Hot deformation behavior of a new type of M3∶ 2 high speed steel with niobium addition made by spray forming was investigated based on compression tests in the temperature range of 950-1 150 ℃ and strain rate of 0. ...Hot deformation behavior of a new type of M3∶ 2 high speed steel with niobium addition made by spray forming was investigated based on compression tests in the temperature range of 950-1 150 ℃ and strain rate of 0. 001-10 s^（-1）. A comprehensive constitutive equation was obtained,which could be used to predict the flow stress at different strains. Processing map was developed on the basis of the flow stress data using the principles of dynamic material model. The results showed that the flow curves were in fair agreement with the dynamic recrystallization model. The flow stresses,which were calculated by the comprehensive constitutive equation,agreed well with the test data at low strain rates（ ≤1 s^（-1））. The material constant（ α）,stress exponent（ n） and the hot deformation activation energy（ Q_（HW）） of the new steel were 0. 006 15 MPa^（-1）,4. 81 and 546 kJ·mol^（-1）,respectively. Analysis of the processing map with an observation of microstructures revealed that hot working processes of the steel could be carried out safely in the domain（ T = 1 050-1 150 ℃,ε = 0. 01- 0. 1 s^（-1））with about 33% peak efficiency of power dissipation（ η）. Cracks was expected in two domains at either lower temperatures（ 〈 1 000 ℃） or low strain rates（ 0. 001 s^（-1）） with different cracking mechanisms. Flow localization occurred when the strain rates exceeded 1 s^（-1） at all testing temperatures.展开更多
Isothermal compression testing of Ti555211 titanium alloys was carried out at deformation temperatures from 750 to 950 °C in 50 °C intervals with a strain rate of0.001-1.000 s^（-1）. The high-temperature de...Isothermal compression testing of Ti555211 titanium alloys was carried out at deformation temperatures from 750 to 950 °C in 50 °C intervals with a strain rate of0.001-1.000 s^（-1）. The high-temperature deformation behavior of the Ti555211 alloy was characterized by analysis of stress-strain behavior, kinetics and processing maps. A constitutive equation was formulated to describe the flow stress as a function of deformation temperature and strain rate, and the calculated apparent activation energies are found to be 454.50 and 207.52 k J mol^（-1）in the a b-phase and b-phase regions, respectively. A processing map based on the Murty instability criterion was developed at a strain of 0.7. The maps exhibit two domains of peak efficiency from 750 to 950 °C. A ＊60 % peak efficiency occurs at 800-850 °C/0.001-0.010 s^（-1）. The other peak efficiency of ＊60 % occurs at C950 °C/0.001-0.010 s^（-1）, which can be considered to be the optimum condition for high-temperature working of this alloy.However, at strain rates of higher than 1.000 s^（-1）and deformation temperatures of 750 and 950 °C, clear process flow lines and bands of flow localization occur in the hightemperature deformation process, which should be avoided in Ti555211 alloy hot processing. The mechanism in stability domain and instability domain was also discussed.展开更多
China has been developed into one of the most active regions in terms of both fundamental and applied research on magnesium （Mg） and its alloys in the world from a solid base laid by its prominent metallurgist and m...China has been developed into one of the most active regions in terms of both fundamental and applied research on magnesium （Mg） and its alloys in the world from a solid base laid by its prominent metallurgist and materials scientists over the past decades. Nowadays, a large number of young-generation researchers have been inspired by their predecessors and become the key participants in the fields of Mg alloys, which consequently led to the establishment of China Youth Scholar Society for Magnesium Alloys Research in 2015. Since then, the first two China Youth Scholars Symposiums on Mg Alloys Research had been held at Harbin （2015） and Chongqing （2016） China, respectively. A number of crucial research inter- ests related to fundamental and applied Mg research were discussed at the conferences and summarized in this short perspective, aiming to boost far-reaching initiatives for development of new Mg-based materials to satisfy the requirements for a broad range of industrial employments. Herein, four main aspects are included as follows： i） Plastic deformation mechanism and strengthening strategy, ii） Design and development of new Mg-based materials, iii） Key service properties, and iv） New processing technologies.展开更多
基金Item Sponsored by National Basic Research Program of China(2011CB606303)Constructed Project for Key Laboratory of Beijing of China
文摘Hot deformation behavior of a new type of M3∶ 2 high speed steel with niobium addition made by spray forming was investigated based on compression tests in the temperature range of 950-1 150 ℃ and strain rate of 0. 001-10 s^（-1）. A comprehensive constitutive equation was obtained,which could be used to predict the flow stress at different strains. Processing map was developed on the basis of the flow stress data using the principles of dynamic material model. The results showed that the flow curves were in fair agreement with the dynamic recrystallization model. The flow stresses,which were calculated by the comprehensive constitutive equation,agreed well with the test data at low strain rates（ ≤1 s^（-1））. The material constant（ α）,stress exponent（ n） and the hot deformation activation energy（ Q_（HW）） of the new steel were 0. 006 15 MPa^（-1）,4. 81 and 546 kJ·mol^（-1）,respectively. Analysis of the processing map with an observation of microstructures revealed that hot working processes of the steel could be carried out safely in the domain（ T = 1 050-1 150 ℃,ε = 0. 01- 0. 1 s^（-1））with about 33% peak efficiency of power dissipation（ η）. Cracks was expected in two domains at either lower temperatures（ 〈 1 000 ℃） or low strain rates（ 0. 001 s^（-1）） with different cracking mechanisms. Flow localization occurred when the strain rates exceeded 1 s^（-1） at all testing temperatures.
基金financially supported by the Project of Introducing Talents of Discipline to Universities‘‘111’’Project(No.B08040)
文摘Isothermal compression testing of Ti555211 titanium alloys was carried out at deformation temperatures from 750 to 950 °C in 50 °C intervals with a strain rate of0.001-1.000 s^（-1）. The high-temperature deformation behavior of the Ti555211 alloy was characterized by analysis of stress-strain behavior, kinetics and processing maps. A constitutive equation was formulated to describe the flow stress as a function of deformation temperature and strain rate, and the calculated apparent activation energies are found to be 454.50 and 207.52 k J mol^（-1）in the a b-phase and b-phase regions, respectively. A processing map based on the Murty instability criterion was developed at a strain of 0.7. The maps exhibit two domains of peak efficiency from 750 to 950 °C. A ＊60 % peak efficiency occurs at 800-850 °C/0.001-0.010 s^（-1）. The other peak efficiency of ＊60 % occurs at C950 °C/0.001-0.010 s^（-1）, which can be considered to be the optimum condition for high-temperature working of this alloy.However, at strain rates of higher than 1.000 s^（-1）and deformation temperatures of 750 and 950 °C, clear process flow lines and bands of flow localization occur in the hightemperature deformation process, which should be avoided in Ti555211 alloy hot processing. The mechanism in stability domain and instability domain was also discussed.
基金support from Chinese Committee for Magnesium and its Application
文摘China has been developed into one of the most active regions in terms of both fundamental and applied research on magnesium （Mg） and its alloys in the world from a solid base laid by its prominent metallurgist and materials scientists over the past decades. Nowadays, a large number of young-generation researchers have been inspired by their predecessors and become the key participants in the fields of Mg alloys, which consequently led to the establishment of China Youth Scholar Society for Magnesium Alloys Research in 2015. Since then, the first two China Youth Scholars Symposiums on Mg Alloys Research had been held at Harbin （2015） and Chongqing （2016） China, respectively. A number of crucial research inter- ests related to fundamental and applied Mg research were discussed at the conferences and summarized in this short perspective, aiming to boost far-reaching initiatives for development of new Mg-based materials to satisfy the requirements for a broad range of industrial employments. Herein, four main aspects are included as follows： i） Plastic deformation mechanism and strengthening strategy, ii） Design and development of new Mg-based materials, iii） Key service properties, and iv） New processing technologies.