The weathering steel (Corten B) was exposed to out-door atmosphere of Hanoi (urban site) and Donghoi (marine site). The results showed the protective ability of corrosion product layer formed on weathering steel in th...The weathering steel (Corten B) was exposed to out-door atmosphere of Hanoi (urban site) and Donghoi (marine site). The results showed the protective ability of corrosion product layer formed on weathering steel in the initial stage. The SEM-EDX analysis detected the presence of chromium and copper in the inner layers of corrosion product formed on weathering steel. These elements improved corrosion resistance of corrosion product layers. In addition, the dense α-FeOOH phase were appeared early in corrosion product which is detected by X-ray diffraction and Micro Raman investigations. The results of polarization and EIS measurements also demonstrated the protectiveness of the corrosion product of weathering steel.展开更多
Nucleation of ice by contact takes place when an aerosol particle collides with asurface of supercooled water drop.Aerosol particle may either bounce off the watersurface or be captured on it.McCully et al.(1956) and ...Nucleation of ice by contact takes place when an aerosol particle collides with asurface of supercooled water drop.Aerosol particle may either bounce off the watersurface or be captured on it.McCully et al.(1956) and Rosinski et al.(1963) have shownthat capture of hydrophilic particles was four times larger than of hydrophobic ones.Hydrophobic aerosol particles will nucleate ice preferentially during the brief time ofcontact when they bounce off the surface.Patricles that become captured on the surfacewill float and produce clusters that may nucleate ice at some later time (delayed on surface展开更多
文摘The weathering steel (Corten B) was exposed to out-door atmosphere of Hanoi (urban site) and Donghoi (marine site). The results showed the protective ability of corrosion product layer formed on weathering steel in the initial stage. The SEM-EDX analysis detected the presence of chromium and copper in the inner layers of corrosion product formed on weathering steel. These elements improved corrosion resistance of corrosion product layers. In addition, the dense α-FeOOH phase were appeared early in corrosion product which is detected by X-ray diffraction and Micro Raman investigations. The results of polarization and EIS measurements also demonstrated the protectiveness of the corrosion product of weathering steel.
基金This work was supported by the National Natural Science Foundation of China under Project(49736200)National Basic Research 973 Project(G1999043503)
文摘Nucleation of ice by contact takes place when an aerosol particle collides with asurface of supercooled water drop.Aerosol particle may either bounce off the watersurface or be captured on it.McCully et al.(1956) and Rosinski et al.(1963) have shownthat capture of hydrophilic particles was four times larger than of hydrophobic ones.Hydrophobic aerosol particles will nucleate ice preferentially during the brief time ofcontact when they bounce off the surface.Patricles that become captured on the surfacewill float and produce clusters that may nucleate ice at some later time (delayed on surface