The Fe48Cr15Mo14Er2C15B6amorphous steel can hardly be used as an engineering material because of its ex- treme brittleness and very low iron content. By changing the composition of the nonmagnetic amorphous steel, and...The Fe48Cr15Mo14Er2C15B6amorphous steel can hardly be used as an engineering material because of its ex- treme brittleness and very low iron content. By changing the composition of the nonmagnetic amorphous steel, and using the relation between the reduced glass transition tempera- ture Trg and the glass forming ability, a new amorphous Fe56Mn5Cr7Mo12Er2C12B6 alloy with good glass forming abil- ity and high iron content was obtained. The diameter of the as-cast sample rod reached 8 mm. This new amorphous steel has lower manufacturing cost due to its high iron content, and thus it can have wider applications.展开更多
基金This work was supported by the National Natural Science Foundation of China(Grans No.50371098 and 50321101)the Key Project of the Beiing Science and Technology Program(Contract No.H02040030320).
文摘The Fe48Cr15Mo14Er2C15B6amorphous steel can hardly be used as an engineering material because of its ex- treme brittleness and very low iron content. By changing the composition of the nonmagnetic amorphous steel, and using the relation between the reduced glass transition tempera- ture Trg and the glass forming ability, a new amorphous Fe56Mn5Cr7Mo12Er2C12B6 alloy with good glass forming abil- ity and high iron content was obtained. The diameter of the as-cast sample rod reached 8 mm. This new amorphous steel has lower manufacturing cost due to its high iron content, and thus it can have wider applications.