Zr-doped CuO-CeO2 catalysts for CO selective oxidation were designed and prepared by the hydrothermal method and coprecipitation. The experimental samples were characterized by means of N2 adsorption-desorption isothe...Zr-doped CuO-CeO2 catalysts for CO selective oxidation were designed and prepared by the hydrothermal method and coprecipitation. The experimental samples were characterized by means of N2 adsorption-desorption isotherms, powder X-ray diffraction, temperature-programmed reduction and Xray photoelectron spectroscopy. It is observed that the catalyst prepared by hydrothermal method exhibits larger specific surface area, smaller crystalline size and higher dispersion of active components compared with those of the catalyst obtained by coprecipitation. Meanwhile, redox properties of copper oxide are improved significantly and highly dispersed copper species providing CO oxidation sites are present on the surface. Furthermore, adsorptive centers of CO and active oxygen species increase on the copper-ceria interfaces. The Zr-doped CuO-CeO2 catalyst prepared by hydrothermal method possesses superior catalytic activity and selectivity for selective oxidation of CO at low temperature compared with those of the sample prepared by coprecipitation. The temperature corresponding to 50% CO conversion is only 73 ℃ and the temperature span of total CO conversion is expanded from 120 to 160 ℃.展开更多
In this paper,MCM-41 was synthesized by a soft template technique and MCM-41 supported CuO-CeO2 nano-sized catalysts with different Cu/Ce molar ratios were prepared by a deposition-precipitation method.N2 adsorption,H...In this paper,MCM-41 was synthesized by a soft template technique and MCM-41 supported CuO-CeO2 nano-sized catalysts with different Cu/Ce molar ratios were prepared by a deposition-precipitation method.N2 adsorption,HRTEM-EDS,H2-TPR,XPS characterization,as well as catalytic activity and durability tests for the catalytic combustion of chlorobenzene(CB)were conducted to explore the relationship between the structure and catalytic performance of the catalysts.It is revealed that cuCe(6:1)/MCM-41 has the highest activity and can completely catalyze the degradation of CB at 260℃.The reasons for the high activity of the catalysts are as follows:MCM-41,a type of mesoporous material which has large pore size and large specific surface area,is suitable as a catalyst carrier.The average diameter of nano-sized CuO and CeO2 particles is about 3-5 nm and adding CeO2 improves the dispersion of active component CuO,which are highly and evenly dispersed on the surface of MCM-41.Characterization results also explain why MCM-41 supported CuO-CeO2 with appropriate proportion can highly enhance the catalytic activity.The reason is that CeO2 acting as an oxygen-rich material can improve the mobility of oxygen species through continuous redox between Ce4^+and Ce3^+,and improve the catalytic performance of CuO for CB combustion.Besides,CuCe(6:1)/MCM-41 also displays good durability for CB combustion,both in the humid condition and in the presence of benzene,making it a promising catalytic material for the elimination of chlorinated VOCs.展开更多
Hollow CuO-CeO2-ZrO2nano-particles were prepared with supercritical anti-solvent apparatus by using methanol as sol-vent and supercritical carbon dioxide as anti-solvent. Two key factors （i.e., pressure and temperat...Hollow CuO-CeO2-ZrO2nano-particles were prepared with supercritical anti-solvent apparatus by using methanol as sol-vent and supercritical carbon dioxide as anti-solvent. Two key factors （i.e., pressure and temperature） were investigated to explore the effects of catalyst structure and physic-chemical properties （i.e., morphology, reducing property, oxygen storage capacity and specific surface area）. The resulting materials were characterized with X-ray diffraction （XRD）, high resolution transmission electron micros-copy （HRTEM）, Brunauer-Emmett-Teller （BET）,hydrogen temperature programmed reduction （H2-TPR） and oxygen storage capac-ity （OSC） measurement, respectively. The experimental results showed that lower temperatures promoted production of hollow struc-ture nano-particulates. The particle morphology also changed significantly, i.e. the solid construction was first transferred to hollow structure then back to solid construction. The optimal conditions for obtaining hollow nano-particles were determined at 45 °C, 18.0–24.0 MPa.展开更多
基金Project supported by the National Natural Science Foundation of China(21406174 and 51508435)
文摘Zr-doped CuO-CeO2 catalysts for CO selective oxidation were designed and prepared by the hydrothermal method and coprecipitation. The experimental samples were characterized by means of N2 adsorption-desorption isotherms, powder X-ray diffraction, temperature-programmed reduction and Xray photoelectron spectroscopy. It is observed that the catalyst prepared by hydrothermal method exhibits larger specific surface area, smaller crystalline size and higher dispersion of active components compared with those of the catalyst obtained by coprecipitation. Meanwhile, redox properties of copper oxide are improved significantly and highly dispersed copper species providing CO oxidation sites are present on the surface. Furthermore, adsorptive centers of CO and active oxygen species increase on the copper-ceria interfaces. The Zr-doped CuO-CeO2 catalyst prepared by hydrothermal method possesses superior catalytic activity and selectivity for selective oxidation of CO at low temperature compared with those of the sample prepared by coprecipitation. The temperature corresponding to 50% CO conversion is only 73 ℃ and the temperature span of total CO conversion is expanded from 120 to 160 ℃.
基金Project supported by the National Natural Science Foundation of China(21577094)Zhejiang Public Welfare Technology Research Project(LGG19B070003)the Foundation of Science and Technology of Shaoxing City(2018C10019)。
文摘In this paper,MCM-41 was synthesized by a soft template technique and MCM-41 supported CuO-CeO2 nano-sized catalysts with different Cu/Ce molar ratios were prepared by a deposition-precipitation method.N2 adsorption,HRTEM-EDS,H2-TPR,XPS characterization,as well as catalytic activity and durability tests for the catalytic combustion of chlorobenzene(CB)were conducted to explore the relationship between the structure and catalytic performance of the catalysts.It is revealed that cuCe(6:1)/MCM-41 has the highest activity and can completely catalyze the degradation of CB at 260℃.The reasons for the high activity of the catalysts are as follows:MCM-41,a type of mesoporous material which has large pore size and large specific surface area,is suitable as a catalyst carrier.The average diameter of nano-sized CuO and CeO2 particles is about 3-5 nm and adding CeO2 improves the dispersion of active component CuO,which are highly and evenly dispersed on the surface of MCM-41.Characterization results also explain why MCM-41 supported CuO-CeO2 with appropriate proportion can highly enhance the catalytic activity.The reason is that CeO2 acting as an oxygen-rich material can improve the mobility of oxygen species through continuous redox between Ce4^+and Ce3^+,and improve the catalytic performance of CuO for CB combustion.Besides,CuCe(6:1)/MCM-41 also displays good durability for CB combustion,both in the humid condition and in the presence of benzene,making it a promising catalytic material for the elimination of chlorinated VOCs.
基金supported by the National Natural Science Foundation of China(20976120)Natural Science Foundation of Tianjin(09JCYBJC06200)
文摘Hollow CuO-CeO2-ZrO2nano-particles were prepared with supercritical anti-solvent apparatus by using methanol as sol-vent and supercritical carbon dioxide as anti-solvent. Two key factors （i.e., pressure and temperature） were investigated to explore the effects of catalyst structure and physic-chemical properties （i.e., morphology, reducing property, oxygen storage capacity and specific surface area）. The resulting materials were characterized with X-ray diffraction （XRD）, high resolution transmission electron micros-copy （HRTEM）, Brunauer-Emmett-Teller （BET）,hydrogen temperature programmed reduction （H2-TPR） and oxygen storage capac-ity （OSC） measurement, respectively. The experimental results showed that lower temperatures promoted production of hollow struc-ture nano-particulates. The particle morphology also changed significantly, i.e. the solid construction was first transferred to hollow structure then back to solid construction. The optimal conditions for obtaining hollow nano-particles were determined at 45 °C, 18.0–24.0 MPa.