In this work, the effectiveness of V2O5-WO3/TiO2 catalysts modified with different CeO2 contents by impregnation and co-precipitation methods on the selective catalytic reduction of NOxby NH3 have been studied compara...In this work, the effectiveness of V2O5-WO3/TiO2 catalysts modified with different CeO2 contents by impregnation and co-precipitation methods on the selective catalytic reduction of NOxby NH3 have been studied comparatively by various experimental techniques. The results showed that the NO conversion of V2O5-WO3/CeO2-TiO2 catalysts modified by co-precipitation method obviously increased with the Ce doping contents in the studied range below 20%（All Ce contents are in mass fractions）, but the NO conversion of V2O5-WO3/CeO2/TiO2 catalysts modified by impregnation methods was lower than V2O5-WO3/CeO2-TiO2 catalysts especially beyond 2.5% Ce doping contents. The V2O5-WO3/CeO2-TiO2 catalysts showed better SCR activity, wider reaction window, and higher sulfur and water resistance. The characterization results elucidated that the modified catalysts by co-precipitation method exhibited higher specific surface area, much better dispersity of Ce component, more Ce^（3＋）species and more Br？nsted acid sites than that by impregnation. The vacancies caused by more Ce^（3＋）species were favorable for more NO oxidation to NO2, and the interaction between Ce species and WOxspecies generated more Br？nsted acid sites. It could be supposed that dispersed Ce Oxspecies and WOxspecies offered more second active centers respectively to adsorb oxygen and activate ammonia as co-catalysis to the primary active center of V ions, thus facilitated the better SCR activity of modified V2O5-WO3/CeO2-TiO2 catalysts by coprecipitation methods. The co-precipitation methods with Ce component were more suitable for production of modified commercial V2O5-WO3/TiO2 catalysts.展开更多
FeTi_1-O_2（= 0.00,0.05,0.10） nanocomposites are synthesized using a sol-gel method involving an ethanol solvent in the presence of ethylene glycol as the stabilizer,and acetic acid as the chemical reagent.Their stru...FeTi_1-O_2（= 0.00,0.05,0.10） nanocomposites are synthesized using a sol-gel method involving an ethanol solvent in the presence of ethylene glycol as the stabilizer,and acetic acid as the chemical reagent.Their structural and optical analyses are studied to reveal their physicochemical properties.Using the x-ray diffractometer（XRD）analysis,the size of the nanoparticles（NPs） is found to be 18-32 nm,where the size of the NPs decreases down to 18 nm when Fe impurity of up to 10% is added,whereas their structure remains unchanged.The results also indicate that the structure of the NPs is tetragonal in the anatase phase.The Fourier transform infrared spectroscopy analysis suggests the presence of a vibration bond（Ti-O） in the sample.The photoluminescence analysis indicates that the diffusion of Fe^（3＋） ions into the TiO_2 matrix results in a decreasing electron-hole recombination,and increases the photocatalytic properties,where the best efficiency appears at an impurity of10%.The UV-diffuse reflection spectroscopy analysis indicates that with the elevation of iron impurity,the band gap value decreases from 3.47 eV for the pure sample to 2.95 eV for the 10 mol% Fe-doped TiO_2 NPs.展开更多
基金Project supported by the Guangxi Natural Science Foundation(2014GXNSFAA118057)Guangxi Science and Technology Planning Project(AB16380276)
文摘In this work, the effectiveness of V2O5-WO3/TiO2 catalysts modified with different CeO2 contents by impregnation and co-precipitation methods on the selective catalytic reduction of NOxby NH3 have been studied comparatively by various experimental techniques. The results showed that the NO conversion of V2O5-WO3/CeO2-TiO2 catalysts modified by co-precipitation method obviously increased with the Ce doping contents in the studied range below 20%（All Ce contents are in mass fractions）, but the NO conversion of V2O5-WO3/CeO2/TiO2 catalysts modified by impregnation methods was lower than V2O5-WO3/CeO2-TiO2 catalysts especially beyond 2.5% Ce doping contents. The V2O5-WO3/CeO2-TiO2 catalysts showed better SCR activity, wider reaction window, and higher sulfur and water resistance. The characterization results elucidated that the modified catalysts by co-precipitation method exhibited higher specific surface area, much better dispersity of Ce component, more Ce^（3＋）species and more Br？nsted acid sites than that by impregnation. The vacancies caused by more Ce^（3＋）species were favorable for more NO oxidation to NO2, and the interaction between Ce species and WOxspecies generated more Br？nsted acid sites. It could be supposed that dispersed Ce Oxspecies and WOxspecies offered more second active centers respectively to adsorb oxygen and activate ammonia as co-catalysis to the primary active center of V ions, thus facilitated the better SCR activity of modified V2O5-WO3/CeO2-TiO2 catalysts by coprecipitation methods. The co-precipitation methods with Ce component were more suitable for production of modified commercial V2O5-WO3/TiO2 catalysts.
文摘FeTi_1-O_2（= 0.00,0.05,0.10） nanocomposites are synthesized using a sol-gel method involving an ethanol solvent in the presence of ethylene glycol as the stabilizer,and acetic acid as the chemical reagent.Their structural and optical analyses are studied to reveal their physicochemical properties.Using the x-ray diffractometer（XRD）analysis,the size of the nanoparticles（NPs） is found to be 18-32 nm,where the size of the NPs decreases down to 18 nm when Fe impurity of up to 10% is added,whereas their structure remains unchanged.The results also indicate that the structure of the NPs is tetragonal in the anatase phase.The Fourier transform infrared spectroscopy analysis suggests the presence of a vibration bond（Ti-O） in the sample.The photoluminescence analysis indicates that the diffusion of Fe^（3＋） ions into the TiO_2 matrix results in a decreasing electron-hole recombination,and increases the photocatalytic properties,where the best efficiency appears at an impurity of10%.The UV-diffuse reflection spectroscopy analysis indicates that with the elevation of iron impurity,the band gap value decreases from 3.47 eV for the pure sample to 2.95 eV for the 10 mol% Fe-doped TiO_2 NPs.
基金supported by the National Natural Science Foundation of China(20976162,21103149,20906079)Natural Science Foundation of Zhejiang Province,China(R5100266)Significant Science and Technology Project of Zhejiang Province,China(2010C13001)~~