Wide gap brazing（WGB） experiments using the butted specimen with a 1.5 mm gap were carried out for the repair of the failed K418B superalloy low-pressure turbine vanes.The high temperature creep rupture strengths of...Wide gap brazing（WGB） experiments using the butted specimen with a 1.5 mm gap were carried out for the repair of the failed K418B superalloy low-pressure turbine vanes.The high temperature creep rupture strengths of the brazed joints were tested,and the microstructures and fracture surfaces of the joints were observed.The results show that the microstructure of K418B alloy joint is composed of dense equiaxed grain,small and discrete compounds with a few micro-pores.During the creep rupture test,the cracks initiate preferentially at the micro-pore or the grain boundary,then propagate along the grain boundary till the fracture happens.The creep rupture strength at 700 ℃ of the brazed joints with 50% braze metal in the working part could exceed 90% that of the K418B superalloy,and the joints with 100% braze metal in the working part achieve 70% to 80% of the creep rupture strengths for the K418 B base metal.展开更多
文摘Wide gap brazing（WGB） experiments using the butted specimen with a 1.5 mm gap were carried out for the repair of the failed K418B superalloy low-pressure turbine vanes.The high temperature creep rupture strengths of the brazed joints were tested,and the microstructures and fracture surfaces of the joints were observed.The results show that the microstructure of K418B alloy joint is composed of dense equiaxed grain,small and discrete compounds with a few micro-pores.During the creep rupture test,the cracks initiate preferentially at the micro-pore or the grain boundary,then propagate along the grain boundary till the fracture happens.The creep rupture strength at 700 ℃ of the brazed joints with 50% braze metal in the working part could exceed 90% that of the K418B superalloy,and the joints with 100% braze metal in the working part achieve 70% to 80% of the creep rupture strengths for the K418 B base metal.