A new stearic acid method(SAM) has been used to prepare ultrafine K2La2Ti3O10 nanocrystalline. Each state of synthesis process was followed by the use of FT IR analysis. The resulting materials have been characterized...A new stearic acid method(SAM) has been used to prepare ultrafine K2La2Ti3O10 nanocrystalline. Each state of synthesis process was followed by the use of FT IR analysis. The resulting materials have been characterized by means of XRD, TEM, BET surface area analysis. The acid exchanging property of the obtained product was also studied. The experimental results showed that comparing with the product of traditional solid state reaction, the particle size of the K2La2Ti3O10 synthesized by SAM is greatly reduced, BET surface area is high(more than 11.83m2· g- 1) and has different acid exchanging properties. It can be easily exfoliated in 2mol· L- 1 HNO3 solution.展开更多
CeO2-based oxygen materials were prepared with co-precipitation method and characterized via Brunauer-Emmet Teller(BET)method,X-ray diffraction(XRD)and temperature-programmed reduction(H2-TPR).This paper revealed that...CeO2-based oxygen materials were prepared with co-precipitation method and characterized via Brunauer-Emmet Teller(BET)method,X-ray diffraction(XRD)and temperature-programmed reduction(H2-TPR).This paper revealed that three CeO2-based oxygen storage materials are all forming homogeneous solid solution.Among the samples,CeO2-ZrO2-Al2O3(CZA)has the best textural properties and excellent thermal stability.The specific surface area and pore volume of aged CZA are 90 m2/g and 0.29 mL/g.We proposed a viewpoint:Al3+ might insert among the interspace of fluorite structure or highly dispersal in solid solutions.展开更多
文摘A new stearic acid method(SAM) has been used to prepare ultrafine K2La2Ti3O10 nanocrystalline. Each state of synthesis process was followed by the use of FT IR analysis. The resulting materials have been characterized by means of XRD, TEM, BET surface area analysis. The acid exchanging property of the obtained product was also studied. The experimental results showed that comparing with the product of traditional solid state reaction, the particle size of the K2La2Ti3O10 synthesized by SAM is greatly reduced, BET surface area is high(more than 11.83m2· g- 1) and has different acid exchanging properties. It can be easily exfoliated in 2mol· L- 1 HNO3 solution.
文摘CeO2-based oxygen materials were prepared with co-precipitation method and characterized via Brunauer-Emmet Teller(BET)method,X-ray diffraction(XRD)and temperature-programmed reduction(H2-TPR).This paper revealed that three CeO2-based oxygen storage materials are all forming homogeneous solid solution.Among the samples,CeO2-ZrO2-Al2O3(CZA)has the best textural properties and excellent thermal stability.The specific surface area and pore volume of aged CZA are 90 m2/g and 0.29 mL/g.We proposed a viewpoint:Al3+ might insert among the interspace of fluorite structure or highly dispersal in solid solutions.