To improve performance of PTFE-based damping material,composites with several fillers were prepared by compressing and sintering. The dynamic mechanical properties of the composites were investigated by means of visco...To improve performance of PTFE-based damping material,composites with several fillers were prepared by compressing and sintering. The dynamic mechanical properties of the composites were investigated by means of viscoanalyser. Temperature-dependent loss factors,storage modulus and loss modulus were obtained. And SEM was employed to study the compatibility between PTFE and fillers. The results show that,when blending PPS and PEEK at proper content,the loss factor curve appears double peaks,which can widen the high-damping temperature region of the composites. Blending graphite or alumina can increase the storage modulus obviously,but decrease the value of loss factor. And because graphite or alumina combines with matrix poorly,glide would happen at interface when bearing external load. The interface friction can dissipate vibration energy,which increases the loss modulus of the composites. Blending PPS,PEEK and graphite or alumina at right content,PTFE-based composites can meet demands as damping material in practical engineering.展开更多
The wear and corrosion resistance of Fe_（72.2）Cr_（16.8）Ni_（7.3）Mo_（1.6）Mn_（0.7）C_（0.2）Si_（1.2） and Fe_（77.3）Cr_（15.8）Ni_（3.9）Mo_（1.1）Mn_（0.5）C_（0.2）Si_（1.2） coatings laser-cladded on AISI 4...The wear and corrosion resistance of Fe_（72.2）Cr_（16.8）Ni_（7.3）Mo_（1.6）Mn_（0.7）C_（0.2）Si_（1.2） and Fe_（77.3）Cr_（15.8）Ni_（3.9）Mo_（1.1）Mn_（0.5）C_（0.2）Si_（1.2） coatings laser-cladded on AISI 4130 steel were studied.The coatings possess excellent wear and corrosion resistance despite the absence of expensive yttrium,tungsten,and cobalt and very little molybdenum.The microstructure mainly consists of dendrites and eutectic phases,such as duplex（γ＋α）-Fe and the Fe–Cr（Ni）solid solution,confirmed via energy dispersive spectrometry and X-ray diffraction.The cladded Fe-based coatings have lower coefficients of friction,and narrower and shallower wear tracks than the substrate without the cladding,and the main wear mechanism is mild abrasive wear.Electrochemical test results suggest that the soft Fe_（72.2）Cr_（16.8）Ni_（7.3）Mo_（1.6）Mn_（0.7）C_（0.2）Si_（1.2） coating with high Cr and Ni concentrations has high passivation resistance,low corrosion current,and positive corrosion potential,providing a better protective barrier layer to the AISI 4130 steel against corrosion.展开更多
Steel matrix composites(SMCs),reinforced by ceramic particles,have received a consistent attention in recent years.Using conventional methods to prepare SMCs is generally challenging,and the mechanical properties of c...Steel matrix composites(SMCs),reinforced by ceramic particles,have received a consistent attention in recent years.Using conventional methods to prepare SMCs is generally challenging,and the mechanical properties of conventionally fabricated SMCs are limited.In this study,we successfully fabricated highperformance SMCs by laser powder bed fusion(LPBF)of a composite powder consisting of Fe-based alloy powder and submicron-sized WC particles.The effect of laser energy density on the phase formation,microstructural evolution,overall density and resulting mechanical properties of LPBF-fabricated composites was investigated.The present results show that a novel Fe_(2)W_(4)C carbidic network precipitates in the solidified microstructure entailing segregations along the boundaries of cellular sub-grains.The presence of this carbidic network hampers the growth of sub-grains even at elevated temperatures,and hence,stabilizes the grain size though prepared at a broad range of different energy densities.The exact distribution of the Fe_(2)W_(4)C carbides depends on the employed laser energy densities,as for instance they are more uniformly distributed at higher energy input.The density of LPBF samples reaches the maximum value of 99.4%at 150 J/mm^(3).In this parameter set,high microhardness of~753 HV,compression strength of~3350 MPa and fracture strain of~24.4%are obtained.The enhanced mechanical properties are ascribed to less metallurgical defects,higher volume fraction of the martensitic phase and increasing pile-up dislocations resulting from the pinning effect by Fe_(2)W_(4)C carbide.展开更多
To select the proper composition and obtain an overall material?microstructure?property relationship for Cu?Fe alloy, theeffect of Fe content on microstructure and properties of Cu?Fe-based composite coatings by laser...To select the proper composition and obtain an overall material?microstructure?property relationship for Cu?Fe alloy, theeffect of Fe content on microstructure and properties of Cu?Fe-based composite coatings by laser induction hybrid rapid claddingwas investigated. Microstructure characterization of the composite coatings was tested utilizing SEM, XRD and EDS. Microhardnessmeasurement was executed to evaluate the mechanical properties of the composite coatings. The results show that for low Fe content,the composite coating presents a feature that Fe-rich equiaxed dendrites are embedded in the Cu-rich matrix. With increasing Fecontent, the Fe-rich particles are dispersed in the Cu-rich matrix. With further increasing Fe content, large amounts of Cu-richparticles are homogeneously dispersed in the interdendrite of the Fe-rich matrix. Correspondingly, the average microhardness of thecomposite coatings increases gradually with the increase of Fe content and the microhardness of Cu14.5Fe83Si2C0.5 coating is muchtwice higher than that of the substrate.展开更多
Among various architectures of polymers,end-group-free rings have attracted growing interests due to their distinct physicochemical performances over the linear counterparts which are exemplified by reduced hydrodynam...Among various architectures of polymers,end-group-free rings have attracted growing interests due to their distinct physicochemical performances over the linear counterparts which are exemplified by reduced hydrodynamic size and slower degradation.It is key to develop facile methods to large-scale synthesis of polymer rings with tunable compositions and microstructures.Recent progresses in large-scale synthesis of polymer rings against single-chain dynamic nanoparticles,and the example applications in synchronous enhancing toughness and strength of polymer nanocomposites are summarized.Once there is the breakthrough in rational design and effective large-scale synthesis of polymer rings and their functional derivatives,a family of cyclic functional hybrids would be available,thus providing a new paradigm in developing polymer science and engineering.展开更多
A composite electrocatalyst,CoMoNiO-S/NF-110(NF is nickel foam),was synthesized through electrodeposition,followed by pyrolysis and then the vulcanization process.CoMoNiO-S/NF-110 exhibited a structure where Ni3S2 and...A composite electrocatalyst,CoMoNiO-S/NF-110(NF is nickel foam),was synthesized through electrodeposition,followed by pyrolysis and then the vulcanization process.CoMoNiO-S/NF-110 exhibited a structure where Ni3S2 and Mo2S3 nanoparticles were integrated at the edges of Co3O4 nanosheets,creating a rich,heterogeneous interface that enhances the synergistic effects of each component.In an alkaline electrolyte,the synthesized CoMoNiO-S/NF-110 exhibited superior electrocatalytic performance for oxygen evolution reaction(OER),achieving current densities of 100 and 200 mA·cm^(-2) with low overpotentials of 199.4 and 224.4 mV,respectively,outperforming RuO2 and several high-performance Mo and Ni-based catalysts.This excellent performance is attributed to the rich interface formed between the components and active sites exposed by the defect structure.展开更多
KIT-5/Beta composite supports were synthesized using an in situ self-assembly hydrothermal method,and NiW/KIT-5/Beta catalysts were prepared by impregnation.A series of characterization techniques were utilized to eva...KIT-5/Beta composite supports were synthesized using an in situ self-assembly hydrothermal method,and NiW/KIT-5/Beta catalysts were prepared by impregnation.A series of characterization techniques were utilized to evaluate the influence of varying hydrothermal synthesis temperatures on the physicochemical properties of both the KIT-5/Beta supports and the resulting catalysts.The catalytic performances of catalysts were evaluated under reaction conditions of 320℃,4 MPa H_(2)pressure,and a weight hourly space velocity(WHSV)of 4.8 h^(-1)for hydrodenitrogenation(HDN)of quinoline.The results indicated that the specific surface area and pore structure of the materials could be effectively regulated by adjusting the hydrothermal synthesis temperature,which in turn influenced the number of active sites on the catalyst.The NiW/KB-125 catalyst,synthesized at 125℃,presented the highest quinoline HDN efficiency(96.8%),which can be attributed to its favorable pore channel structure,greater Brønsted acid number,higher degree of metal sulfidation(80.12%)and appropriate metal-support interaction(MSI).展开更多
The poor electrical conductivity of metal-organic frameworks(MOFs)limits their electrocatalytic performance in the oxygen evolution reaction(OER).In this study,a Py@Co-MOF composite material based on pyrene(Py)molecul...The poor electrical conductivity of metal-organic frameworks(MOFs)limits their electrocatalytic performance in the oxygen evolution reaction(OER).In this study,a Py@Co-MOF composite material based on pyrene(Py)molecules and{[Co2(BINDI)(DMA)_(2)]·DMA}_(n)(Co-MOF,H4BINDI=N,N'-bis(5-isophthalic acid)naphthalenediimide,DMA=N,N-dimethylacetamide)was synthesized via a one-pot method,leveragingπ-πinteractions between pyrene and Co-MOF to modulate electrical conductivity.Results demonstrate that the Py@Co-MOF catalyst exhibited significantly enhanced OER performance compared to pure Co-MOF or pyrene-based electrodes,achieving an overpotential of 246 mV at a current density of 10 mA·cm^(-2) along with excellent stability.Density functional theory(DFT)calculations reveal that the formation of O*in the second step is the rate-determining step(RDS)during the OER process on Co-MOF,with an energy barrier of 0.85 eV due to the weak adsorption affinity of the OH*intermediate for Co sites.CCDC:2419276.展开更多
Biochar and biochar composites are versatile materials that can be used in many applications.In this study,biochar was prepared from sawdust and combined with the yttrium iron garnet(YIG)nanocrystal to investigate the...Biochar and biochar composites are versatile materials that can be used in many applications.In this study,biochar was prepared from sawdust and combined with the yttrium iron garnet(YIG)nanocrystal to investigate the shielding effectiveness of the composite structure.Firstly,the effect of the pyrolysis temperature on the shielding effectiveness of biochar was investigated.Secondly,biochars combined with YIG nanocrystals with different contents and shielding effectiveness of the composites were investigated.The electromagnetic effectiveness of the samples was investigated within the X band(8-12 GHz).The findings indicate that biochar demonstrates enhanced absorption properties with elevated pyrolysis temperatures.Biochars demonstrated an approximate 40 d B shielding effectiveness,while YIG exhibited approximately 7 d B,corresponding to absorption at 8 GHz.However,the combination of biochar and YIG exhibited exceptional absorption,reaching 67.12 d B at 8 GHz.展开更多
A new method was proposed for preparing AZ31/1060 composite plates with a corrugated interface,which involved cold-pressing a corrugated surface on the Al plate and then hot-pressing the assembled Mg/Al plate.The resu...A new method was proposed for preparing AZ31/1060 composite plates with a corrugated interface,which involved cold-pressing a corrugated surface on the Al plate and then hot-pressing the assembled Mg/Al plate.The results show that cold-pressing produces intense plastic deformation near the corrugated surface of the Al plate,which promotes dynamic recrystallization of the Al substrate near the interface during the subsequent hot-pressing.In addition,the initial corrugation on the surface of the Al plate also changes the local stress state near the interface during hot pressing,which has a large effect on the texture components of the substrates near the corrugated interface.The construction of the corrugated interface can greatly enhance the shear strength by 2−4 times due to the increased contact area and the strong“mechanical gearing”effect.Moreover,the mechanical properties are largely depended on the orientation relationship between corrugated direction and loading direction.展开更多
Monocolumn composite bucket foundation is a new type of offshore wind energy foundation.Its bearing characteristics under shallow bedrock conditions and complex geological conditions have not been extensively studied....Monocolumn composite bucket foundation is a new type of offshore wind energy foundation.Its bearing characteristics under shallow bedrock conditions and complex geological conditions have not been extensively studied.Therefore,to analyze its bearing characteristics under complex conditions-such as silty soil,chalky soil,and shallow bedrock-this paper employs finite element software to establish various soil combination scenarios.The load-displacement curves of the foundations under these scenarios are calculated to subsequently evaluate the horizontal ultimate bearing capacity.This study investigates the effects of shallow bedrock depth,the type of soil above the bedrock,the thickness of layered soil,and the quality of layered soil on the bearing characteristics of the monocolumn composite bucket foundation.Based on the principle of single-variable control,the ultimate bearing capacity characteristics of the foundation under different conditions are compared.The distribution of soil pressure inside and outside the bucket wall on the compressed side of the foundation,along with the plastic strain of the soil at the base of the foundation,is also analyzed.In conclusion,shallow bedrock somewhat reduces foundation bearing capacity.Under shallow bedrock conditions,the degree of influence on foundation bearing capacity characteristics can considerably vary on different upper soils.The thickness of each soil layer and the depth to bedrock in stratified soils also affect the bearing capacity of the foundation.The findings of this paper provide a theoretical reference for related foundation design and construction.In practice,the bearing performance of the foundation can be enhanced by improvingthe soil quality in the bucket,adjusting the penetration depth,adjusting the percentage of different types of soil layers in the bucket,and applying other technical construction methods.展开更多
To enhance the electrochemical performance of lithium-ion battery anodes with higher silicon content,it is essential to engineer their microstructure for better lithium-ion transport and mitigated volume change as wel...To enhance the electrochemical performance of lithium-ion battery anodes with higher silicon content,it is essential to engineer their microstructure for better lithium-ion transport and mitigated volume change as well.Herein,we suggest an effective approach to control the micropore structure of silicon oxide(SiO_(x))/artificial graphite(AG)composite electrodes using a perforated current collector.The electrode features a unique pore structure,where alternating high-porosity domains and low-porosity domains markedly reduce overall electrode resistance,leading to a 20%improvement in rate capability at a 5C-rate discharge condition.Using microstructure-resolved modeling and simulations,we demonstrate that the patterned micropore structure enhances lithium-ion transport,mitigating the electrolyte concentration gradient of lithium-ion.Additionally,perforating current collector with a chemical etching process increases the number of hydrogen bonding sites and enlarges the interface with the SiO_(x)/AG composite electrode,significantly improving adhesion strength.This,in turn,suppresses mechanical degradation and leads to a 50%higher capacity retention.Thus,regularly arranged micropore structure enabled by the perforated current collector successfully improves both rate capability and cycle life in SiO_(x)/AG composite electrodes,providing valuable insights into electrode engineering.展开更多
The Fe-based WC composite coatings were clad on Q235 steel by double-pass plasma cladding method,in which the WC-Co(WC covered with cobalt:78wt%WC,12wt%Co)doping was about 10wt%,20wt%and 40wt%,respectively.The microst...The Fe-based WC composite coatings were clad on Q235 steel by double-pass plasma cladding method,in which the WC-Co(WC covered with cobalt:78wt%WC,12wt%Co)doping was about 10wt%,20wt%and 40wt%,respectively.The microstructure and wear performance of the composite coatings were investigated by X-ray diffraction(XRD),scanning electron microscope(SEM),energy dispersive spectrometer(EDS)and ball-disc wear tests.The results show that the clad coatings contain mainly?-Fe,WC and carbides(Cr23C6,Fe3W3C-Fe4W2C)phases and the precipitation of carbides increases with the increase of WC-Co doping content.The WC-Co doping content has an obvious effect on the microstructure of the clad coatings.For the clad coatings with low WC-Co doping,the microstructure gradually transforms from planar crystal at the interface of substrate/coating to cell/dendritic crystal at the middle and the upper portion of the coatings.But there are a number of fishbone-like structure at the middle and the upper portion of clad coating with 40wt%WC-Co doping.The microstructure at the top is smaller than that at the bottom for all the coatings.The maximum of hardness of the clad coatings is 72.3HRC which is about 6.9 as much as the hardness of Q235 steel substrate.The composite coatings have good wear resistance due to the reinforcement of carbide particles and the strong bonding between carbide particles and ferroalloy.The suitable increase of WC-Co doping content can improve the wear resistance of the composite coatings.展开更多
Titanium plates with a Ti−O solid solution surface-hardened layer were cold roll-bonded with 304 stainless steel plates with high work hardening rates.The evolution and mechanisms affecting the interfacial bonding str...Titanium plates with a Ti−O solid solution surface-hardened layer were cold roll-bonded with 304 stainless steel plates with high work hardening rates.The evolution and mechanisms affecting the interfacial bonding strength in titanium/stainless steel laminated composites were investigated.Results indicate that the hardened layer reduces the interfacial bonding strength from over 261 MPa to less than 204 MPa.During the cold roll-bonding process,the hardened layer fractures,leading to the formation of multi-scale cracks that are difficult for the stainless steel to fill.This not only hinders the development of an interlocking interface but also leads to the presence of numerous microcracks and hardened blocks along the nearly straight interface,consequently weakening the interfacial bonding strength.In metals with high work hardening rates,the conventional approach of enhancing interface interlocking and improving interfacial bonding strength by using a surface-hardened layer becomes less effective.展开更多
A new Fe-based amorphous–crystalline composite without non-metallic elements, Fe_(55)Cr_(15)Mo_(15)Ni_(10)W_(5), was prepared by melt-spinning. The formation ability and structure information were investigated by X-r...A new Fe-based amorphous–crystalline composite without non-metallic elements, Fe_(55)Cr_(15)Mo_(15)Ni_(10)W_(5), was prepared by melt-spinning. The formation ability and structure information were investigated by X-ray diffractometer(XRD), energy-dispersive spectrometer(EDS) and scanning electron microscope(SEM). The mechanical properties of the amorphous–crystalline composite were investigated by nanoindentation. A molecular dynamics simulation study was performed to simulate the formation of Fe_(55)Cr_(15)Mo_(15)Ni_(10)W_(5) amorphous alloy. The mechanical properties were obtained by compression simulations simultaneously. The results indicate that the Fe_(55)Cr_(15)Mo_(15)Ni_(10)W_(5) ribbon is an amorphous–crystalline composite structure with good ductility, and the hardness of the amorphous–crystalline composite is about 75%higher than that of master ingot. The simulation mechanical properties are in good agreement with the results of nanoindentation at the nanoscale.展开更多
In this study,a few Fe-based amorphous matrix composite coatings reinforced with various portions(4,8 and16 vol.%) of 31 6L stainless steel powders have been successfully produced through high velocity oxy-fuel(HVOF) ...In this study,a few Fe-based amorphous matrix composite coatings reinforced with various portions(4,8 and16 vol.%) of 31 6L stainless steel powders have been successfully produced through high velocity oxy-fuel(HVOF) spraying.The microstructure of the composite coatings was systematically characterized by X-ray diffraction(XRD),scanning electron microscopy(SEM) and transmission electron microscopy(TEM).The main structure of composite coatings remained amorphous while 31 6L stainless steel splats were distributed homogeneously in the amorphous matrix and well connected with surrounding amorphous phase.Bonding strength of coatings to the substrate was determined by 'pull-off' tensile tests.The results revealed that the31 6L stainless steel phase effectively improved the bonding strength of amorphous coatings,which is mainly contributed by the strong metallurgical bonding between stainless steel and amorphous splats.The addition of31 6L stainless steel also enhanced the ductility and fracture resistance of the coatings due to the ductile stainless steel phases,which can arrest crack propagation and increase energy dissipation.展开更多
Some properties of the Fe-based P/M composites sintered and reinforced by infiltration with Cu-Sn alloy were described.It is shown that the hardness of the sintered material is 2.5 times lower,tensile strength is 1.7 ...Some properties of the Fe-based P/M composites sintered and reinforced by infiltration with Cu-Sn alloy were described.It is shown that the hardness of the sintered material is 2.5 times lower,tensile strength is 1.7 times lower and the wear resistance is 2.5-3.3 times lower in comparison with those of the infiltrated material.The presence of pores on the friction surface of the sintered material affects the features of the wear process.Due to the specific morphology of copper in the infiltrated material,the phenomenon of selective mass transfer is observed and worn surfaces have a spongy-capillary texture.展开更多
Effects of sintering temperature in hot pressing, t yp es, states and amounts of rare earth as well as TiH 2 on the transverse rupture strength (TRS) of Fe-based composites are studied by means of orthogonal test and ...Effects of sintering temperature in hot pressing, t yp es, states and amounts of rare earth as well as TiH 2 on the transverse rupture strength (TRS) of Fe-based composites are studied by means of orthogonal test and variance analysis in this paper. It is found that sintering temperature has a significant effect on the TRS of Fe-based diamond composites. The optimal sin tering temperature is 780～860 ℃. On the contrary, the effects of RE additi v es on values of TRS of the diamond composites have on distinct difference no mat ter the RE is in the state of mixture or compound or oxidization. Experimental r esults demonstrate that Fe-based diamond composites with RE additives exhibit h igher TRS, which results in an increase in diamond retention capacity. The degre e of increment of TRS is different at different sintering temperatures. The opti mal amount of rare earth was found to be about 1% in weight. The effect of RE is more significant at lower sintering temperature. The experimental results also reveal that TiH 2 additive has a negative effect on the TRS of Fe-based compos ites. Microscope observations demonstrate that specimen without TiH 2 additives , shows fewer pores and denser structures in the base metal. It can also be seen from the SEM observation of the resulting fracturing surface of bending test sp ecimens that the bonding of the diamond-matrix interface is better in the speci men without TiH 2 than in the specimen with TiH 2. Also the fracture surface o f the specimen without TiH 2 reveals ductile cup and cone behavior.展开更多
Cu-Fe based diamond composites used for saw-blade segments are directly fabricated by vacuum and pressureassisted sintering. The carbide forming elements Cr and Ti are added to improve interfacial bonding between diam...Cu-Fe based diamond composites used for saw-blade segments are directly fabricated by vacuum and pressureassisted sintering. The carbide forming elements Cr and Ti are added to improve interfacial bonding between diamond and the Cu-Fe matrix. The interfacial reactions between diamond/graphite and Cr or Ti, and diamond graphitization are investigated by thermodynamics/kinetics analyses and experimental methods. The results show that interfacial reactions and graphitization of diamond can automatically proceed thermodynamically. The Cr3C2, Cr7C3, Cr23C6, and TiC are formed at the interfaces of composites by reactions between diamond and Cr or Ti; diamond graphitization does not occur because of the kinetic difficulty at 1093 K under the pressure of 13 MPa.展开更多
Fe-based amorphous composite coatings were fabricated on AISI 1045 steel by laser cladding. The results of the X- ray diffraction and transmission electron microscopy analyses .show the coating is composed of an amorp...Fe-based amorphous composite coatings were fabricated on AISI 1045 steel by laser cladding. The results of the X- ray diffraction and transmission electron microscopy analyses .show the coating is composed of an amorphous phase in majority and a nanocrystaUine phuse in m,inority. Phase composition of the coating changes along the depth of the coating. The reasonable scanning speed for fabricating an amorphous composite coating is 3 500 mm/min when the laser power is 4 800 W and the laser beam diameter is 2 mm. If the scanning speed is lower than 3 500 mm/min, the intensity of the two main diffraction peaks in X-ray diffraction patterns of the coatings decreases with the scanning speeds increasing. At the same time, a broad halo peak emerges and enlarges. High laser power and fast scanning speed are the essential conditions of amorphization. The coating exhibits high microhardness.展开更多
基金the National Natural Science Foundation of China (Grant No. 50575054)the Science and Technology Tackle Key Problem Plan Foun-dation of Harbin, China (Grant No. 2004AA2CG126).
文摘To improve performance of PTFE-based damping material,composites with several fillers were prepared by compressing and sintering. The dynamic mechanical properties of the composites were investigated by means of viscoanalyser. Temperature-dependent loss factors,storage modulus and loss modulus were obtained. And SEM was employed to study the compatibility between PTFE and fillers. The results show that,when blending PPS and PEEK at proper content,the loss factor curve appears double peaks,which can widen the high-damping temperature region of the composites. Blending graphite or alumina can increase the storage modulus obviously,but decrease the value of loss factor. And because graphite or alumina combines with matrix poorly,glide would happen at interface when bearing external load. The interface friction can dissipate vibration energy,which increases the loss modulus of the composites. Blending PPS,PEEK and graphite or alumina at right content,PTFE-based composites can meet demands as damping material in practical engineering.
基金financially supported by the Ocean Public Science and Technology Research Fund Projects of China (No. 201405013-3)the Science & Technology Program of Shanghai Maritime University (No. 20130448)+1 种基金the China Postdoctoral Science Foundation (No. 2017M620153)the National Natural Science Foundation of China (No. 51609133)
文摘The wear and corrosion resistance of Fe_（72.2）Cr_（16.8）Ni_（7.3）Mo_（1.6）Mn_（0.7）C_（0.2）Si_（1.2） and Fe_（77.3）Cr_（15.8）Ni_（3.9）Mo_（1.1）Mn_（0.5）C_（0.2）Si_（1.2） coatings laser-cladded on AISI 4130 steel were studied.The coatings possess excellent wear and corrosion resistance despite the absence of expensive yttrium,tungsten,and cobalt and very little molybdenum.The microstructure mainly consists of dendrites and eutectic phases,such as duplex（γ＋α）-Fe and the Fe–Cr（Ni）solid solution,confirmed via energy dispersive spectrometry and X-ray diffraction.The cladded Fe-based coatings have lower coefficients of friction,and narrower and shallower wear tracks than the substrate without the cladding,and the main wear mechanism is mild abrasive wear.Electrochemical test results suggest that the soft Fe_（72.2）Cr_（16.8）Ni_（7.3）Mo_（1.6）Mn_（0.7）C_（0.2）Si_（1.2） coating with high Cr and Ni concentrations has high passivation resistance,low corrosion current,and positive corrosion potential,providing a better protective barrier layer to the AISI 4130 steel against corrosion.
基金the financial support from the National Natural Science Foundation of China(No.51735005)Basic Strengthening Program of Science and Technology(No.2019-JCJQJJ-331)+3 种基金the 5th Jiangsu Province 333 High Level Talents Training Project(BRA2019048)The 15th Batch of“Six Talents Peaks”Innovative Talents Team Program“Laser Precise Additive Manufacturing of Structure-Performance Integrated Lightweight Alloy Components”(No.TD-GDZB-001)2017 Excellent Scientific and Technological Innovation Teams of Universities in Jiangsu“Laser Additive Manufacturing Technologies for Metallic Components”funded by Jiangsu Provincial Department of Education of China(No.51921003)the support from DFG under grant no.KO 5771/1-1。
文摘Steel matrix composites(SMCs),reinforced by ceramic particles,have received a consistent attention in recent years.Using conventional methods to prepare SMCs is generally challenging,and the mechanical properties of conventionally fabricated SMCs are limited.In this study,we successfully fabricated highperformance SMCs by laser powder bed fusion(LPBF)of a composite powder consisting of Fe-based alloy powder and submicron-sized WC particles.The effect of laser energy density on the phase formation,microstructural evolution,overall density and resulting mechanical properties of LPBF-fabricated composites was investigated.The present results show that a novel Fe_(2)W_(4)C carbidic network precipitates in the solidified microstructure entailing segregations along the boundaries of cellular sub-grains.The presence of this carbidic network hampers the growth of sub-grains even at elevated temperatures,and hence,stabilizes the grain size though prepared at a broad range of different energy densities.The exact distribution of the Fe_(2)W_(4)C carbides depends on the employed laser energy densities,as for instance they are more uniformly distributed at higher energy input.The density of LPBF samples reaches the maximum value of 99.4%at 150 J/mm^(3).In this parameter set,high microhardness of~753 HV,compression strength of~3350 MPa and fracture strain of~24.4%are obtained.The enhanced mechanical properties are ascribed to less metallurgical defects,higher volume fraction of the martensitic phase and increasing pile-up dislocations resulting from the pinning effect by Fe_(2)W_(4)C carbide.
基金Projects(51471084,61475117)supported by the National Natural Science Foundation of ChinaProject(13ZCZDGX01109)supported by Tianjin Municipal Science and Technology Commission of ChinaProject(20122BBE500031)supported by the Key Technology Project of Jiangxi Province in China
文摘To select the proper composition and obtain an overall material?microstructure?property relationship for Cu?Fe alloy, theeffect of Fe content on microstructure and properties of Cu?Fe-based composite coatings by laser induction hybrid rapid claddingwas investigated. Microstructure characterization of the composite coatings was tested utilizing SEM, XRD and EDS. Microhardnessmeasurement was executed to evaluate the mechanical properties of the composite coatings. The results show that for low Fe content,the composite coating presents a feature that Fe-rich equiaxed dendrites are embedded in the Cu-rich matrix. With increasing Fecontent, the Fe-rich particles are dispersed in the Cu-rich matrix. With further increasing Fe content, large amounts of Cu-richparticles are homogeneously dispersed in the interdendrite of the Fe-rich matrix. Correspondingly, the average microhardness of thecomposite coatings increases gradually with the increase of Fe content and the microhardness of Cu14.5Fe83Si2C0.5 coating is muchtwice higher than that of the substrate.
基金Supported by the National Natural Science Foundation of China(Nos.52293472,22473096 and 22471164)。
文摘Among various architectures of polymers,end-group-free rings have attracted growing interests due to their distinct physicochemical performances over the linear counterparts which are exemplified by reduced hydrodynamic size and slower degradation.It is key to develop facile methods to large-scale synthesis of polymer rings with tunable compositions and microstructures.Recent progresses in large-scale synthesis of polymer rings against single-chain dynamic nanoparticles,and the example applications in synchronous enhancing toughness and strength of polymer nanocomposites are summarized.Once there is the breakthrough in rational design and effective large-scale synthesis of polymer rings and their functional derivatives,a family of cyclic functional hybrids would be available,thus providing a new paradigm in developing polymer science and engineering.
文摘A composite electrocatalyst,CoMoNiO-S/NF-110(NF is nickel foam),was synthesized through electrodeposition,followed by pyrolysis and then the vulcanization process.CoMoNiO-S/NF-110 exhibited a structure where Ni3S2 and Mo2S3 nanoparticles were integrated at the edges of Co3O4 nanosheets,creating a rich,heterogeneous interface that enhances the synergistic effects of each component.In an alkaline electrolyte,the synthesized CoMoNiO-S/NF-110 exhibited superior electrocatalytic performance for oxygen evolution reaction(OER),achieving current densities of 100 and 200 mA·cm^(-2) with low overpotentials of 199.4 and 224.4 mV,respectively,outperforming RuO2 and several high-performance Mo and Ni-based catalysts.This excellent performance is attributed to the rich interface formed between the components and active sites exposed by the defect structure.
基金Supported by the Autonomous Research Project of SKLCC(2024BWZ003)Strategic Priority Research Program of the Chinese Academy of Sciences(XDA0390401)the Doctoral Research Start-up Funding of Shanxi Institute of Technology(026012).
文摘KIT-5/Beta composite supports were synthesized using an in situ self-assembly hydrothermal method,and NiW/KIT-5/Beta catalysts were prepared by impregnation.A series of characterization techniques were utilized to evaluate the influence of varying hydrothermal synthesis temperatures on the physicochemical properties of both the KIT-5/Beta supports and the resulting catalysts.The catalytic performances of catalysts were evaluated under reaction conditions of 320℃,4 MPa H_(2)pressure,and a weight hourly space velocity(WHSV)of 4.8 h^(-1)for hydrodenitrogenation(HDN)of quinoline.The results indicated that the specific surface area and pore structure of the materials could be effectively regulated by adjusting the hydrothermal synthesis temperature,which in turn influenced the number of active sites on the catalyst.The NiW/KB-125 catalyst,synthesized at 125℃,presented the highest quinoline HDN efficiency(96.8%),which can be attributed to its favorable pore channel structure,greater Brønsted acid number,higher degree of metal sulfidation(80.12%)and appropriate metal-support interaction(MSI).
文摘The poor electrical conductivity of metal-organic frameworks(MOFs)limits their electrocatalytic performance in the oxygen evolution reaction(OER).In this study,a Py@Co-MOF composite material based on pyrene(Py)molecules and{[Co2(BINDI)(DMA)_(2)]·DMA}_(n)(Co-MOF,H4BINDI=N,N'-bis(5-isophthalic acid)naphthalenediimide,DMA=N,N-dimethylacetamide)was synthesized via a one-pot method,leveragingπ-πinteractions between pyrene and Co-MOF to modulate electrical conductivity.Results demonstrate that the Py@Co-MOF catalyst exhibited significantly enhanced OER performance compared to pure Co-MOF or pyrene-based electrodes,achieving an overpotential of 246 mV at a current density of 10 mA·cm^(-2) along with excellent stability.Density functional theory(DFT)calculations reveal that the formation of O*in the second step is the rate-determining step(RDS)during the OER process on Co-MOF,with an energy barrier of 0.85 eV due to the weak adsorption affinity of the OH*intermediate for Co sites.CCDC:2419276.
基金support provided by the Center for Fabrication and Application of Electronic Materials at Dokuz Eylül University,Türkiye。
文摘Biochar and biochar composites are versatile materials that can be used in many applications.In this study,biochar was prepared from sawdust and combined with the yttrium iron garnet(YIG)nanocrystal to investigate the shielding effectiveness of the composite structure.Firstly,the effect of the pyrolysis temperature on the shielding effectiveness of biochar was investigated.Secondly,biochars combined with YIG nanocrystals with different contents and shielding effectiveness of the composites were investigated.The electromagnetic effectiveness of the samples was investigated within the X band(8-12 GHz).The findings indicate that biochar demonstrates enhanced absorption properties with elevated pyrolysis temperatures.Biochars demonstrated an approximate 40 d B shielding effectiveness,while YIG exhibited approximately 7 d B,corresponding to absorption at 8 GHz.However,the combination of biochar and YIG exhibited exceptional absorption,reaching 67.12 d B at 8 GHz.
基金supported by Guangdong Major Project of Basic and Applied Basic Research, China (No. 2020B0301030006)Fundamental Research Funds for the Central Universities, China (No. SWU-XDJH202313)+1 种基金Chongqing Postdoctoral Science Foundation Funded Project, China (No. 2112012728014435)the Chongqing Postgraduate Research and Innovation Project, China (No. CYS23197)。
文摘A new method was proposed for preparing AZ31/1060 composite plates with a corrugated interface,which involved cold-pressing a corrugated surface on the Al plate and then hot-pressing the assembled Mg/Al plate.The results show that cold-pressing produces intense plastic deformation near the corrugated surface of the Al plate,which promotes dynamic recrystallization of the Al substrate near the interface during the subsequent hot-pressing.In addition,the initial corrugation on the surface of the Al plate also changes the local stress state near the interface during hot pressing,which has a large effect on the texture components of the substrates near the corrugated interface.The construction of the corrugated interface can greatly enhance the shear strength by 2−4 times due to the increased contact area and the strong“mechanical gearing”effect.Moreover,the mechanical properties are largely depended on the orientation relationship between corrugated direction and loading direction.
文摘Monocolumn composite bucket foundation is a new type of offshore wind energy foundation.Its bearing characteristics under shallow bedrock conditions and complex geological conditions have not been extensively studied.Therefore,to analyze its bearing characteristics under complex conditions-such as silty soil,chalky soil,and shallow bedrock-this paper employs finite element software to establish various soil combination scenarios.The load-displacement curves of the foundations under these scenarios are calculated to subsequently evaluate the horizontal ultimate bearing capacity.This study investigates the effects of shallow bedrock depth,the type of soil above the bedrock,the thickness of layered soil,and the quality of layered soil on the bearing characteristics of the monocolumn composite bucket foundation.Based on the principle of single-variable control,the ultimate bearing capacity characteristics of the foundation under different conditions are compared.The distribution of soil pressure inside and outside the bucket wall on the compressed side of the foundation,along with the plastic strain of the soil at the base of the foundation,is also analyzed.In conclusion,shallow bedrock somewhat reduces foundation bearing capacity.Under shallow bedrock conditions,the degree of influence on foundation bearing capacity characteristics can considerably vary on different upper soils.The thickness of each soil layer and the depth to bedrock in stratified soils also affect the bearing capacity of the foundation.The findings of this paper provide a theoretical reference for related foundation design and construction.In practice,the bearing performance of the foundation can be enhanced by improvingthe soil quality in the bucket,adjusting the penetration depth,adjusting the percentage of different types of soil layers in the bucket,and applying other technical construction methods.
基金supported by the National Research Foundation of Korea(NRF)grant funded by the Korean government(MSIT)(No.NRF-2021M3H4A1A02048529)the Ministry of Trade,Industry and Energy(MOTIE)of the Korean government under grant No.RS-2022-00155854support from the DGIST Supercomputing and Big Data Center.
文摘To enhance the electrochemical performance of lithium-ion battery anodes with higher silicon content,it is essential to engineer their microstructure for better lithium-ion transport and mitigated volume change as well.Herein,we suggest an effective approach to control the micropore structure of silicon oxide(SiO_(x))/artificial graphite(AG)composite electrodes using a perforated current collector.The electrode features a unique pore structure,where alternating high-porosity domains and low-porosity domains markedly reduce overall electrode resistance,leading to a 20%improvement in rate capability at a 5C-rate discharge condition.Using microstructure-resolved modeling and simulations,we demonstrate that the patterned micropore structure enhances lithium-ion transport,mitigating the electrolyte concentration gradient of lithium-ion.Additionally,perforating current collector with a chemical etching process increases the number of hydrogen bonding sites and enlarges the interface with the SiO_(x)/AG composite electrode,significantly improving adhesion strength.This,in turn,suppresses mechanical degradation and leads to a 50%higher capacity retention.Thus,regularly arranged micropore structure enabled by the perforated current collector successfully improves both rate capability and cycle life in SiO_(x)/AG composite electrodes,providing valuable insights into electrode engineering.
基金Fundamental Research Funds for the Central Universities(2009B16214)China Postdoctoral Science Foundation funded project(20100481079)Scientific Research Start-up Fund Project of Hohai University(20080403)
文摘The Fe-based WC composite coatings were clad on Q235 steel by double-pass plasma cladding method,in which the WC-Co(WC covered with cobalt:78wt%WC,12wt%Co)doping was about 10wt%,20wt%and 40wt%,respectively.The microstructure and wear performance of the composite coatings were investigated by X-ray diffraction(XRD),scanning electron microscope(SEM),energy dispersive spectrometer(EDS)and ball-disc wear tests.The results show that the clad coatings contain mainly?-Fe,WC and carbides(Cr23C6,Fe3W3C-Fe4W2C)phases and the precipitation of carbides increases with the increase of WC-Co doping content.The WC-Co doping content has an obvious effect on the microstructure of the clad coatings.For the clad coatings with low WC-Co doping,the microstructure gradually transforms from planar crystal at the interface of substrate/coating to cell/dendritic crystal at the middle and the upper portion of the coatings.But there are a number of fishbone-like structure at the middle and the upper portion of clad coating with 40wt%WC-Co doping.The microstructure at the top is smaller than that at the bottom for all the coatings.The maximum of hardness of the clad coatings is 72.3HRC which is about 6.9 as much as the hardness of Q235 steel substrate.The composite coatings have good wear resistance due to the reinforcement of carbide particles and the strong bonding between carbide particles and ferroalloy.The suitable increase of WC-Co doping content can improve the wear resistance of the composite coatings.
基金supported by the National Key R&D Program of China (No. 2018YFA0707300)the National Natural Science Foundation of China (No. 52374376)the Introduction Plan for High end Foreign Experts, China (No. G2023105001L)。
文摘Titanium plates with a Ti−O solid solution surface-hardened layer were cold roll-bonded with 304 stainless steel plates with high work hardening rates.The evolution and mechanisms affecting the interfacial bonding strength in titanium/stainless steel laminated composites were investigated.Results indicate that the hardened layer reduces the interfacial bonding strength from over 261 MPa to less than 204 MPa.During the cold roll-bonding process,the hardened layer fractures,leading to the formation of multi-scale cracks that are difficult for the stainless steel to fill.This not only hinders the development of an interlocking interface but also leads to the presence of numerous microcracks and hardened blocks along the nearly straight interface,consequently weakening the interfacial bonding strength.In metals with high work hardening rates,the conventional approach of enhancing interface interlocking and improving interfacial bonding strength by using a surface-hardened layer becomes less effective.
基金financially supported by the National Key Research and Development Program of China(No.2016YFC0801905)。
文摘A new Fe-based amorphous–crystalline composite without non-metallic elements, Fe_(55)Cr_(15)Mo_(15)Ni_(10)W_(5), was prepared by melt-spinning. The formation ability and structure information were investigated by X-ray diffractometer(XRD), energy-dispersive spectrometer(EDS) and scanning electron microscope(SEM). The mechanical properties of the amorphous–crystalline composite were investigated by nanoindentation. A molecular dynamics simulation study was performed to simulate the formation of Fe_(55)Cr_(15)Mo_(15)Ni_(10)W_(5) amorphous alloy. The mechanical properties were obtained by compression simulations simultaneously. The results indicate that the Fe_(55)Cr_(15)Mo_(15)Ni_(10)W_(5) ribbon is an amorphous–crystalline composite structure with good ductility, and the hardness of the amorphous–crystalline composite is about 75%higher than that of master ingot. The simulation mechanical properties are in good agreement with the results of nanoindentation at the nanoscale.
基金financially supported by the National Natural Science Foundation of China (Grant Nos. 51271081 and 51301072)partially supported by the Key Fundamental Research Project from Shenzhen Research Council (No. JC201105170745A)
文摘In this study,a few Fe-based amorphous matrix composite coatings reinforced with various portions(4,8 and16 vol.%) of 31 6L stainless steel powders have been successfully produced through high velocity oxy-fuel(HVOF) spraying.The microstructure of the composite coatings was systematically characterized by X-ray diffraction(XRD),scanning electron microscopy(SEM) and transmission electron microscopy(TEM).The main structure of composite coatings remained amorphous while 31 6L stainless steel splats were distributed homogeneously in the amorphous matrix and well connected with surrounding amorphous phase.Bonding strength of coatings to the substrate was determined by 'pull-off' tensile tests.The results revealed that the31 6L stainless steel phase effectively improved the bonding strength of amorphous coatings,which is mainly contributed by the strong metallurgical bonding between stainless steel and amorphous splats.The addition of31 6L stainless steel also enhanced the ductility and fracture resistance of the coatings due to the ductile stainless steel phases,which can arrest crack propagation and increase energy dissipation.
文摘Some properties of the Fe-based P/M composites sintered and reinforced by infiltration with Cu-Sn alloy were described.It is shown that the hardness of the sintered material is 2.5 times lower,tensile strength is 1.7 times lower and the wear resistance is 2.5-3.3 times lower in comparison with those of the infiltrated material.The presence of pores on the friction surface of the sintered material affects the features of the wear process.Due to the specific morphology of copper in the infiltrated material,the phenomenon of selective mass transfer is observed and worn surfaces have a spongy-capillary texture.
文摘Effects of sintering temperature in hot pressing, t yp es, states and amounts of rare earth as well as TiH 2 on the transverse rupture strength (TRS) of Fe-based composites are studied by means of orthogonal test and variance analysis in this paper. It is found that sintering temperature has a significant effect on the TRS of Fe-based diamond composites. The optimal sin tering temperature is 780～860 ℃. On the contrary, the effects of RE additi v es on values of TRS of the diamond composites have on distinct difference no mat ter the RE is in the state of mixture or compound or oxidization. Experimental r esults demonstrate that Fe-based diamond composites with RE additives exhibit h igher TRS, which results in an increase in diamond retention capacity. The degre e of increment of TRS is different at different sintering temperatures. The opti mal amount of rare earth was found to be about 1% in weight. The effect of RE is more significant at lower sintering temperature. The experimental results also reveal that TiH 2 additive has a negative effect on the TRS of Fe-based compos ites. Microscope observations demonstrate that specimen without TiH 2 additives , shows fewer pores and denser structures in the base metal. It can also be seen from the SEM observation of the resulting fracturing surface of bending test sp ecimens that the bonding of the diamond-matrix interface is better in the speci men without TiH 2 than in the specimen with TiH 2. Also the fracture surface o f the specimen without TiH 2 reveals ductile cup and cone behavior.
基金Project supported by the National Natural Science Foundation of China (Grant No. 51165021)the Science Fund for Distinguished Young Scholars of Gansu Province, China (Grant No. 111RJDA0103)
文摘Cu-Fe based diamond composites used for saw-blade segments are directly fabricated by vacuum and pressureassisted sintering. The carbide forming elements Cr and Ti are added to improve interfacial bonding between diamond and the Cu-Fe matrix. The interfacial reactions between diamond/graphite and Cr or Ti, and diamond graphitization are investigated by thermodynamics/kinetics analyses and experimental methods. The results show that interfacial reactions and graphitization of diamond can automatically proceed thermodynamically. The Cr3C2, Cr7C3, Cr23C6, and TiC are formed at the interfaces of composites by reactions between diamond and Cr or Ti; diamond graphitization does not occur because of the kinetic difficulty at 1093 K under the pressure of 13 MPa.
文摘Fe-based amorphous composite coatings were fabricated on AISI 1045 steel by laser cladding. The results of the X- ray diffraction and transmission electron microscopy analyses .show the coating is composed of an amorphous phase in majority and a nanocrystaUine phuse in m,inority. Phase composition of the coating changes along the depth of the coating. The reasonable scanning speed for fabricating an amorphous composite coating is 3 500 mm/min when the laser power is 4 800 W and the laser beam diameter is 2 mm. If the scanning speed is lower than 3 500 mm/min, the intensity of the two main diffraction peaks in X-ray diffraction patterns of the coatings decreases with the scanning speeds increasing. At the same time, a broad halo peak emerges and enlarges. High laser power and fast scanning speed are the essential conditions of amorphization. The coating exhibits high microhardness.