A new type of thermal stabilizer, antimony pent（isooctyl thioglycollate）(Sb(SCH2COOC8H17)5), was synthesized by using antimony trioxide, isooctanol and thioglycolic acid in 2 steps. Firstly, antimony trioxide was ox...A new type of thermal stabilizer, antimony pent（isooctyl thioglycollate）(Sb(SCH2COOC8H17)5), was synthesized by using antimony trioxide, isooctanol and thioglycolic acid in 2 steps. Firstly, antimony trioxide was oxidized into colloidal antimony peroxide. Then antimony peroxide and isooctyl thioglycollate reacted stoichiometrically for 2 h with the yield of 87%. This compound was used as thermal stabilizer for polyvinyl chloride（PVC）. The results show that the thermal stability time is 52min at 200℃ by heat-ageing oven test when adding 2.5% thermal stabilizer to PVC resin. Compared with antimony tris（isooctyl thiolycollate）, the initial thermal stability of antimony pent（isooctyl thioglycollate） is better than that of antimony tris（isooctyl thioglycollate）, while the long-term thermal stability time is shorter than that of antimony tris（isooctyl thioglycollate）. Meanwhile, the synergism of antimony pent（isooctyl thioglycollate） with calcium stearate was studied, indicating that when the mass ratio of antimony pent（isooctyl thioglycollate） to calcium stearate is （2∶1,） the thermal stability time of PVC is 58min.展开更多
[ Objective] The purpose was to supply experimental base for preparing new types of high efficient and safe mixture herbicide for sugarcane field. [ Method ] The associated function of MCPA-isooctyl and ametryn on Dig...[ Objective] The purpose was to supply experimental base for preparing new types of high efficient and safe mixture herbicide for sugarcane field. [ Method ] The associated function of MCPA-isooctyl and ametryn on Digitaria sanguinalis and Celosia argentea was evaluated by co-tox. icity coefficient method by potting experiment. [ Result] When active ingredient of MCPA-isooctyl and ametryn was mixed in the proportion of 9： 5, there was obvious synergistic effect on D. sanguinalis and C. argentea, while the co-toxicity coefficients reached 156.24 and 140.40. Proportion method and bisection method were used to confirm the optimum proportion of various ingredients in mixture of MCPA-isooctyl and ametryn, and the optimum proportion was as follows： 35.4% MCPA-isooctyl, 19.6% ametryn, 10.0% emulsifier and the rest were solvents. The stability test indicated that each index of this EC was consistent with standard for pesticide EC. Field efficacy test of 55% MCPA-isooctyl and ametryn EC showed that most weeds in sugarcane field could be effectively controlled with the dose range of 1 073 -2 310 g （a. i. ）/hm^2. [ Conclusion ] Mixture product of ametryn and MCPA-isooctyl with high content was successfully developed, which had the advantages including high efficiency, broad spectrum, good economy and convenient utilization, etc.展开更多
A sun-screening agent isooctyl p-methoxy cinnamate was prepared by reaction of p-methoxyl benzaldehyde with isooctyl acetate using titanium tetrachloride as catalyst. The optimum conditions are as follows： molar rati...A sun-screening agent isooctyl p-methoxy cinnamate was prepared by reaction of p-methoxyl benzaldehyde with isooctyl acetate using titanium tetrachloride as catalyst. The optimum conditions are as follows： molar ratio of p-methoxyl benzaldehyde to isooctyl acetate and titanium tetrachloride is 1 ： 1.1 ： 0.5; reaction temperature is 30℃; and reaction time is 6 h. The yield of isooctyl p-methoxy cinnamate can reach 98%. The method of the synthesis of isooctyl p-methoxy cinnamate is efficient and economical.展开更多
Facing the challenge of expensive photoresist and complex process flow for the fabrication of submicron structures based on laser interference lithography,we propose a low-cost fabrication method for submicron periodi...Facing the challenge of expensive photoresist and complex process flow for the fabrication of submicron structures based on laser interference lithography,we propose a low-cost fabrication method for submicron periodic structures with isooctyl acrylate by laser interference photocuring,which simplifies more processes and reduces costs.Results showed that the period of the grating structures is approximately 0.97±0.01μm,and the minimum feature size can reach 0.24±0.02μm.The period of the dot array is approximately 0.98±0.01μm for dx and 1.97±0.01μm for dy,and the minimum feature size is 0.64±0.01μm.In addition,we demonstrate the diffraction properties of the grating structures.In conclusion,we propose a new method for fabricating submicron grating structures with high efficiency and low cost.展开更多
基金Project supported by the Postdoctoral Foundation of Central South University
文摘A new type of thermal stabilizer, antimony pent（isooctyl thioglycollate）(Sb(SCH2COOC8H17)5), was synthesized by using antimony trioxide, isooctanol and thioglycolic acid in 2 steps. Firstly, antimony trioxide was oxidized into colloidal antimony peroxide. Then antimony peroxide and isooctyl thioglycollate reacted stoichiometrically for 2 h with the yield of 87%. This compound was used as thermal stabilizer for polyvinyl chloride（PVC）. The results show that the thermal stability time is 52min at 200℃ by heat-ageing oven test when adding 2.5% thermal stabilizer to PVC resin. Compared with antimony tris（isooctyl thiolycollate）, the initial thermal stability of antimony pent（isooctyl thioglycollate） is better than that of antimony tris（isooctyl thioglycollate）, while the long-term thermal stability time is shorter than that of antimony tris（isooctyl thioglycollate）. Meanwhile, the synergism of antimony pent（isooctyl thioglycollate） with calcium stearate was studied, indicating that when the mass ratio of antimony pent（isooctyl thioglycollate） to calcium stearate is （2∶1,） the thermal stability time of PVC is 58min.
基金Supported by Guangxi Youth Fund Project(Guikeqing0832062)~~
文摘[ Objective] The purpose was to supply experimental base for preparing new types of high efficient and safe mixture herbicide for sugarcane field. [ Method ] The associated function of MCPA-isooctyl and ametryn on Digitaria sanguinalis and Celosia argentea was evaluated by co-tox. icity coefficient method by potting experiment. [ Result] When active ingredient of MCPA-isooctyl and ametryn was mixed in the proportion of 9： 5, there was obvious synergistic effect on D. sanguinalis and C. argentea, while the co-toxicity coefficients reached 156.24 and 140.40. Proportion method and bisection method were used to confirm the optimum proportion of various ingredients in mixture of MCPA-isooctyl and ametryn, and the optimum proportion was as follows： 35.4% MCPA-isooctyl, 19.6% ametryn, 10.0% emulsifier and the rest were solvents. The stability test indicated that each index of this EC was consistent with standard for pesticide EC. Field efficacy test of 55% MCPA-isooctyl and ametryn EC showed that most weeds in sugarcane field could be effectively controlled with the dose range of 1 073 -2 310 g （a. i. ）/hm^2. [ Conclusion ] Mixture product of ametryn and MCPA-isooctyl with high content was successfully developed, which had the advantages including high efficiency, broad spectrum, good economy and convenient utilization, etc.
文摘A sun-screening agent isooctyl p-methoxy cinnamate was prepared by reaction of p-methoxyl benzaldehyde with isooctyl acetate using titanium tetrachloride as catalyst. The optimum conditions are as follows： molar ratio of p-methoxyl benzaldehyde to isooctyl acetate and titanium tetrachloride is 1 ： 1.1 ： 0.5; reaction temperature is 30℃; and reaction time is 6 h. The yield of isooctyl p-methoxy cinnamate can reach 98%. The method of the synthesis of isooctyl p-methoxy cinnamate is efficient and economical.
基金National Science Foundation of China(No.62175019)Guangdong Basic and Applied Basic Research Foundation(No.2022A1515140053)+1 种基金Scientific Research Project of Education Department of Guangdong Province(No.2022KCXTD029)Project of Jihua Laboratory(No.X220961UZ230)to provide financial support to this research.
文摘Facing the challenge of expensive photoresist and complex process flow for the fabrication of submicron structures based on laser interference lithography,we propose a low-cost fabrication method for submicron periodic structures with isooctyl acrylate by laser interference photocuring,which simplifies more processes and reduces costs.Results showed that the period of the grating structures is approximately 0.97±0.01μm,and the minimum feature size can reach 0.24±0.02μm.The period of the dot array is approximately 0.98±0.01μm for dx and 1.97±0.01μm for dy,and the minimum feature size is 0.64±0.01μm.In addition,we demonstrate the diffraction properties of the grating structures.In conclusion,we propose a new method for fabricating submicron grating structures with high efficiency and low cost.