We report the magnetic properties of Tb/Si multilayers obtained by rf-sputtering at the Tb layer thickness LTb = 3 nm. Analysis of the magnetization processes indicates more complex behaviour than canonical spinglass ...We report the magnetic properties of Tb/Si multilayers obtained by rf-sputtering at the Tb layer thickness LTb = 3 nm. Analysis of the magnetization processes indicates more complex behaviour than canonical spinglass transition. It is more probable that these multilayers contain both Tb superparamagnetic particles and Tb-Si spin-glass alloys.展开更多
The as-cast Mg-8 Li-xZn-yGd(x=1 2, 3,4;y=1,2;wt.%)alloys were prepared in a vacuum induction furnace and their microstructure and mechanical properties were investigated. The results show that the increase of Zn conte...The as-cast Mg-8 Li-xZn-yGd(x=1 2, 3,4;y=1,2;wt.%)alloys were prepared in a vacuum induction furnace and their microstructure and mechanical properties were investigated. The results show that the increase of Zn content results in the volume fraction of W-phase(Mg3 Zn3 Gd2) increasing while that of Mg3 Gd phase decreasing. The strength of Mg-8 Li-xZn-1 Gd alloys is improved with the increase of Zn content,which is ascribed to the second phase strengthening of fine strip-like W-phase and the solid solution strengthening of Zn element.For Mg-8 Li-4 Zn-yGd alloys,the increase of Gd content leads to the appearance of coarse and discontinuous net-like W-phase, which decreases the strength. The Mg-8 Li-4 Zn-1 Gd alloy exhibits an optimum comprehensive performance with the yield strength, ultimate tensile strength and elongation of 154.7 MPa, 197.0 MPa and 12.4%, respectively. In addition,the aging behavior of the typical alloys was also investigated.展开更多
文摘We report the magnetic properties of Tb/Si multilayers obtained by rf-sputtering at the Tb layer thickness LTb = 3 nm. Analysis of the magnetization processes indicates more complex behaviour than canonical spinglass transition. It is more probable that these multilayers contain both Tb superparamagnetic particles and Tb-Si spin-glass alloys.
基金Project(2016YFB0301004)supported by the National Key Research and Development Program of ChinaProject(51771115)supported by the National Natural Science Foundation of China+3 种基金Project(6141B06310106)supported by the Joint Fund for Space Science and Technology,ChinaProject(009-031-001)supported by the Science and Technology Innovation Program,ChinaProject(USCAST2016-18)supported by the Research Program of Joint Research Center of Advanced Spaceflight Technologies,ChinaProject(SAST2016048)supported by the Science Innovation Foundation of Shanghai Academy of Spaceflight Technology,China
文摘The as-cast Mg-8 Li-xZn-yGd(x=1 2, 3,4;y=1,2;wt.%)alloys were prepared in a vacuum induction furnace and their microstructure and mechanical properties were investigated. The results show that the increase of Zn content results in the volume fraction of W-phase(Mg3 Zn3 Gd2) increasing while that of Mg3 Gd phase decreasing. The strength of Mg-8 Li-xZn-1 Gd alloys is improved with the increase of Zn content,which is ascribed to the second phase strengthening of fine strip-like W-phase and the solid solution strengthening of Zn element.For Mg-8 Li-4 Zn-yGd alloys,the increase of Gd content leads to the appearance of coarse and discontinuous net-like W-phase, which decreases the strength. The Mg-8 Li-4 Zn-1 Gd alloy exhibits an optimum comprehensive performance with the yield strength, ultimate tensile strength and elongation of 154.7 MPa, 197.0 MPa and 12.4%, respectively. In addition,the aging behavior of the typical alloys was also investigated.