Microdamage accumulation in bone is one of the mechanisms for energy dissipation during the fracture process. Changes in the ultrastructure and composition of bone constituents due to aging or diseases could affect mi...Microdamage accumulation in bone is one of the mechanisms for energy dissipation during the fracture process. Changes in the ultrastructure and composition of bone constituents due to aging or diseases could affect microdamage accumulation. Low concentration （1 mM） of sodium fluoride （NaF） has been used in this study to investigate the effect of ultrastructural changes on microdamage accumu- lation in mouse tibias following free-fall impact loadings. Twenty-two tibias were divided randomly into control and NaF-treated groups. Free-fall impact loading was conducted twice on each tibia to produce microdamage. The elas- tic modulus of NaF-treated tibias decreased significantly after the impact loadings, while there was no significant difference in the modulus of untreated samples between pre- and post-damage loadings. Microdamage morphology analysis showed that less and shorter microcracks existed in NaF-treated tibias compared with control bones. Meanwhile, more and longer microcracks were observed in tensile regions in untreated samples compared with that in compressive regions, whereas no significant difference was observed between tensile and compressive regions in NaF-treated bones. The results of this study indicate that more energy is required to generate microcracks in NaF-treated bone than in normal bone. A low concentration of fluoride treatment may increase the toughness of bone under impact loading.展开更多
基金supported by the National Natural Science Foundation of China (Grant 10872007)
文摘Microdamage accumulation in bone is one of the mechanisms for energy dissipation during the fracture process. Changes in the ultrastructure and composition of bone constituents due to aging or diseases could affect microdamage accumulation. Low concentration （1 mM） of sodium fluoride （NaF） has been used in this study to investigate the effect of ultrastructural changes on microdamage accumu- lation in mouse tibias following free-fall impact loadings. Twenty-two tibias were divided randomly into control and NaF-treated groups. Free-fall impact loading was conducted twice on each tibia to produce microdamage. The elas- tic modulus of NaF-treated tibias decreased significantly after the impact loadings, while there was no significant difference in the modulus of untreated samples between pre- and post-damage loadings. Microdamage morphology analysis showed that less and shorter microcracks existed in NaF-treated tibias compared with control bones. Meanwhile, more and longer microcracks were observed in tensile regions in untreated samples compared with that in compressive regions, whereas no significant difference was observed between tensile and compressive regions in NaF-treated bones. The results of this study indicate that more energy is required to generate microcracks in NaF-treated bone than in normal bone. A low concentration of fluoride treatment may increase the toughness of bone under impact loading.