This work studied the effects of firing temperatures on the refractory properties of insulating firebricks produced from a blend of hydrometallurgically purified clay, high alumina cement and sawdust. Twenty grams out...This work studied the effects of firing temperatures on the refractory properties of insulating firebricks produced from a blend of hydrometallurgically purified clay, high alumina cement and sawdust. Twenty grams out of a bulk (1000 Kg) of clay obtained from Ipetumodu in Nigeria was analyzed for size range, consequent upon which the remaining bulk was sieved to 100 μm, being the average size. The bulk was there after leached under a predetermined condition (1.6 mol/dm3 of oxalic acid at 70oC for 150 min and 200 rev/min agitation speed) and cylindrical samples (5 cm diameter by 5 cm high) containing different quantities of high alumina cement (5% - 20%) and sawdust (1% - 5%) were prepared, dried at 110oC and subsequently fired at 900oC, 1100oC, 1300oC and 1500oC, at the rate of 4oC/min and soaked for 2 hrs. These samples were subjected to different refractory tests (permanent linear change, modulus of rupture, bulk density, cold crushing strength and apparent porosity). Even though samples containing more than 20% alumina crumbled at elevated temperatures, it was still observed that the bricks performed to expectations at lower alumina contents, even at 1500oC. The sample containing 3% sawdust and 10% alumina cement however, gave the desired requirement for preparing good insulating firebricks with reliable phase integrity, as revealed by scanning electron microscopy (SEM).展开更多
Laboratory and industrial experiments were carried out to study the possibility of producing high purity purity mullite-corundumthermal insulating firebricks. The results show that by using industrial alumina. natuua...Laboratory and industrial experiments were carried out to study the possibility of producing high purity purity mullite-corundumthermal insulating firebricks. The results show that by using industrial alumina. natuual powder power, coal gangues and a small amountof additives. high purity mullite-corundum thermal insulating firebrieks can be produced The service. temperature of these brick can beup to 1780 with low. thermal conductivity' and good thermal shock resistance展开更多
文摘This work studied the effects of firing temperatures on the refractory properties of insulating firebricks produced from a blend of hydrometallurgically purified clay, high alumina cement and sawdust. Twenty grams out of a bulk (1000 Kg) of clay obtained from Ipetumodu in Nigeria was analyzed for size range, consequent upon which the remaining bulk was sieved to 100 μm, being the average size. The bulk was there after leached under a predetermined condition (1.6 mol/dm3 of oxalic acid at 70oC for 150 min and 200 rev/min agitation speed) and cylindrical samples (5 cm diameter by 5 cm high) containing different quantities of high alumina cement (5% - 20%) and sawdust (1% - 5%) were prepared, dried at 110oC and subsequently fired at 900oC, 1100oC, 1300oC and 1500oC, at the rate of 4oC/min and soaked for 2 hrs. These samples were subjected to different refractory tests (permanent linear change, modulus of rupture, bulk density, cold crushing strength and apparent porosity). Even though samples containing more than 20% alumina crumbled at elevated temperatures, it was still observed that the bricks performed to expectations at lower alumina contents, even at 1500oC. The sample containing 3% sawdust and 10% alumina cement however, gave the desired requirement for preparing good insulating firebricks with reliable phase integrity, as revealed by scanning electron microscopy (SEM).
文摘Laboratory and industrial experiments were carried out to study the possibility of producing high purity purity mullite-corundumthermal insulating firebricks. The results show that by using industrial alumina. natuual powder power, coal gangues and a small amountof additives. high purity mullite-corundum thermal insulating firebrieks can be produced The service. temperature of these brick can beup to 1780 with low. thermal conductivity' and good thermal shock resistance
