A series samples of La0.6M0.4FeO3-δ （M = Ca, Sr, process （GNP）. FTIR, TG-DSC, XRD and TEM techniques Ba） perovskite-type oxides were prepared by glycine nitrate were used to characterize the chemical constitution...A series samples of La0.6M0.4FeO3-δ （M = Ca, Sr, process （GNP）. FTIR, TG-DSC, XRD and TEM techniques Ba） perovskite-type oxides were prepared by glycine nitrate were used to characterize the chemical constitution, thermal stability and phase structure. The electrical conductivity of the samples was investigated by four-probe technique. With the increase of substituted-ionic radius, the temperature of phase formation increases, and the solid solubility decreases gradually, respectively. The La0.6Ca0.4FeO3-δ（LCF）powder is pure cubic perovskite-type crystalline after fired at 850℃ for 2 h. The XRD patterns of La0.6Sr0.4FeO3-δ（LSF） powder shows a small quantity of SrO peaks sintered at 1050℃ for 2 h. The electrical conductivity of LCF and LSF at 500 - 800℃ is over 100 S·cm^ - 1, and the value of LCF is 1170 S·cm^ - 1 at 800℃, which indicate that LCF and LSF may be used as a profitable cathode for IT-SOFCs. The characteristic of La0.6 Ba0.4FeO3-δ（LBF） is poor, and the electrical conductivity at intermediate temperatures is 1/20 less than that of LSF.展开更多
基金National Natural Science Foundation of China(51261003)National Key Basic Research Development Program of China("973"Program)(2010CB631303)Natural Science Foundation of Guangxi(2012 GXNSFGA060002,2011GXNSFD018004)
基金Project Supported bythe Natural Science Foundation of Bureau Education Anhui Province (N2004kj326)
文摘A series samples of La0.6M0.4FeO3-δ （M = Ca, Sr, process （GNP）. FTIR, TG-DSC, XRD and TEM techniques Ba） perovskite-type oxides were prepared by glycine nitrate were used to characterize the chemical constitution, thermal stability and phase structure. The electrical conductivity of the samples was investigated by four-probe technique. With the increase of substituted-ionic radius, the temperature of phase formation increases, and the solid solubility decreases gradually, respectively. The La0.6Ca0.4FeO3-δ（LCF）powder is pure cubic perovskite-type crystalline after fired at 850℃ for 2 h. The XRD patterns of La0.6Sr0.4FeO3-δ（LSF） powder shows a small quantity of SrO peaks sintered at 1050℃ for 2 h. The electrical conductivity of LCF and LSF at 500 - 800℃ is over 100 S·cm^ - 1, and the value of LCF is 1170 S·cm^ - 1 at 800℃, which indicate that LCF and LSF may be used as a profitable cathode for IT-SOFCs. The characteristic of La0.6 Ba0.4FeO3-δ（LBF） is poor, and the electrical conductivity at intermediate temperatures is 1/20 less than that of LSF.