The mechanical properties of pressureless sintering Fe-Si_ 3N_ 4 bonded SiC and Si_ 3N_ 4 bonded SiC with same manufacture process have been compared in this paper. The oxidizing mechanism of Fe-Si_ 3N_ 4 bonded...The mechanical properties of pressureless sintering Fe-Si_ 3N_ 4 bonded SiC and Si_ 3N_ 4 bonded SiC with same manufacture process have been compared in this paper. The oxidizing mechanism of Fe-Si_ 3N_ 4 bonded SiC ceramic matrix composite has been investigated especially through TG-DSC (thermo gravimetric analysis-differential scanning calorimeter) experiment. During oxidation procedure the main reaction is the oxidation of SiC and Si_ 3N_ 4, SiO_ 2 which form protecting film to prevent further oxidizing. And residual iron in the samples become Fe_ 2O_ 3 and Fe_ 3O_ 4,_ the oxidation kinetics at 1100～1300℃ of Fe-Si_ 3N_ 4 bonded SiC has been studied especially. The weight gain per unit area at initial stage changes according to beeline rule, in the middle according to conic, and in the last oxidation period follows parabola rule.展开更多
文摘The mechanical properties of pressureless sintering Fe-Si_ 3N_ 4 bonded SiC and Si_ 3N_ 4 bonded SiC with same manufacture process have been compared in this paper. The oxidizing mechanism of Fe-Si_ 3N_ 4 bonded SiC ceramic matrix composite has been investigated especially through TG-DSC (thermo gravimetric analysis-differential scanning calorimeter) experiment. During oxidation procedure the main reaction is the oxidation of SiC and Si_ 3N_ 4, SiO_ 2 which form protecting film to prevent further oxidizing. And residual iron in the samples become Fe_ 2O_ 3 and Fe_ 3O_ 4,_ the oxidation kinetics at 1100～1300℃ of Fe-Si_ 3N_ 4 bonded SiC has been studied especially. The weight gain per unit area at initial stage changes according to beeline rule, in the middle according to conic, and in the last oxidation period follows parabola rule.