The corrosion behavior and electrochemical impedance spectroscopy (EIS) features of 8090 Al-Li alloys in EXCO solution were investigated, and the EIS was simulated using an equivalent circuit. At the beginning of imme...The corrosion behavior and electrochemical impedance spectroscopy (EIS) features of 8090 Al-Li alloys in EXCO solution were investigated, and the EIS was simulated using an equivalent circuit. At the beginning of immersion in EXCO solution, the EIS is comprised by a depressed capacitive arc at high-mediate frequency and an inductive arc at low frequency, and the inductive component decreases and disappears with im- mersion time. Once exfoliation or severe pitting corrosion is produced, two capacitive arcs appear in the EIS. These two capacitive arcs are originated from the two parts of the corroded alloy surface, the original flat alloy surface and the new inter-face exposed to the aggressive EXCO solution due to the exfoliation or pitting corrosion. Some corrosion development features of 8090 Al-Li alloys in EXCO solution can be obtained through simulated EIS information.展开更多
The notched and smooth specimens of aluminum alloy LC4CS soaked in EXCO solution for different time are tested under the constant amplitude cyclic loading to obtain S-N curves and fatigue notch factors with different ...The notched and smooth specimens of aluminum alloy LC4CS soaked in EXCO solution for different time are tested under the constant amplitude cyclic loading to obtain S-N curves and fatigue notch factors with different pre-corrosion time. By analyzing the corrosion process of LC4CS specimens in EXCO solution, the influ- ence mechanism of corrosion on fatigue notch factor is expounded. Then, a two-parameter model used to describe the change of corrosion fatigue notch factor with time is established and verified by experiment. The results show that the pre-corrosion fatigue notch factor of LC4CS material decreases at first and then increases with the increasing pre-corrosion time. The inflection point appears at the beginning of denudation stage.展开更多
文摘The corrosion behavior and electrochemical impedance spectroscopy (EIS) features of 8090 Al-Li alloys in EXCO solution were investigated, and the EIS was simulated using an equivalent circuit. At the beginning of immersion in EXCO solution, the EIS is comprised by a depressed capacitive arc at high-mediate frequency and an inductive arc at low frequency, and the inductive component decreases and disappears with im- mersion time. Once exfoliation or severe pitting corrosion is produced, two capacitive arcs appear in the EIS. These two capacitive arcs are originated from the two parts of the corroded alloy surface, the original flat alloy surface and the new inter-face exposed to the aggressive EXCO solution due to the exfoliation or pitting corrosion. Some corrosion development features of 8090 Al-Li alloys in EXCO solution can be obtained through simulated EIS information.
基金Supported by the Program for Changjiang Scholars and Innovative Research Team of Ministry of Education(Irt0906)~~
文摘The notched and smooth specimens of aluminum alloy LC4CS soaked in EXCO solution for different time are tested under the constant amplitude cyclic loading to obtain S-N curves and fatigue notch factors with different pre-corrosion time. By analyzing the corrosion process of LC4CS specimens in EXCO solution, the influ- ence mechanism of corrosion on fatigue notch factor is expounded. Then, a two-parameter model used to describe the change of corrosion fatigue notch factor with time is established and verified by experiment. The results show that the pre-corrosion fatigue notch factor of LC4CS material decreases at first and then increases with the increasing pre-corrosion time. The inflection point appears at the beginning of denudation stage.