The effect of heating temperature and thermal-cold recycle times on microstructure and hardness of a W-Cr-Mn-Mo-V Ferro-based hardfacing layer was studied.The results show the surfacing layer has good high-temperature...The effect of heating temperature and thermal-cold recycle times on microstructure and hardness of a W-Cr-Mn-Mo-V Ferro-based hardfacing layer was studied.The results show the surfacing layer has good high-temperature stability and ability to resist quench heat and heat softening.After thermal-cold recycle at 560°C??18°C for 120 times,the hardness of the hardfacing layer is HRC 57.5,its microstructure is mainly tempered martensite and a small amount of retained austenite,when thermal-cold recycled at 680°C??18°C for 120 times,the hardness of the hardfacing layer is HRC 44.5,martensite in the hardfacing layer has almost decomposed.展开更多
文摘The effect of heating temperature and thermal-cold recycle times on microstructure and hardness of a W-Cr-Mn-Mo-V Ferro-based hardfacing layer was studied.The results show the surfacing layer has good high-temperature stability and ability to resist quench heat and heat softening.After thermal-cold recycle at 560°C??18°C for 120 times,the hardness of the hardfacing layer is HRC 57.5,its microstructure is mainly tempered martensite and a small amount of retained austenite,when thermal-cold recycled at 680°C??18°C for 120 times,the hardness of the hardfacing layer is HRC 44.5,martensite in the hardfacing layer has almost decomposed.