This paper reports that the high-K HfO2 gate dielectrics are fabricated on n-germanium substrates by sputtering Hf on Ge and following by a furnace annealing. The impacts of sputtering ambient, annealing ambient and a...This paper reports that the high-K HfO2 gate dielectrics are fabricated on n-germanium substrates by sputtering Hf on Ge and following by a furnace annealing. The impacts of sputtering ambient, annealing ambient and annealing temperature on the electrical properties of high-K HfO2 gate dielectrics on germanium substrates are investigated. Experimental results indicate that high-K HfO2 gate dielectrics on germanium substrates with good electrical characteristics are obtained, the electrical properties of high-K HfO2 gate dielectrics is strongly correlated with sputtering ambient, annealing ambient and annealing temperature.展开更多
Europium doped hafnium dioxide nanoparticles were crystallized using biologically friendly microwave hydrothermal method and employed in observation of small rodents tissues.Main solvent in synthesis is water,in conse...Europium doped hafnium dioxide nanoparticles were crystallized using biologically friendly microwave hydrothermal method and employed in observation of small rodents tissues.Main solvent in synthesis is water,in consequence nanoparticles are found surrounded by thin hydroxide layer.Size of the nanoparticles is controlled by temperature of calcination.1200℃heating causes drop of luminescence intensity,explained as damage of high symmetry surface emission centers in the nanocrystals.On the other hand,growth of crystallites increases intensity of X-ray and electron beam excited luminescence.This makes them promising activator in photodynamic therapy.展开更多
Trichloroethylene （TCE） pretreatment of Si surface prior to HfO2 deposition is employed to fabricate HfO2 gatedielectric MOS capacitors. Influence of this processing procedure on interlayer growth, HfO2/Si interface...Trichloroethylene （TCE） pretreatment of Si surface prior to HfO2 deposition is employed to fabricate HfO2 gatedielectric MOS capacitors. Influence of this processing procedure on interlayer growth, HfO2/Si interface properties, gate-oxide leakage and device reliability is investigated. Among the surface pretreatments in NH3, NO, N2O and TCE ambients, the TCE pretreatment gives the least interlayer growths the lowest interface-state density, the smallest gate leakage and the highest reliability. All these improvements should be ascribed to the passivation effects of Cl2 and HC1 on the structural defects in the interlayer and at the interface, and also their gettering effects on the ion contamination in the gate dielectric.展开更多
文摘采用金属有机化学气相沉积（MOCVD）方法在（010）Fe掺杂半绝缘Ga2O3同质衬底上外延得到n型β-Ga2O3薄膜材料,材料结构包括400 nm的非故意掺杂Ga2O3缓冲层和40 nm的Si掺杂Ga2O3沟道层。基于掺杂浓度为2.0×1018cm-3的n型β-Ga2O3薄膜材料,采用原子层沉积的25 nm的HfO2作为栅下绝缘介质层,研制出Ga2O3金属氧化物半导体场效应晶体管（MOSFET）。器件展示出良好的电学特性,在栅偏压为8 V时,漏源饱和电流密度达到42 m A/mm,器件的峰值跨导约为3.8 m S/mm,漏源电流开关比达到108。此外,器件的三端关态击穿电压为113 V。采用场板结构并结合n型Ga2O3沟道层结构优化设计能进一步提升器件饱和电流和击穿电压等电学特性。
基金Project supported by the National Natural Science Foundation of China （Grant No 90307006）, by the National High Tech. Development Program of China （Grant No 2003AA1Z1370）, and by the State Key Development Program for Basic Research of China （Grant No G2000036500）.
文摘This paper reports that the high-K HfO2 gate dielectrics are fabricated on n-germanium substrates by sputtering Hf on Ge and following by a furnace annealing. The impacts of sputtering ambient, annealing ambient and annealing temperature on the electrical properties of high-K HfO2 gate dielectrics on germanium substrates are investigated. Experimental results indicate that high-K HfO2 gate dielectrics on germanium substrates with good electrical characteristics are obtained, the electrical properties of high-K HfO2 gate dielectrics is strongly correlated with sputtering ambient, annealing ambient and annealing temperature.
基金Project supported by National Science Centre(2012/05/E/NZ4/02994 and 2012/06/A/ST7/00398)
文摘Europium doped hafnium dioxide nanoparticles were crystallized using biologically friendly microwave hydrothermal method and employed in observation of small rodents tissues.Main solvent in synthesis is water,in consequence nanoparticles are found surrounded by thin hydroxide layer.Size of the nanoparticles is controlled by temperature of calcination.1200℃heating causes drop of luminescence intensity,explained as damage of high symmetry surface emission centers in the nanocrystals.On the other hand,growth of crystallites increases intensity of X-ray and electron beam excited luminescence.This makes them promising activator in photodynamic therapy.
基金Project supported by the National Natural Science Foundation of China （Grant No 60376019）.
文摘Trichloroethylene （TCE） pretreatment of Si surface prior to HfO2 deposition is employed to fabricate HfO2 gatedielectric MOS capacitors. Influence of this processing procedure on interlayer growth, HfO2/Si interface properties, gate-oxide leakage and device reliability is investigated. Among the surface pretreatments in NH3, NO, N2O and TCE ambients, the TCE pretreatment gives the least interlayer growths the lowest interface-state density, the smallest gate leakage and the highest reliability. All these improvements should be ascribed to the passivation effects of Cl2 and HC1 on the structural defects in the interlayer and at the interface, and also their gettering effects on the ion contamination in the gate dielectric.