Liquid-phase enhanced sintering of powder metallurgy（P/M）316L stainless steel by addition of sintering aids was studied.2%-8% of pre-alloyed Fe-Mo-B powder with two different particle sizes was added as sintering ai...Liquid-phase enhanced sintering of powder metallurgy（P/M）316L stainless steel by addition of sintering aids was studied.2%-8% of pre-alloyed Fe-Mo-B powder with two different particle sizes was added as sintering aids,and the specimens were sintered in vacuum at 1 200-1 350 ℃.The results show that the fine Fe-Mo-B powder（5-10 μm）has stronger activated effect.The sintered density increases with the increase in sintering aid content or sintering temperature.Warm compaction has a better effect on the control of dimensional precision of compacts.The prealloyed Fe-Mo-B powder deviated from Mo2FeB2 component can also be sintering aid of P/M 316L stainless steel.展开更多
研究了粉末316L不锈钢添加活化剂的液相强化烧结。在1200～1350℃采用真空烧结,对含量为2%～8%的Cu3P和Fe Mo B两种烧结助剂进行比较,后者采用两种粒度。结果表明:Fe Mo B细粉强化作用最强;增加烧结助剂含量和提高烧结温度可以提高烧结...研究了粉末316L不锈钢添加活化剂的液相强化烧结。在1200～1350℃采用真空烧结,对含量为2%～8%的Cu3P和Fe Mo B两种烧结助剂进行比较,后者采用两种粒度。结果表明:Fe Mo B细粉强化作用最强;增加烧结助剂含量和提高烧结温度可以提高烧结密度;最佳条件为添加6%的Fe Mo B细粉、室温压制、1250℃烧结,烧结密度接近7.70g/cm3。另外,压缩试验表明添加量大于6%后,添加Fe Mo B的烧结制品的塑性比添加Cu3P的塑性要好。展开更多
Thermal stability,crystallization behavior,Vickers hardness and magnetic properties of the Fe41Co7-xNixCr15Mo14C15B6Y2（x=0,1,3,5） bulk metallic glasses were investigated.The Fe41Co7-xNixCr15Mo14C15B6Y2（x=0,1,3,5） ...Thermal stability,crystallization behavior,Vickers hardness and magnetic properties of the Fe41Co7-xNixCr15Mo14C15B6Y2（x=0,1,3,5） bulk metallic glasses were investigated.The Fe41Co7-xNixCr15Mo14C15B6Y2（x=0,1,3,5） metallic glasses were fabricated by copper mold casting method.The thermal stability and crystallization behavior of the metallic glass rods were investigated by differential scanning calorimetry and isothermal experiments.Hardness measurements for samples annealed at different temperatures for different time were carried out at room temperature by the Vickers hardness tester,and magnetic measurements were performed at different temperatures by the vibrating sample magnetometer.It is shown that the addition of Ni does not play a positive role for enlarging ΔTx and GFA from parameter γ（=Tx/（Tg＋Tl））,and it can,however,increase the activation energy in the initial stage of crystallization by changing the initial crystallization behavior.The minor addition of Ni can refine the crystal grain obtained from the full crystallization experiment.The primary crystallization causes the decrease of hardness in these alloys,and as the crystallization continues,the hardness in all samples increases instead due to the precipitation of carbide and boride.The annealing temperature has an obvious effect on magnetic properties of these alloys,and the minor addition of Ni can effectively prevent the alloy annealed at high temperature to transform from paramagnetic to ferromagnetic state.展开更多
The preparation, formation mechanism, surface appearance and structure of electroless plating Fe-Mo-W-B amorphous alloys were systematically studied. The deposition rates of the deposits in different bath composition ...The preparation, formation mechanism, surface appearance and structure of electroless plating Fe-Mo-W-B amorphous alloys were systematically studied. The deposition rates of the deposits in different bath composition as plated were measured. The formation mechanism of the deposits was discussed. The parameter for amorphous structures formation was suggested for the deposits.展开更多
基金Item Sponsored by National High-Tech ResearchDevelopment Programof China(2001AA337010)
文摘Liquid-phase enhanced sintering of powder metallurgy（P/M）316L stainless steel by addition of sintering aids was studied.2%-8% of pre-alloyed Fe-Mo-B powder with two different particle sizes was added as sintering aids,and the specimens were sintered in vacuum at 1 200-1 350 ℃.The results show that the fine Fe-Mo-B powder（5-10 μm）has stronger activated effect.The sintered density increases with the increase in sintering aid content or sintering temperature.Warm compaction has a better effect on the control of dimensional precision of compacts.The prealloyed Fe-Mo-B powder deviated from Mo2FeB2 component can also be sintering aid of P/M 316L stainless steel.
文摘研究了粉末316L不锈钢添加活化剂的液相强化烧结。在1200～1350℃采用真空烧结,对含量为2%～8%的Cu3P和Fe Mo B两种烧结助剂进行比较,后者采用两种粒度。结果表明:Fe Mo B细粉强化作用最强;增加烧结助剂含量和提高烧结温度可以提高烧结密度;最佳条件为添加6%的Fe Mo B细粉、室温压制、1250℃烧结,烧结密度接近7.70g/cm3。另外,压缩试验表明添加量大于6%后,添加Fe Mo B的烧结制品的塑性比添加Cu3P的塑性要好。
基金Project(2012CB825700) supported by the National Basic Research Program of China
文摘Thermal stability,crystallization behavior,Vickers hardness and magnetic properties of the Fe41Co7-xNixCr15Mo14C15B6Y2（x=0,1,3,5） bulk metallic glasses were investigated.The Fe41Co7-xNixCr15Mo14C15B6Y2（x=0,1,3,5） metallic glasses were fabricated by copper mold casting method.The thermal stability and crystallization behavior of the metallic glass rods were investigated by differential scanning calorimetry and isothermal experiments.Hardness measurements for samples annealed at different temperatures for different time were carried out at room temperature by the Vickers hardness tester,and magnetic measurements were performed at different temperatures by the vibrating sample magnetometer.It is shown that the addition of Ni does not play a positive role for enlarging ΔTx and GFA from parameter γ（=Tx/（Tg＋Tl））,and it can,however,increase the activation energy in the initial stage of crystallization by changing the initial crystallization behavior.The minor addition of Ni can refine the crystal grain obtained from the full crystallization experiment.The primary crystallization causes the decrease of hardness in these alloys,and as the crystallization continues,the hardness in all samples increases instead due to the precipitation of carbide and boride.The annealing temperature has an obvious effect on magnetic properties of these alloys,and the minor addition of Ni can effectively prevent the alloy annealed at high temperature to transform from paramagnetic to ferromagnetic state.
文摘The preparation, formation mechanism, surface appearance and structure of electroless plating Fe-Mo-W-B amorphous alloys were systematically studied. The deposition rates of the deposits in different bath composition as plated were measured. The formation mechanism of the deposits was discussed. The parameter for amorphous structures formation was suggested for the deposits.