The atomic structure of the active sites in Cu/CeO2 catalysts is intimately associated with the copper-ceria interaction. Both the shape of ceria and the loading of copper affect the chemical bonding of copper species...The atomic structure of the active sites in Cu/CeO2 catalysts is intimately associated with the copper-ceria interaction. Both the shape of ceria and the loading of copper affect the chemical bonding of copper species on ceria surfaces and the electronic and geometric character of the relevant interfaces. Nanostructured ceria, including particles(polyhedra), rods, and cubes, provides anchoring sites for the copper species. The atomic arrangements and chemical properties of the(111),(110) and(100) facets, preferentially exposed depending on the shape of ceria, govern the copper-ceria interactions and in turn determine their catalytic properties. Also, the metal loading significantly influences the dispersion of copper species on ceria with a specific shape, forming copper layers, clusters, and nanoparticles. Lower copper contents result in copper monolayers and/or bilayers while higher copper loadings lead to multi-layered clusters and faceted particles. The active sites are usually generated via interactions between the copper atoms in the metal species and the oxygen vacancies on ceria, which is closely linked to the number and density of surface oxygen vacancies dominated by the shape of ceria.展开更多
CeO2 was synthesized via sol-gel process and used as supporter to prepare CuO/CeO2, Cu/CeO2 catalysts by impregnation method. The catalytic properties and characterization of CeO2, CuO/CeO2 and Cu/CeO2 catalysts were ...CeO2 was synthesized via sol-gel process and used as supporter to prepare CuO/CeO2, Cu/CeO2 catalysts by impregnation method. The catalytic properties and characterization of CeO2, CuO/CeO2 and Cu/CeO2 catalysts were examined by means of a microreactor-GC system, HRTEM, XRD, TPR and XPS techniques. The results show that CuO has not catalytic activity and the activity of CeO2 is quite low for CO oxidation. However, the catalytic activity of CuO/CeO2 and Cu/ CeO2 catalysts increases significantly. Furthermore, the activity of CuO/CeO2 is higher than that of Cu/CeO2 catalysts.展开更多
Cu/CeO2-ZrO2 catalysts for water-gas shift （WGS） reaction were prepared with co-precipitation method, and the influence of ZrO2 content on the catalytic structure and properties was investigated by the techniques of...Cu/CeO2-ZrO2 catalysts for water-gas shift （WGS） reaction were prepared with co-precipitation method, and the influence of ZrO2 content on the catalytic structure and properties was investigated by the techniques of N2 physical adsorption analysis, XRD and H2-TPR. The results indicate that the BET surface areas of the catalysts are increased in varying degrees due to the presence of ZrO2. With increasing ZrO2 content, the pore size distribution is centered on 1.9 nm. ZrO2 can efficiently restrain the growth of Cu crystal particles. The appropriate amount of ZrO2 in the Cu/CeO2 catalysts can help the catalyst keep better copper dispersion in the WGS reaction, which can lead to both higher catalytic activity and better thermal stability. When ZrO2 content is 10% （atom fraction）, Cu/CeO2-Zr02 catalyst reaches a CO conversion rate of 73.7% at the reaction temperature of 200℃.展开更多
文摘The atomic structure of the active sites in Cu/CeO2 catalysts is intimately associated with the copper-ceria interaction. Both the shape of ceria and the loading of copper affect the chemical bonding of copper species on ceria surfaces and the electronic and geometric character of the relevant interfaces. Nanostructured ceria, including particles(polyhedra), rods, and cubes, provides anchoring sites for the copper species. The atomic arrangements and chemical properties of the(111),(110) and(100) facets, preferentially exposed depending on the shape of ceria, govern the copper-ceria interactions and in turn determine their catalytic properties. Also, the metal loading significantly influences the dispersion of copper species on ceria with a specific shape, forming copper layers, clusters, and nanoparticles. Lower copper contents result in copper monolayers and/or bilayers while higher copper loadings lead to multi-layered clusters and faceted particles. The active sites are usually generated via interactions between the copper atoms in the metal species and the oxygen vacancies on ceria, which is closely linked to the number and density of surface oxygen vacancies dominated by the shape of ceria.
基金Projected supported by the National Natural Science Foundation of China (20271028) and Tianjin Natural Science Foundation(033602511)
文摘CeO2 was synthesized via sol-gel process and used as supporter to prepare CuO/CeO2, Cu/CeO2 catalysts by impregnation method. The catalytic properties and characterization of CeO2, CuO/CeO2 and Cu/CeO2 catalysts were examined by means of a microreactor-GC system, HRTEM, XRD, TPR and XPS techniques. The results show that CuO has not catalytic activity and the activity of CeO2 is quite low for CO oxidation. However, the catalytic activity of CuO/CeO2 and Cu/ CeO2 catalysts increases significantly. Furthermore, the activity of CuO/CeO2 is higher than that of Cu/CeO2 catalysts.
基金supported by the National Natural Science Foundation of China(10674042)Innovation Scientists and Technicians Troop Construction Projects of Henan Province,China(104200510014)~~
文摘Cu/CeO2-ZrO2 catalysts for water-gas shift （WGS） reaction were prepared with co-precipitation method, and the influence of ZrO2 content on the catalytic structure and properties was investigated by the techniques of N2 physical adsorption analysis, XRD and H2-TPR. The results indicate that the BET surface areas of the catalysts are increased in varying degrees due to the presence of ZrO2. With increasing ZrO2 content, the pore size distribution is centered on 1.9 nm. ZrO2 can efficiently restrain the growth of Cu crystal particles. The appropriate amount of ZrO2 in the Cu/CeO2 catalysts can help the catalyst keep better copper dispersion in the WGS reaction, which can lead to both higher catalytic activity and better thermal stability. When ZrO2 content is 10% （atom fraction）, Cu/CeO2-Zr02 catalyst reaches a CO conversion rate of 73.7% at the reaction temperature of 200℃.