The Fe silicon nitride synthesized by flashing combustion process was studied to determine the reaction temperature between Fe and silicon nitride, the account of N2 given out in the course of the reaction, and the ch...The Fe silicon nitride synthesized by flashing combustion process was studied to determine the reaction temperature between Fe and silicon nitride, the account of N2 given out in the course of the reaction, and the change of the microstructure during calcination. The results showed that at 1127.2℃ the Fe-silicon nitride self-reacts and releases N2 and under 101.3 kPa the volume of N2 given out in the course of the reaction is 20 times more than that of the starting material. N2 is produced quickly, and completes in several decade seconds. With the producing of N2, the structure of Silicon Nitride around Fe becomes loose and porous, or cracks are formed by the reaction between Fe and silicon nitride. So if it is made use of that Fe-silicon nitride self-producing N2 at the high temperature, the performance of the material on a base of Fe-silicon nitride could be greatly improved.展开更多
基金financially supported by the National Nature Science Foundation of China (No. 50172007 and No. 50332010)
文摘The Fe silicon nitride synthesized by flashing combustion process was studied to determine the reaction temperature between Fe and silicon nitride, the account of N2 given out in the course of the reaction, and the change of the microstructure during calcination. The results showed that at 1127.2℃ the Fe-silicon nitride self-reacts and releases N2 and under 101.3 kPa the volume of N2 given out in the course of the reaction is 20 times more than that of the starting material. N2 is produced quickly, and completes in several decade seconds. With the producing of N2, the structure of Silicon Nitride around Fe becomes loose and porous, or cracks are formed by the reaction between Fe and silicon nitride. So if it is made use of that Fe-silicon nitride self-producing N2 at the high temperature, the performance of the material on a base of Fe-silicon nitride could be greatly improved.
基金National Natural Science Foundation of China(51274107)China Postdoctoral Science Foundation Funded Project(2013M531986)Fund for Fostering Talents of Kunming University of Science and Technology(KKSY201251115)