Li2FeSiO4 is deemed to be a potential candidate for large-scale applications because of its abundance,low cost and high safety,etc.Unfortunately,its low conductivity,resulting in poor rate performance,has become a mai...Li2FeSiO4 is deemed to be a potential candidate for large-scale applications because of its abundance,low cost and high safety,etc.Unfortunately,its low conductivity,resulting in poor rate performance,has become a main obstacle to its applications in power battery and energy storage system.In this work,C-Ag coated Li2FeSiO4 is introduced to improve the innate electronic conductivity and Li-ion diffusion ability.The results demonstrate that Li2FeSiO4/C/Ag composite exhibits better electrochemical performance.It possesses a specific discharge capacity of 152,121,108 mA.h/g at 0.2C,5C and 10C,respectively.At the same time,the Li2FeSiO4/C/Ag composite shows good cycle stability and a capacity retention ratio of 97.9%after 100 cycles at 1C.展开更多
Nanosphere-like Li2FeSiO4/C was synthesized via a solution method using sucrose as carbon sources under a mild condition of time-saving and energy-saving, followed by sintering at high temperatures for crystallization...Nanosphere-like Li2FeSiO4/C was synthesized via a solution method using sucrose as carbon sources under a mild condition of time-saving and energy-saving, followed by sintering at high temperatures for crystallization. The amount of carbon in the composite is less than 10% （mass fraction）, and the X-ray diffraction result confirms that the sample is of pure single phase indexed with the orthorhombic Pmn21 space group. The particle size of the Li2FeSiO4/C synthesized at 700 °C for 9 h is very fine and spherical-like with a size of 200 nm. The electrochemical performance of this material, including reversible capacity, cycle number, and charge-discharge characteristics, were tested. The cell of this sample can deliver a discharge capacity of 166 mA-h/g at C/20 rate in the first three cycles. After 30 cycles, the capacity decreases to 158 mA-h/g, and the capacity retention is up to 95%. The results show that this method can prepare nanosphere-like Li2FeSiO4/C composite with good electrochemical performance.展开更多
基金Project(21771062)supported by the National Natural Science Foundation of ChinaProject(2016JJ2092)supported by the Hunan Provincial Natural Science Foundation,ChinaProject(2019013)supported by the Open Project Program of Key Laboratory of Preparation and Application of Environmental Friendly Materials,Ministry of Education,Jilin Normal University,China
文摘Li2FeSiO4 is deemed to be a potential candidate for large-scale applications because of its abundance,low cost and high safety,etc.Unfortunately,its low conductivity,resulting in poor rate performance,has become a main obstacle to its applications in power battery and energy storage system.In this work,C-Ag coated Li2FeSiO4 is introduced to improve the innate electronic conductivity and Li-ion diffusion ability.The results demonstrate that Li2FeSiO4/C/Ag composite exhibits better electrochemical performance.It possesses a specific discharge capacity of 152,121,108 mA.h/g at 0.2C,5C and 10C,respectively.At the same time,the Li2FeSiO4/C/Ag composite shows good cycle stability and a capacity retention ratio of 97.9%after 100 cycles at 1C.
基金Project supported by Ministry of Education Key Laboratory of Synthetic and Natural Functional Molecular Chemistry, China Project (2010JK765) supported by the Education Department of Shaanxi Province, China
文摘Nanosphere-like Li2FeSiO4/C was synthesized via a solution method using sucrose as carbon sources under a mild condition of time-saving and energy-saving, followed by sintering at high temperatures for crystallization. The amount of carbon in the composite is less than 10% （mass fraction）, and the X-ray diffraction result confirms that the sample is of pure single phase indexed with the orthorhombic Pmn21 space group. The particle size of the Li2FeSiO4/C synthesized at 700 °C for 9 h is very fine and spherical-like with a size of 200 nm. The electrochemical performance of this material, including reversible capacity, cycle number, and charge-discharge characteristics, were tested. The cell of this sample can deliver a discharge capacity of 166 mA-h/g at C/20 rate in the first three cycles. After 30 cycles, the capacity decreases to 158 mA-h/g, and the capacity retention is up to 95%. The results show that this method can prepare nanosphere-like Li2FeSiO4/C composite with good electrochemical performance.