TiCoTi granular films were prepared by DC facing-target magnetron sputtering system onto glass substrates and subsequently in situ annealing in vacuum. Structural of Ti (t nm)/Co (40 nm)/Ti (t nm) films were investiga...TiCoTi granular films were prepared by DC facing-target magnetron sputtering system onto glass substrates and subsequently in situ annealing in vacuum. Structural of Ti (t nm)/Co (40 nm)/Ti (t nm) films were investigated in detail, which shows that the majority Co nanograins are formed as the hexagonal-close-packed (HCP) structure. Vibrating sample magnetometer (VSM) and scanning probe microscope (SPM) were applied to study the magnetic properties, morphologies and domain structures of these samples. It has been found that the structure and magnetic properties of the Ti/Co/Ti films depend strongly on the Ti layer thickness. The out-of-plane coercivities (Hc) of the film is maximum about 78.8 kA·m-1 when t=5 nm with annealing at 300 ℃; the distributing of grains of the sample is uniformity; and the average size of particles is about 13 nm. The obtained results suggest that this system is perpendicular anisotropy and might be applicable to perpendicular magnetic recording media.展开更多
基金This work was financially supported by the National Natural Science Foundation of China (No.10274018) and the Foundation of Hebei Provincial Education Department (No.2002116).
文摘TiCoTi granular films were prepared by DC facing-target magnetron sputtering system onto glass substrates and subsequently in situ annealing in vacuum. Structural of Ti (t nm)/Co (40 nm)/Ti (t nm) films were investigated in detail, which shows that the majority Co nanograins are formed as the hexagonal-close-packed (HCP) structure. Vibrating sample magnetometer (VSM) and scanning probe microscope (SPM) were applied to study the magnetic properties, morphologies and domain structures of these samples. It has been found that the structure and magnetic properties of the Ti/Co/Ti films depend strongly on the Ti layer thickness. The out-of-plane coercivities (Hc) of the film is maximum about 78.8 kA·m-1 when t=5 nm with annealing at 300 ℃; the distributing of grains of the sample is uniformity; and the average size of particles is about 13 nm. The obtained results suggest that this system is perpendicular anisotropy and might be applicable to perpendicular magnetic recording media.