperature,investigated at different n(H2) /n(MTS) values,show that hydrogen exhibits strongly influences on the deposition rate. Especially,the deposition of Si co-deposit can be obtained in broader substrate length and at higher temperatures with increasing hydrogen partial pressure. Influence of hydrogen on the deposition process was also studied using gas phase composition and deposit composition analysis at various n(H2) /n(MTS) . SEM micrographs directly show the variation of surface morphologies at various n(H2) /n(MTS) . It can be found that the crystal grain of the deposit at 1 100 ℃ is better developed and the crystallization is also improved with increasing n(H2) /n(MTS) .展开更多
A silylated melamine sponge(SMS)was prepared by two simple steps,namely,immersion and dehydration of a melamine sponge coated with methyltrichlorosilane.The silylated structure of SMS was characterized by FT-IR(Fourie...A silylated melamine sponge(SMS)was prepared by two simple steps,namely,immersion and dehydration of a melamine sponge coated with methyltrichlorosilane.The silylated structure of SMS was characterized by FT-IR(Fourier-transform infrared)spectroscopy,SEM(Scanning electron microscopy)and in terms of water contact angles.Its oil-water absorption and separation capacities were measured by FT-IR and UV-visible spectrophoto-metry.The experimental results have shown that oligomeric silanol covalently bonds by Si-N onto the surface of melamine sponge skeletons.SMS has shown superhydrophobicity with a water contact angle exceeding 150°±1°,a better separation efficiency with regard to diesel oil(by 99.31%(wt/wt%)in oil-water mixture and even up to 99.99%(wt/wt%)for diesel oil in its saturated aqueous solution.Moreover,SMS inherited the intrinsicflame retardancy of the melamine sponge.In general,SMS has shown superhydrophobicity,high porosity,excellent selectivity,remarkable recyclability,and better absorption capacity for various oils and organic solvents,and a high separation efficiency for oil in saturated aqueous solutions.展开更多
基金Project supported by the One Hundred Talents Program of Chinese Academy of Sciences
文摘Chemical vapor deposition(CVD) of SiC from methyltrichlorosilane(MTS) was studied at two different molar ratios of H2 to MTS(n(H2) /n(MTS) ) . The total pressure was kept as 100 kPa and the temperature was varied from 850 to 1 100 ℃ at a total residence time of 1 s. Steady-state deposition rates as functions of reactor length and of temperature,investigated at different n(H2) /n(MTS) values,show that hydrogen exhibits strongly influences on the deposition rate. Especially,the deposition of Si co-deposit can be obtained in broader substrate length and at higher temperatures with increasing hydrogen partial pressure. Influence of hydrogen on the deposition process was also studied using gas phase composition and deposit composition analysis at various n(H2) /n(MTS) . SEM micrographs directly show the variation of surface morphologies at various n(H2) /n(MTS) . It can be found that the crystal grain of the deposit at 1 100 ℃ is better developed and the crystallization is also improved with increasing n(H2) /n(MTS) .
基金funded by Qingyang Science and Technology Support Project(KT2019-03)。
文摘A silylated melamine sponge(SMS)was prepared by two simple steps,namely,immersion and dehydration of a melamine sponge coated with methyltrichlorosilane.The silylated structure of SMS was characterized by FT-IR(Fourier-transform infrared)spectroscopy,SEM(Scanning electron microscopy)and in terms of water contact angles.Its oil-water absorption and separation capacities were measured by FT-IR and UV-visible spectrophoto-metry.The experimental results have shown that oligomeric silanol covalently bonds by Si-N onto the surface of melamine sponge skeletons.SMS has shown superhydrophobicity with a water contact angle exceeding 150°±1°,a better separation efficiency with regard to diesel oil(by 99.31%(wt/wt%)in oil-water mixture and even up to 99.99%(wt/wt%)for diesel oil in its saturated aqueous solution.Moreover,SMS inherited the intrinsicflame retardancy of the melamine sponge.In general,SMS has shown superhydrophobicity,high porosity,excellent selectivity,remarkable recyclability,and better absorption capacity for various oils and organic solvents,and a high separation efficiency for oil in saturated aqueous solutions.