Cu/ZSM-5 and CeO_2-modified Cu/ZSM-5 catalysts were prepared by a wetness impregnation method. The addition of CeO_2 was found to enhance the NO_x selective catalytic reduction（SCR） activity of the catalyst at low t...Cu/ZSM-5 and CeO_2-modified Cu/ZSM-5 catalysts were prepared by a wetness impregnation method. The addition of CeO_2 was found to enhance the NO_x selective catalytic reduction（SCR） activity of the catalyst at low temperatures, but the high-temperature activity was weakened. The catalysts were characterized by X-ray diffraction（XRD）, nitrogen physisorption, inductively coupled plasma optical emission spectrometry（ICP-OES）, X-ray photoelectron spectroscopy（XPS）, electron paramagnetic resonance（EPR）, H_2 temperature-programmed reduction（TPR） and NH_3 temperature-programmed desorption（TPD）. The results showed that more CuO clusters instead of isolated Cu^（2＋） species were obtained on the modified catalyst. These active CuO clusters, as well as the Cu-Ce synergistic effect, improved the redox property of the catalyst and low-temperatures SCR activity via promoting the oxidation of NO to NO_2 and fast SCR reaction. The loss in high-temperatures activity was attributed to the enhanced competitive oxidation of NH_3 by O_2 and decreased surface acidity of the catalyst.展开更多
基金Project supported by the the National Natural Science Foundation of China(51372137)Ministry of Science and Technology,China(2015AA034603)
文摘Cu/ZSM-5 and CeO_2-modified Cu/ZSM-5 catalysts were prepared by a wetness impregnation method. The addition of CeO_2 was found to enhance the NO_x selective catalytic reduction（SCR） activity of the catalyst at low temperatures, but the high-temperature activity was weakened. The catalysts were characterized by X-ray diffraction（XRD）, nitrogen physisorption, inductively coupled plasma optical emission spectrometry（ICP-OES）, X-ray photoelectron spectroscopy（XPS）, electron paramagnetic resonance（EPR）, H_2 temperature-programmed reduction（TPR） and NH_3 temperature-programmed desorption（TPD）. The results showed that more CuO clusters instead of isolated Cu^（2＋） species were obtained on the modified catalyst. These active CuO clusters, as well as the Cu-Ce synergistic effect, improved the redox property of the catalyst and low-temperatures SCR activity via promoting the oxidation of NO to NO_2 and fast SCR reaction. The loss in high-temperatures activity was attributed to the enhanced competitive oxidation of NH_3 by O_2 and decreased surface acidity of the catalyst.