Micron sized hexagon- and flower-like nanostructures of lead oxide（α-PbO2） have been synthesized by very simple and cost effective route of anodic oxidation of lead sheet. These structures were easily obtained by t...Micron sized hexagon- and flower-like nanostructures of lead oxide（α-PbO2） have been synthesized by very simple and cost effective route of anodic oxidation of lead sheet. These structures were easily obtained by the simple variation of applied voltage from 2-6 V between the electrodes. Lead sheet was used as an anode and platinum sheet served as a cathode. Anodic oxidation at 2 V resulted in the variable edge sized（1-2 μm） hexagon-like structures in the electrolyte. When the applied potential was increased to 4 V a structure of distorted hexagons consisting of some flower-like structures were obtained. Further increment of potential up to 6 V resulted in flower like structures of α-PbO2 having six petals. The diameter of the flower-like structures was 200-500 nm and the size of a petal was 100-200 nm.展开更多
基金financial support from USACH-Chile, Council of Scientific and Industrial Research (CSIR) and University Grant Commission (UGC) New Delhi, India
文摘Micron sized hexagon- and flower-like nanostructures of lead oxide（α-PbO2） have been synthesized by very simple and cost effective route of anodic oxidation of lead sheet. These structures were easily obtained by the simple variation of applied voltage from 2-6 V between the electrodes. Lead sheet was used as an anode and platinum sheet served as a cathode. Anodic oxidation at 2 V resulted in the variable edge sized（1-2 μm） hexagon-like structures in the electrolyte. When the applied potential was increased to 4 V a structure of distorted hexagons consisting of some flower-like structures were obtained. Further increment of potential up to 6 V resulted in flower like structures of α-PbO2 having six petals. The diameter of the flower-like structures was 200-500 nm and the size of a petal was 100-200 nm.