Under different magnetic field intensities, the dependence of the permeability μ on temperature T(μ-T curve) for the Fe7.3Cu1Nb3Si13.5B9 alloy annealed at 350-620℃ was investigated. The results showed that the magn...Under different magnetic field intensities, the dependence of the permeability μ on temperature T(μ-T curve) for the Fe7.3Cu1Nb3Si13.5B9 alloy annealed at 350-620℃ was investigated. The results showed that the magnetic field intensity had a remarkable influence on the shape of μ-T curves. For amorphous alloy, the sharp Hopkinson peak of μ-T curve disappeared gradually with the increase of magnetic field intensity.展开更多
用HP4294A型阻抗分析仪测量了经不同温度预退火后再540℃退火的Fe73.5Cu1Nb3S i13.5B9纳米晶合金薄带的巨磁阻抗,并结合XRD衍射图谱和AFM图谱,研究了预退火对纳米晶介观结构的影响.结果发现,200℃、300℃和400℃预退火处理40 m in对随后...用HP4294A型阻抗分析仪测量了经不同温度预退火后再540℃退火的Fe73.5Cu1Nb3S i13.5B9纳米晶合金薄带的巨磁阻抗,并结合XRD衍射图谱和AFM图谱,研究了预退火对纳米晶介观结构的影响.结果发现,200℃、300℃和400℃预退火处理40 m in对随后540℃退火的Fe73.5Cu1Nb3S i13.5B9薄带-αFe(S i)纳米晶介观结构产生了影响,颗粒团聚优势明显减弱,横向各向异性场减小,巨磁阻抗比得到了显著的提高.展开更多
基金This work was supported by the National Natural Science Foundation of China(No.59871013).
文摘Under different magnetic field intensities, the dependence of the permeability μ on temperature T(μ-T curve) for the Fe7.3Cu1Nb3Si13.5B9 alloy annealed at 350-620℃ was investigated. The results showed that the magnetic field intensity had a remarkable influence on the shape of μ-T curves. For amorphous alloy, the sharp Hopkinson peak of μ-T curve disappeared gradually with the increase of magnetic field intensity.