Fe-Cr-Ti-C composite powder was synthesized by precursor carbonization-composition process using the mixture of ferrotitanium, chromium, iron powder and precursor sucrose as raw material. And then the Fe-Cr-Ti-C coati...Fe-Cr-Ti-C composite powder was synthesized by precursor carbonization-composition process using the mixture of ferrotitanium, chromium, iron powder and precursor sucrose as raw material. And then the Fe-Cr-Ti-C coating was prepared by reactive plasma cladding method. Microstructure of the samples was observed by scanning electron microscope （SEM）, the phases were determined by X-ray diffraction （XRD）, and the wear resistance was evaluated under dry sliding wear test conditions at room temperature. Results indicate that the composite coating consists of primary austenite and dendritic eutectic austenite, chrysanthemum-shaped eutectic （Cr, Fe ） 7 C3 and TiC carbide. TiC presents the gradient distribution and different shapes in the coating, corresponding to equiaxial structure both in fusion zone and central zone, while it presents dendritic structure on the surface, respectively. The wear mass loss is insensitive to load for the coating while it increases rapidly for Q235 steel base metal in this test. The wear mass loss ofQ235 steel is 14 times as that of the composite coating under applied load of 40 kg.展开更多
基金Supported by Natural Science Foundation of Shandong Province （No. ZR2011EMM017 ）.
文摘Fe-Cr-Ti-C composite powder was synthesized by precursor carbonization-composition process using the mixture of ferrotitanium, chromium, iron powder and precursor sucrose as raw material. And then the Fe-Cr-Ti-C coating was prepared by reactive plasma cladding method. Microstructure of the samples was observed by scanning electron microscope （SEM）, the phases were determined by X-ray diffraction （XRD）, and the wear resistance was evaluated under dry sliding wear test conditions at room temperature. Results indicate that the composite coating consists of primary austenite and dendritic eutectic austenite, chrysanthemum-shaped eutectic （Cr, Fe ） 7 C3 and TiC carbide. TiC presents the gradient distribution and different shapes in the coating, corresponding to equiaxial structure both in fusion zone and central zone, while it presents dendritic structure on the surface, respectively. The wear mass loss is insensitive to load for the coating while it increases rapidly for Q235 steel base metal in this test. The wear mass loss ofQ235 steel is 14 times as that of the composite coating under applied load of 40 kg.