The 3-sheet structure of Inconel 718 superalloy will be used in flying vehicles as heat resisting and shielding structure due to its lightweight, high strength and stiffness. The 3-sheet structure of Inconel 718 super...The 3-sheet structure of Inconel 718 superalloy will be used in flying vehicles as heat resisting and shielding structure due to its lightweight, high strength and stiffness. The 3-sheet structure of Inconel 718 superalloy processed by LBW/SPF (laser beam welding/superplastic forming) technology exhibited good configuration and uniform thickness distribution. The LBW parameters for 3-sheet structure were as follows: Pulse frequency was 32 Hz, impulse duration 3 ms, peak power per pulse 4500 W, and welding speed 180 mm/min. The SPF parameters were as follows: Temperature T=965°C, forming pressure P=4.2 MPa, and forming time t=130 min. The microstructure in weld fusion zone was constituted of austenite dendritics and Laves phase precipitated in interdendritics. After the SPF process, austenite dendritics in the weld fusion became coarser and most of Laves phases were dissolved and turned into δ precipitated phase, but a few of Laves phases were still reserved. And Nb concentration in dendritics increased to 5.42% compared to 2.82% in as-weld condition. Weld metal Vickers-hardness increased from 331.63 in as-weld condition to 391.74 in post-SPF condition which was closed to the base material Vickers-hardness of post-SPF. Grain size of base material grew slightly and an amount of precipitated phase appeared in the base material undergoing SPF process. The tensile test results of base material showed that tensile strength increased obviously and the ductility decreased slightly after SPF process. Load response test results indicated that the 3-sheet structure possessed good resistance to compression and bending load. Accordingly, the LBW/SPF technology is an appropriate forming technique for the 3-sheet structure of Inconel 718 superalloy.展开更多
The characteristics of 5A90 Aluminum-Lithium alloy by YAG laser and MIG arc hybrid welding (Hybrid welding) were studied.Compared with the laser beam welding (LBW),the hybrid welding could not only improve the weld ap...The characteristics of 5A90 Aluminum-Lithium alloy by YAG laser and MIG arc hybrid welding (Hybrid welding) were studied.Compared with the laser beam welding (LBW),the hybrid welding could not only improve the weld appearance significantly,but also have better engineering compatibility.The obvious microstructure characteristics of joint by the hybrid welding are fine-grained layer near fusion-line and the equiaxed grain in most area of welded seam.The subgrains of the equiaxed grains,located in the weld center,tend to coarse from bottom to top of weld joint.The microhardness of welded seam by the hybrid welding (83.57HV0.2) is lower than that by LBW (95.65HV0.2),but the uniformity of the former is better than that of the latter.The ultimate strength and the elongations after fracture of the joint by the hybrid welding are lower than that by LBW.The tensile fracture always occurs in HAZ or weld centerline,and the fractography presents mixture rupture.Therefore,if the combined mechanical properties of joint by the hybrid welding meet the operation requirements,it should be improved by reasonable artificial aging or heat treatment after welding,and it also should develop a better filler wire matched with the base metal.展开更多
基金Supported by the National Natural Science Foundation of China (Grant No. 50672106)the Intellectual Innovation Project of the Chinese Academy of Sciences (Grant No. KJCX3-SYW.No.12)
文摘The 3-sheet structure of Inconel 718 superalloy will be used in flying vehicles as heat resisting and shielding structure due to its lightweight, high strength and stiffness. The 3-sheet structure of Inconel 718 superalloy processed by LBW/SPF (laser beam welding/superplastic forming) technology exhibited good configuration and uniform thickness distribution. The LBW parameters for 3-sheet structure were as follows: Pulse frequency was 32 Hz, impulse duration 3 ms, peak power per pulse 4500 W, and welding speed 180 mm/min. The SPF parameters were as follows: Temperature T=965°C, forming pressure P=4.2 MPa, and forming time t=130 min. The microstructure in weld fusion zone was constituted of austenite dendritics and Laves phase precipitated in interdendritics. After the SPF process, austenite dendritics in the weld fusion became coarser and most of Laves phases were dissolved and turned into δ precipitated phase, but a few of Laves phases were still reserved. And Nb concentration in dendritics increased to 5.42% compared to 2.82% in as-weld condition. Weld metal Vickers-hardness increased from 331.63 in as-weld condition to 391.74 in post-SPF condition which was closed to the base material Vickers-hardness of post-SPF. Grain size of base material grew slightly and an amount of precipitated phase appeared in the base material undergoing SPF process. The tensile test results of base material showed that tensile strength increased obviously and the ductility decreased slightly after SPF process. Load response test results indicated that the 3-sheet structure possessed good resistance to compression and bending load. Accordingly, the LBW/SPF technology is an appropriate forming technique for the 3-sheet structure of Inconel 718 superalloy.
文摘The characteristics of 5A90 Aluminum-Lithium alloy by YAG laser and MIG arc hybrid welding (Hybrid welding) were studied.Compared with the laser beam welding (LBW),the hybrid welding could not only improve the weld appearance significantly,but also have better engineering compatibility.The obvious microstructure characteristics of joint by the hybrid welding are fine-grained layer near fusion-line and the equiaxed grain in most area of welded seam.The subgrains of the equiaxed grains,located in the weld center,tend to coarse from bottom to top of weld joint.The microhardness of welded seam by the hybrid welding (83.57HV0.2) is lower than that by LBW (95.65HV0.2),but the uniformity of the former is better than that of the latter.The ultimate strength and the elongations after fracture of the joint by the hybrid welding are lower than that by LBW.The tensile fracture always occurs in HAZ or weld centerline,and the fractography presents mixture rupture.Therefore,if the combined mechanical properties of joint by the hybrid welding meet the operation requirements,it should be improved by reasonable artificial aging or heat treatment after welding,and it also should develop a better filler wire matched with the base metal.