La 4- x (P 2O 5) 3:Eu x were synthesized from a mixed solution of La(NO 3) 3 and Eu(NO 3) 3 in nitric acid solution(pH=4.5) followed by precipitation on addition of Na 4P 2O 7 solution and calcination at 900 ℃. The p...La 4- x (P 2O 5) 3:Eu x were synthesized from a mixed solution of La(NO 3) 3 and Eu(NO 3) 3 in nitric acid solution(pH=4.5) followed by precipitation on addition of Na 4P 2O 7 solution and calcination at 900 ℃. The products showed a highest excitation peak at 349 nm and highest emission peak at 596 nm .展开更多
采用溶胶-凝胶的方法低温制备石榴石结构的固体电解质Li5La3Ta2O12,并用其包覆Li Mn2O4来改善材料的电化学性能。通过XRD,SEM和TEM等表征手段对材料的结构和形貌进行分析,并通过恒电流充放电、循环伏安、交流阻抗等测试分析材料的电化...采用溶胶-凝胶的方法低温制备石榴石结构的固体电解质Li5La3Ta2O12,并用其包覆Li Mn2O4来改善材料的电化学性能。通过XRD,SEM和TEM等表征手段对材料的结构和形貌进行分析,并通过恒电流充放电、循环伏安、交流阻抗等测试分析材料的电化学性能。研究结果表明:Li5La3Ta2O12包覆的Li Mn2O4材料与未包覆的材料相比,其电化学性能得到明显改善,经过150次循环后包覆材料的放电比容量保持率为92%,在高倍率10C(C为倍率)下包覆材料放电比容量为61.2 m A·h/g,而未包覆材料放电比容量仅为40.7 m A·h/g;包覆Li5La3Ta2O12后,Li Mn2O4的阻抗明显减小,大幅度提高了其循环性能和倍率性能。展开更多
文摘La 4- x (P 2O 5) 3:Eu x were synthesized from a mixed solution of La(NO 3) 3 and Eu(NO 3) 3 in nitric acid solution(pH=4.5) followed by precipitation on addition of Na 4P 2O 7 solution and calcination at 900 ℃. The products showed a highest excitation peak at 349 nm and highest emission peak at 596 nm .
文摘采用溶胶-凝胶的方法低温制备石榴石结构的固体电解质Li5La3Ta2O12,并用其包覆Li Mn2O4来改善材料的电化学性能。通过XRD,SEM和TEM等表征手段对材料的结构和形貌进行分析,并通过恒电流充放电、循环伏安、交流阻抗等测试分析材料的电化学性能。研究结果表明:Li5La3Ta2O12包覆的Li Mn2O4材料与未包覆的材料相比,其电化学性能得到明显改善,经过150次循环后包覆材料的放电比容量保持率为92%,在高倍率10C(C为倍率)下包覆材料放电比容量为61.2 m A·h/g,而未包覆材料放电比容量仅为40.7 m A·h/g;包覆Li5La3Ta2O12后,Li Mn2O4的阻抗明显减小,大幅度提高了其循环性能和倍率性能。