Aiming at the cracking phenomenon of the thin shell mould in the expendable pattern shell casting during the pattern removing process, some systemic researches are presented.The influence of the pattern removing metho...Aiming at the cracking phenomenon of the thin shell mould in the expendable pattern shell casting during the pattern removing process, some systemic researches are presented.The influence of the pattern removing method and temperature on the pattern removing were investigated.The shell mould cracking mechanism was analyzed by using thermo-gravimetric analysis (TGA), and combining the temperature field and the volume change of the expanded polystyrene (EPS) foam pattern being tested.The results indicated that the shell mould was not easily cracked when the pattern removing process was carried out with the furnace being heated little by little because of the shell slowly shrinking with dehydration and shell strength gradually increasing.The shell mould was soon destroyed when it was set directly into the furnace at above 400 oC because of the thin shell mould rapidly shrinking and the foam pattern hindering.However, the shell mould had no cracking when it had been preheated for a long time even if the furnace temperature was above 400 oC and the shell was put into the furnace directly.Moreover, when the shell mould was directly set into the furnace at lower temperatures, 250 to 300 ℃, the shell would shrink slowly and the foam pattern would stay at the maximum expansion stage temperature of 100 to 110 ℃ for a long time; and the shell mould would experience an expansion force from the foam pattern for a long time.The expansion force is related to the pattern removing temperature, holding time, foam pattern thickness and density.Therefore, the foam pattern with higher density could make the shell crack.展开更多
To refine the microstructure and improve the mechanical properties of AZ91 D alloy by expendable pattern shell casting(EPSC),the mechanical vibration method was applied in the solidification process of the alloy.The e...To refine the microstructure and improve the mechanical properties of AZ91 D alloy by expendable pattern shell casting(EPSC),the mechanical vibration method was applied in the solidification process of the alloy.The effects of amplitude and pouring temperature on microstructure and mechanical properties of AZ91 D magnesium alloy were studied.The results indicated that the mechanical vibration remarkably improved the sizes,morphologies and distributions of the primaryα-Mg phase andβ-Mg17 Al12 phase,and the densification and tensile properties of the AZ91 D alloy.With an increase in amplitude,the microstructures were gradually refined,resulting in a continuous increase in mechanical properties of the AZ91 D alloy.While,with the increase of pouring temperature,the microstructures were continuously coarsened,leading to an obvious decrease of the mechanical properties.The tensile strength and yield strength of the AZ91 D alloy with a vibration amplitude of 1.0 mm and a pouring temperature of 730℃were 60%and 38%higher than those of the alloy without vibration,respectively.展开更多
The effective surface treatment method for steel insert composited with Al base metal by expendable pattern casting （EPC） process and the bonding interface between steel insert and Al base metal were investigated.It...The effective surface treatment method for steel insert composited with Al base metal by expendable pattern casting （EPC） process and the bonding interface between steel insert and Al base metal were investigated.It was found that Zn plating on steel insert was effective on improving the bonding property between steel insert and Al base metal in EPC process.Zn is thought to promote the formation of diffusion layer.But almost none content of Zn was observed in the boundary which had been plated on the steel insert.A diffusion layer consisting of Al,Si and Fe was formed at the insert/alloy interface and its hardness was higher than the steel insert as matter of course Al base metal.This layer turned out to be intermetallic compounds of Al-Si-Fe system.Higher pouring temperature promoted the diffusion of Fe into Al alloy,so Fe content in intermetallic layers increased at higher pouring temperature.The layer nearest to steel disappeared due to applied pressure.展开更多
基金supported by the National High Technology Research and Development Program of China (No.2007AA03Z113)
文摘Aiming at the cracking phenomenon of the thin shell mould in the expendable pattern shell casting during the pattern removing process, some systemic researches are presented.The influence of the pattern removing method and temperature on the pattern removing were investigated.The shell mould cracking mechanism was analyzed by using thermo-gravimetric analysis (TGA), and combining the temperature field and the volume change of the expanded polystyrene (EPS) foam pattern being tested.The results indicated that the shell mould was not easily cracked when the pattern removing process was carried out with the furnace being heated little by little because of the shell slowly shrinking with dehydration and shell strength gradually increasing.The shell mould was soon destroyed when it was set directly into the furnace at above 400 oC because of the thin shell mould rapidly shrinking and the foam pattern hindering.However, the shell mould had no cracking when it had been preheated for a long time even if the furnace temperature was above 400 oC and the shell was put into the furnace directly.Moreover, when the shell mould was directly set into the furnace at lower temperatures, 250 to 300 ℃, the shell would shrink slowly and the foam pattern would stay at the maximum expansion stage temperature of 100 to 110 ℃ for a long time; and the shell mould would experience an expansion force from the foam pattern for a long time.The expansion force is related to the pattern removing temperature, holding time, foam pattern thickness and density.Therefore, the foam pattern with higher density could make the shell crack.
基金the financial support from the State Key Laboratory of Materials Processing and Die&Mould Technology,Huazhong University of Science and Technology(P2020-05)。
文摘To refine the microstructure and improve the mechanical properties of AZ91 D alloy by expendable pattern shell casting(EPSC),the mechanical vibration method was applied in the solidification process of the alloy.The effects of amplitude and pouring temperature on microstructure and mechanical properties of AZ91 D magnesium alloy were studied.The results indicated that the mechanical vibration remarkably improved the sizes,morphologies and distributions of the primaryα-Mg phase andβ-Mg17 Al12 phase,and the densification and tensile properties of the AZ91 D alloy.With an increase in amplitude,the microstructures were gradually refined,resulting in a continuous increase in mechanical properties of the AZ91 D alloy.While,with the increase of pouring temperature,the microstructures were continuously coarsened,leading to an obvious decrease of the mechanical properties.The tensile strength and yield strength of the AZ91 D alloy with a vibration amplitude of 1.0 mm and a pouring temperature of 730℃were 60%and 38%higher than those of the alloy without vibration,respectively.
文摘The effective surface treatment method for steel insert composited with Al base metal by expendable pattern casting （EPC） process and the bonding interface between steel insert and Al base metal were investigated.It was found that Zn plating on steel insert was effective on improving the bonding property between steel insert and Al base metal in EPC process.Zn is thought to promote the formation of diffusion layer.But almost none content of Zn was observed in the boundary which had been plated on the steel insert.A diffusion layer consisting of Al,Si and Fe was formed at the insert/alloy interface and its hardness was higher than the steel insert as matter of course Al base metal.This layer turned out to be intermetallic compounds of Al-Si-Fe system.Higher pouring temperature promoted the diffusion of Fe into Al alloy,so Fe content in intermetallic layers increased at higher pouring temperature.The layer nearest to steel disappeared due to applied pressure.