Microstructures and mechanical properties of LZ83?xY alloys containingI-phase andW-phase were investigated by XRD, OM, SEM and EDS. The experimental results show that the content ofI-phase andW-phase changes by varyin...Microstructures and mechanical properties of LZ83?xY alloys containingI-phase andW-phase were investigated by XRD, OM, SEM and EDS. The experimental results show that the content ofI-phase andW-phase changes by varying Zn/Y mass ratio in the LZ83?xY alloys. The cohesion ofI-phase/α-Mg eutectic pockets can enhance the strength in the as-cast LZ83?0.5Y and LZ83?1.0Y alloys, while theW-phase has no obvious strengthening effect on the LZ83?1.5Y alloy. In the extruded alloys, the I-phase andW-phase were extruded into the particles with nanoscale size in theβ-Li matrix phase. The dispersion strengthening of W-phase was more obvious because of the higher volume fraction. The ultimate tensile strength of extruded LZ83?1.5Y alloy is up to 238 MPa while the elongation is up to 20%.展开更多
The particles of Mg-Zn-Gd icosahedral quasicrystal master alloy were added into the AZ31 alloy by the repeated plastic working(RPW)process in order to improve the mechanical properties of the AZ31 alloy at room temper...The particles of Mg-Zn-Gd icosahedral quasicrystal master alloy were added into the AZ31 alloy by the repeated plastic working(RPW)process in order to improve the mechanical properties of the AZ31 alloy at room temperature.The microstructure and tensile properties of composites were investigated by scanning electron microscopy(SEM),transmission electron microscopy(TEM),X-ray diffraction(XRD),and tensile testing machine at room temperature.The results suggest that the RPW process can effectively refine the matrix and make the I-phase particles distribute uniformly.The ultimate tensile strength and the yield strength of the composites reach their maximum values of 362.3 and 330.5 MPa,respectively,when the amount of I-phase particles added is10 %.Meanwhile,the elongation of the composites decreases sharply.展开更多
基金Project(2007CB613702)supported by the National Basic Research Program of ChinaProject(CDJZR14130007)supported by the Fundamental Research Funds for the Central Universities,China
文摘Microstructures and mechanical properties of LZ83?xY alloys containingI-phase andW-phase were investigated by XRD, OM, SEM and EDS. The experimental results show that the content ofI-phase andW-phase changes by varying Zn/Y mass ratio in the LZ83?xY alloys. The cohesion ofI-phase/α-Mg eutectic pockets can enhance the strength in the as-cast LZ83?0.5Y and LZ83?1.0Y alloys, while theW-phase has no obvious strengthening effect on the LZ83?1.5Y alloy. In the extruded alloys, the I-phase andW-phase were extruded into the particles with nanoscale size in theβ-Li matrix phase. The dispersion strengthening of W-phase was more obvious because of the higher volume fraction. The ultimate tensile strength of extruded LZ83?1.5Y alloy is up to 238 MPa while the elongation is up to 20%.
基金financially supported by Beijing Municipal Science and Technology Commission(No.Z131100003213019)National Natural Science Foundation of China(Nos.51101002 and 51301006)Beijing Municipal Commission of Education(Nos.KM201310005001 and KM201110005001)
文摘The particles of Mg-Zn-Gd icosahedral quasicrystal master alloy were added into the AZ31 alloy by the repeated plastic working(RPW)process in order to improve the mechanical properties of the AZ31 alloy at room temperature.The microstructure and tensile properties of composites were investigated by scanning electron microscopy(SEM),transmission electron microscopy(TEM),X-ray diffraction(XRD),and tensile testing machine at room temperature.The results suggest that the RPW process can effectively refine the matrix and make the I-phase particles distribute uniformly.The ultimate tensile strength and the yield strength of the composites reach their maximum values of 362.3 and 330.5 MPa,respectively,when the amount of I-phase particles added is10 %.Meanwhile,the elongation of the composites decreases sharply.