Gd2PdSi3 single crystals were grown by a vertical floating zone method with radiation heating at a zone traveling rate of 3 mm/h. The compound exhibited congruent melting behavior at a liquidus temperature of about 17...Gd2PdSi3 single crystals were grown by a vertical floating zone method with radiation heating at a zone traveling rate of 3 mm/h. The compound exhibited congruent melting behavior at a liquidus temperature of about 1700 ＆#176;C. The slightly Pd-depleted composition of the crystal, with respect to the nominal Gd2PdSi3 stoichiometry, led to gradual accumulation of Pd in the traveling zone and to a decreasing operating temperature during the growth process. Thin platelet-like precipitates of a GdSi phase were detected in the stoichiometric feed rod growth crystal matrix which can be reduced by annealing treatment. Feed rod composition shift crystal growth was proved to be a better way of getting high quality of Gd2PdSi3 single crystal.展开更多
基金Project(51301021)supported by the National Natural Science Foundation of ChinaProjects(2013G1311051,CHD2011JC139)supported by the Fundamental Research Funds for the Central Universities,ChinaProject(SKLSP201302)supported by the State Key Laboratory of Solidification Processing in NWPU,China
文摘Gd2PdSi3 single crystals were grown by a vertical floating zone method with radiation heating at a zone traveling rate of 3 mm/h. The compound exhibited congruent melting behavior at a liquidus temperature of about 1700 ＆#176;C. The slightly Pd-depleted composition of the crystal, with respect to the nominal Gd2PdSi3 stoichiometry, led to gradual accumulation of Pd in the traveling zone and to a decreasing operating temperature during the growth process. Thin platelet-like precipitates of a GdSi phase were detected in the stoichiometric feed rod growth crystal matrix which can be reduced by annealing treatment. Feed rod composition shift crystal growth was proved to be a better way of getting high quality of Gd2PdSi3 single crystal.