The layered LiNi0.6Co0.2-xMn0.2MgxO2 （x=0.00,0.03,0.05,0.07） cathode materials were prepared by a co-precipitation method.The properties of the Mg-doped LiNi0.6Co0.2Mn0.2O2 were investigated by X-ray diffraction （...The layered LiNi0.6Co0.2-xMn0.2MgxO2 （x=0.00,0.03,0.05,0.07） cathode materials were prepared by a co-precipitation method.The properties of the Mg-doped LiNi0.6Co0.2Mn0.2O2 were investigated by X-ray diffraction （XRD）,scanning electron microscopy （SEM）,and electrochemical measurements.XRD studies showed that the Mg-doped LiNi0.6Co0.2Mn0.2O2 had the same layered structure as the undoped LiNi0.6Co0.2Mn0.2O2.The SEM images exhibited that the particle size of Mg-doped LiNi0.6Co0.2Mn0.2O2 was finer than that of the undoped LiNi0.6Co0.2 Mn0.2O2 and that the smallest particle size is only about 1μm.The Mg-doped LiNi0.6Co0.2Mn0.2O2 samples were investigated on the Li extraction/insertion performances through charge/discharge,cyclic voltammogram （CV）,and electrochemical impedance spectra（EIS）.The optimal doping content of Mg was that x= 0.03 in the LiNi0.6Co0.2-xMn0.2MgxO2 samples to achieve high discharge capacity and good cyclic stability.The electrode reaction reversibility and electronic conductivity was enhanced,and the charge transfer resistance was decreased through Mg-doping.The improved electrochemical performances of the Mg-doped LiNi0.6Co0.2Mn0.2O2 cathode materials are attributed to the addition of Mg 2＋ ion by stabilizing the layer structure.展开更多
A well-ordered and spherical LiNi0.6Co0.2Mn0.2O2 cathode material was successfully synthesized from Ni and Mn concentration-gradient precursors via co-precipitation. The crystal structure, morphology and electrochemic...A well-ordered and spherical LiNi0.6Co0.2Mn0.2O2 cathode material was successfully synthesized from Ni and Mn concentration-gradient precursors via co-precipitation. The crystal structure, morphology and electrochemical properties of LiNi0.6Co0.2Mn0.2O2 were characterized by X-ray diffraction, scanning electron microscopy, energy-dispersive spectroscopy, and charge-discharge tests. The material delivered an initial discharge capacity of 174.3 mAh/g at 180 mA/g （1 C rate） between 2.8 and 4.3 V and more than 93.1% of that was retained after 100 cycles. In addition, it also exhibited excellent rate capability, high cut-off voltage and temperature performance.展开更多
基金Funded by the Scientific Research Fund of Hunan Education Department(10C0294)
文摘The layered LiNi0.6Co0.2-xMn0.2MgxO2 （x=0.00,0.03,0.05,0.07） cathode materials were prepared by a co-precipitation method.The properties of the Mg-doped LiNi0.6Co0.2Mn0.2O2 were investigated by X-ray diffraction （XRD）,scanning electron microscopy （SEM）,and electrochemical measurements.XRD studies showed that the Mg-doped LiNi0.6Co0.2Mn0.2O2 had the same layered structure as the undoped LiNi0.6Co0.2Mn0.2O2.The SEM images exhibited that the particle size of Mg-doped LiNi0.6Co0.2Mn0.2O2 was finer than that of the undoped LiNi0.6Co0.2 Mn0.2O2 and that the smallest particle size is only about 1μm.The Mg-doped LiNi0.6Co0.2Mn0.2O2 samples were investigated on the Li extraction/insertion performances through charge/discharge,cyclic voltammogram （CV）,and electrochemical impedance spectra（EIS）.The optimal doping content of Mg was that x= 0.03 in the LiNi0.6Co0.2-xMn0.2MgxO2 samples to achieve high discharge capacity and good cyclic stability.The electrode reaction reversibility and electronic conductivity was enhanced,and the charge transfer resistance was decreased through Mg-doping.The improved electrochemical performances of the Mg-doped LiNi0.6Co0.2Mn0.2O2 cathode materials are attributed to the addition of Mg 2＋ ion by stabilizing the layer structure.
文摘A well-ordered and spherical LiNi0.6Co0.2Mn0.2O2 cathode material was successfully synthesized from Ni and Mn concentration-gradient precursors via co-precipitation. The crystal structure, morphology and electrochemical properties of LiNi0.6Co0.2Mn0.2O2 were characterized by X-ray diffraction, scanning electron microscopy, energy-dispersive spectroscopy, and charge-discharge tests. The material delivered an initial discharge capacity of 174.3 mAh/g at 180 mA/g （1 C rate） between 2.8 and 4.3 V and more than 93.1% of that was retained after 100 cycles. In addition, it also exhibited excellent rate capability, high cut-off voltage and temperature performance.