Fe-Al/Cr3C2 composite coatings were manufactured using high velocity arc spraying （HVAS） technology. The high temperature erosion, wear and corrosion resistance of the coatings were investigated. The coating propert...Fe-Al/Cr3C2 composite coatings were manufactured using high velocity arc spraying （HVAS） technology. The high temperature erosion, wear and corrosion resistance of the coatings were investigated. The coating properties such as bonding strength, porosity, hardness as well as microstructures were characterized. The results show that the coatings have relatively high heat tremble bond strength, hardness, and typical layer-shaped coatings＇ microstructures. With the rise of temperature, the coating erosion resistance increases too; the impingement angel does effects on erosion properties, and the erosion mechanism changes from ductile to brittle behaviors at 450℃. The coatings have good room temperature wear resistance and relatively good high temperature resistance. The wear mechanism of the coatings is peeling wear behavior. The coatings have excellent high temperature corrosion resistance because of the produce of oxides during corrosion.展开更多
Double glow plasma surface metallurgy technique was used to fabricate a Fe?Al?Cr?Nb alloyed layer onto the surface of the 45 steel. The microstructures and composition of th?eA Fl?eCr?Nb alloyed layer were analyzed by...Double glow plasma surface metallurgy technique was used to fabricate a Fe?Al?Cr?Nb alloyed layer onto the surface of the 45 steel. The microstructures and composition of th?eA Fl?eCr?Nb alloyed layer were analyzed by scanning electronic microscopy, X-ray diffraction and energy dispersive spectroscopy. The results indicate thatthe 20 μm alloyed layer is homogeneous and compact. The alloyed elements exhibit a gradient distribution along the cross section. Microhardness and nanoindentation tests imply that the surface hardness of the alloyed layer reaches HV 580, which is almost 2.8 times that of the substrate. Compared with the substrate, the alloyed layer has a much smaller displacement and a larger elastic modulus. According to the friction and wear tests at room temperature, the? FeAl?Cr?Nb alloyed layer has lower friction coefficient and less wear mass, implying that the Fe?Al?Cr?Nb alloyed layer can effectively improve the surface hardness and wear resistance of the substrate.展开更多
Iron aluminide intermetallic coatings were prepared from Fe-Al/Cr3C2 cored wires using High Velocity Are Spraying （ HVAS ） technology. Erosion and corrosion properties of HVAS sprayed Fe-Al/Cr3C2 coatings were inves...Iron aluminide intermetallic coatings were prepared from Fe-Al/Cr3C2 cored wires using High Velocity Are Spraying （ HVAS ） technology. Erosion and corrosion properties of HVAS sprayed Fe-Al/Cr3C2 coatings were investigated. Results show that the erosion at impingement angle of 30°is more than that of 90°. The erosion resistance of coatings was enhanced uith the inereaase of temperature. Coatings had a better erosion resislance than substrwles. The erosion changed from ductile behariors to brittle behaviors above 450℃ . At high temperature, the erosion resistances were superior to those at low temperwlure and roonl temperwlure. Cowlings had much higher corrosion properties than substrates. The temperature had a little effect on the corrosion resistance of coatings ; The corrosion losing of cowlings increased slowly with the increase of corrosion time. The HVAS-sprayed Fe-Al/Cr3C2 coatings exhibited a high bond strength and hardness.展开更多
Dense Fe-Al-Cr coatings with approximately 50 μm in thickness are successfully prepared on the 1045 carbon steel substrates via a laser cladding process. Proper Cr content(5 at% Cr) will lead to decrease in the melti...Dense Fe-Al-Cr coatings with approximately 50 μm in thickness are successfully prepared on the 1045 carbon steel substrates via a laser cladding process. Proper Cr content(5 at% Cr) will lead to decrease in the melting point, and improves the viscosity of the liquid and the nucleation rate of the molten pool, leading to refining grains of the solidification structure. As a result, the Fe-29 Al-5 Cr laser cladding layer exhibits the best hardness, plasticity properties, and wear resistance at 400 °C. Excessive Cr for the Fe-29 Al-7.5 Cr coating leads to the formation of Cr2 Al in the grain boundaries and thermal vacancies during the solidification process, resulting in inferior mechanical properties and poor tribological behavior.展开更多
文摘Fe-Al/Cr3C2 composite coatings were manufactured using high velocity arc spraying （HVAS） technology. The high temperature erosion, wear and corrosion resistance of the coatings were investigated. The coating properties such as bonding strength, porosity, hardness as well as microstructures were characterized. The results show that the coatings have relatively high heat tremble bond strength, hardness, and typical layer-shaped coatings＇ microstructures. With the rise of temperature, the coating erosion resistance increases too; the impingement angel does effects on erosion properties, and the erosion mechanism changes from ductile to brittle behaviors at 450℃. The coatings have good room temperature wear resistance and relatively good high temperature resistance. The wear mechanism of the coatings is peeling wear behavior. The coatings have excellent high temperature corrosion resistance because of the produce of oxides during corrosion.
基金Project(51371097)supported by the National Natural Science Foundation of ChinaProject supported by the Priority Academic Program Development of Jiangsu Higher Education Institutions,China
文摘Double glow plasma surface metallurgy technique was used to fabricate a Fe?Al?Cr?Nb alloyed layer onto the surface of the 45 steel. The microstructures and composition of th?eA Fl?eCr?Nb alloyed layer were analyzed by scanning electronic microscopy, X-ray diffraction and energy dispersive spectroscopy. The results indicate thatthe 20 μm alloyed layer is homogeneous and compact. The alloyed elements exhibit a gradient distribution along the cross section. Microhardness and nanoindentation tests imply that the surface hardness of the alloyed layer reaches HV 580, which is almost 2.8 times that of the substrate. Compared with the substrate, the alloyed layer has a much smaller displacement and a larger elastic modulus. According to the friction and wear tests at room temperature, the? FeAl?Cr?Nb alloyed layer has lower friction coefficient and less wear mass, implying that the Fe?Al?Cr?Nb alloyed layer can effectively improve the surface hardness and wear resistance of the substrate.
基金Founded by the National Natural Science Foundation of China(Grant No.50235030 ,50005024)
文摘Iron aluminide intermetallic coatings were prepared from Fe-Al/Cr3C2 cored wires using High Velocity Are Spraying （ HVAS ） technology. Erosion and corrosion properties of HVAS sprayed Fe-Al/Cr3C2 coatings were investigated. Results show that the erosion at impingement angle of 30°is more than that of 90°. The erosion resistance of coatings was enhanced uith the inereaase of temperature. Coatings had a better erosion resislance than substrwles. The erosion changed from ductile behariors to brittle behaviors above 450℃ . At high temperature, the erosion resistances were superior to those at low temperwlure and roonl temperwlure. Cowlings had much higher corrosion properties than substrates. The temperature had a little effect on the corrosion resistance of coatings ; The corrosion losing of cowlings increased slowly with the increase of corrosion time. The HVAS-sprayed Fe-Al/Cr3C2 coatings exhibited a high bond strength and hardness.
基金Funded by National Natural Science Foundation of China(No.51371097)Six Talent Peaks(2015)Project of Jiangsu Province(No.YPC16005-PT)the Priority Academic Program Development of Jiangsu Higher Education Institutions
文摘Dense Fe-Al-Cr coatings with approximately 50 μm in thickness are successfully prepared on the 1045 carbon steel substrates via a laser cladding process. Proper Cr content(5 at% Cr) will lead to decrease in the melting point, and improves the viscosity of the liquid and the nucleation rate of the molten pool, leading to refining grains of the solidification structure. As a result, the Fe-29 Al-5 Cr laser cladding layer exhibits the best hardness, plasticity properties, and wear resistance at 400 °C. Excessive Cr for the Fe-29 Al-7.5 Cr coating leads to the formation of Cr2 Al in the grain boundaries and thermal vacancies during the solidification process, resulting in inferior mechanical properties and poor tribological behavior.