The roller is one of the main parts of a high-pressure grinding roller, which is a type of highly efficient ore crushing equipment. Its working life is strongly affected by the materials used. In this paper, a new kin...The roller is one of the main parts of a high-pressure grinding roller, which is a type of highly efficient ore crushing equipment. Its working life is strongly affected by the materials used. In this paper, a new kind of roller material, the high-vanadium alloy steel （HVAS）, was investigated. The results showed that the as-cast microstructures of the HVAS roller contained martensite, residual austenite, and alloy carbides. The HVAS sample quenched at 1,080 ℃ had a high hardness, and it had much higher compressive strength and abrasive wear resistance after tempering at 560 ℃ for 30 rain. The mechanical properties of the HVAS are more sufficient than the existing roller materials, which are feasible for larger machine design.展开更多
A high-vanadium alloy composite layer was prepared on the surface of a carbon steel using cast composite technology,and the wear properties of the composite layer were investigated.The results showed that the microstr...A high-vanadium alloy composite layer was prepared on the surface of a carbon steel using cast composite technology,and the wear properties of the composite layer were investigated.The results showed that the microstructure of the composite layer was composed of primary vanadium carbides(VC),flake martensite,residual austenite,and fine VC.The hardness of the cast alloy layer was 63 HRC.The abrasive wear resistance and impact wear resistance were increased by 60%and 26%,respectively,compared with those of high-chromium cast iron.The excellent wear resistance of the cast alloy layer is attributed to the high-hardness primary vanadium carbide and the large number of fine secondary vanadium carbides precipitated out of the cast alloy layer.展开更多
基金supported by the National High Technology Research and Development Program (No. 2012AA03A508)Project of Science and Technology Plan of Shenyang City (No. F12-027-2-00)Project of Science and Technology Plan of Liaoning Province (No. LNSBQ4-2010921055)
文摘The roller is one of the main parts of a high-pressure grinding roller, which is a type of highly efficient ore crushing equipment. Its working life is strongly affected by the materials used. In this paper, a new kind of roller material, the high-vanadium alloy steel （HVAS）, was investigated. The results showed that the as-cast microstructures of the HVAS roller contained martensite, residual austenite, and alloy carbides. The HVAS sample quenched at 1,080 ℃ had a high hardness, and it had much higher compressive strength and abrasive wear resistance after tempering at 560 ℃ for 30 rain. The mechanical properties of the HVAS are more sufficient than the existing roller materials, which are feasible for larger machine design.
基金The authors greatly acknowledge the National Natural Science Foundation of China(No.51171060)Program for Changjiang Scholars and Innovative Research Team in University(No.IRT1234).
文摘A high-vanadium alloy composite layer was prepared on the surface of a carbon steel using cast composite technology,and the wear properties of the composite layer were investigated.The results showed that the microstructure of the composite layer was composed of primary vanadium carbides(VC),flake martensite,residual austenite,and fine VC.The hardness of the cast alloy layer was 63 HRC.The abrasive wear resistance and impact wear resistance were increased by 60%and 26%,respectively,compared with those of high-chromium cast iron.The excellent wear resistance of the cast alloy layer is attributed to the high-hardness primary vanadium carbide and the large number of fine secondary vanadium carbides precipitated out of the cast alloy layer.