采用共沉淀法在不同母盐溶液浓度条件下合成出Gd_2Ti_2O_7:Ce纳米粒子;用XRD、SEM、TG-DTA等测试手段分析了样品的物相、形貌及发光性能;用热分析动力学计算不同升温速率下样品的活化能。结果表明:前驱体在升温过程的物相变化分3个阶段,...采用共沉淀法在不同母盐溶液浓度条件下合成出Gd_2Ti_2O_7:Ce纳米粒子;用XRD、SEM、TG-DTA等测试手段分析了样品的物相、形貌及发光性能;用热分析动力学计算不同升温速率下样品的活化能。结果表明:前驱体在升温过程的物相变化分3个阶段,用Doyle-Ozawa和Kissinger法分别对初始浓度为0.08和0.04 mol/L条件下各阶段表观活化能进行计算,其平均值为42.43、145.58、381.98 k J·mol^(-1)和51.28、161.51、446.30 k J·mol^(-1),晶粒生长活化能分别为12.58和19.54 k J·mol^(-1)。浓度为0.08 mol/L时,1173 K煅烧2 h制备出的纳米粒子表面活性较高,铈离子掺杂0.7%(摩尔分数)时发光强度最大。展开更多
Nanosized Gd2(1–x)Eu2xTi2O7:yV5+ phosphors were prepared via sol-gel method and characterized with X-ray diffraction,Raman spectroscopy,diffuse reflectance spectra and photoluminescence spectra.Their PL properties we...Nanosized Gd2(1–x)Eu2xTi2O7:yV5+ phosphors were prepared via sol-gel method and characterized with X-ray diffraction,Raman spectroscopy,diffuse reflectance spectra and photoluminescence spectra.Their PL properties were investigated as functions of the Eu3+ doping concentration and annealing temperature.The results indicated that the as-prepared samples showed a strong emission of Eu3+ under the irradiation of 303 nm.For Eu3+-doped Gd2Ti2O7,the orange emission at 586 nm was the strongest,which was correspond...展开更多
文摘采用共沉淀法在不同母盐溶液浓度条件下合成出Gd_2Ti_2O_7:Ce纳米粒子;用XRD、SEM、TG-DTA等测试手段分析了样品的物相、形貌及发光性能;用热分析动力学计算不同升温速率下样品的活化能。结果表明:前驱体在升温过程的物相变化分3个阶段,用Doyle-Ozawa和Kissinger法分别对初始浓度为0.08和0.04 mol/L条件下各阶段表观活化能进行计算,其平均值为42.43、145.58、381.98 k J·mol^(-1)和51.28、161.51、446.30 k J·mol^(-1),晶粒生长活化能分别为12.58和19.54 k J·mol^(-1)。浓度为0.08 mol/L时,1173 K煅烧2 h制备出的纳米粒子表面活性较高,铈离子掺杂0.7%(摩尔分数)时发光强度最大。
基金supported by Cultivating Innovative Talents for Colleges & Universities of Henan Province (2002006)Open Research Foundation of Henan University
文摘Nanosized Gd2(1–x)Eu2xTi2O7:yV5+ phosphors were prepared via sol-gel method and characterized with X-ray diffraction,Raman spectroscopy,diffuse reflectance spectra and photoluminescence spectra.Their PL properties were investigated as functions of the Eu3+ doping concentration and annealing temperature.The results indicated that the as-prepared samples showed a strong emission of Eu3+ under the irradiation of 303 nm.For Eu3+-doped Gd2Ti2O7,the orange emission at 586 nm was the strongest,which was correspond...