The paper introduces the research and new development on soft-contacting electromagnetic continuous casting in Baosteel.At the year of 2008,Baosteel successfully completed the carbon steel SCEMCC industrial experiment...The paper introduces the research and new development on soft-contacting electromagnetic continuous casting in Baosteel.At the year of 2008,Baosteel successfully completed the carbon steel SCEMCC industrial experiment in a 6-strand curved type round billet caster.At the year of 2011,Baosteel selected another 3-strand curved billet caster. Baosteel successfully developed the SCEMCC mold for the first time to do the industrial production experiment for stainless steel round billet continuous casting.Then,in the same stainless steel caster,the square billet SCEMCC mold was successfully developed too.And at the beginning of the year 2012,the square billet SCEMCC of SUS304 and SUS303Cu was implemented up to now.It was proved the machine system was reliable for the long time production.The industrial experimental result shows the soft-contacting electromagnetic continuous casting can reduce the depth of oscillation mark from about 0.7mm to near zero.The SCEMCC billets without surface grinding were transferred to mill tubes,of which the quality is satisfied.展开更多
通过分析碳钢和不锈钢材质的电阻率差异性,以及304不锈钢软接触电磁连铸的中试试验结果,证实了不锈钢软接触电磁连铸的可行性。进而,在商业级规模铸机上分别开发了不锈钢圆坯和方坯软接触电磁连铸系统,进行了不同钢种、不同保护渣条件...通过分析碳钢和不锈钢材质的电阻率差异性,以及304不锈钢软接触电磁连铸的中试试验结果,证实了不锈钢软接触电磁连铸的可行性。进而,在商业级规模铸机上分别开发了不锈钢圆坯和方坯软接触电磁连铸系统,进行了不同钢种、不同保护渣条件下的相关工业生产试验。结果表明,不锈钢圆坯和方坯软接触电磁连铸在不超过150 k W的电源输出功率条件下,均能获得较佳的振痕去除效果,改善铸坯表面质量。对获得的铸坯进行免修磨轧制成?8 mm线材,并经过固溶热处理以及酸洗等工序,使线材成品的综合成材率提高3%以上。多次生产试验采用不间断连浇方式,期间,软接触电磁连铸设备系统生产稳定可靠,未发现液面异常波动以及铸坯低倍组织卷渣等缺陷,使软接触电磁连铸技术向商业化生产运营迈出了关键一步。最后,讨论了软接触电磁连铸技术拓展至不锈钢板坯断面的可行性。展开更多
文摘The paper introduces the research and new development on soft-contacting electromagnetic continuous casting in Baosteel.At the year of 2008,Baosteel successfully completed the carbon steel SCEMCC industrial experiment in a 6-strand curved type round billet caster.At the year of 2011,Baosteel selected another 3-strand curved billet caster. Baosteel successfully developed the SCEMCC mold for the first time to do the industrial production experiment for stainless steel round billet continuous casting.Then,in the same stainless steel caster,the square billet SCEMCC mold was successfully developed too.And at the beginning of the year 2012,the square billet SCEMCC of SUS304 and SUS303Cu was implemented up to now.It was proved the machine system was reliable for the long time production.The industrial experimental result shows the soft-contacting electromagnetic continuous casting can reduce the depth of oscillation mark from about 0.7mm to near zero.The SCEMCC billets without surface grinding were transferred to mill tubes,of which the quality is satisfied.
文摘通过分析碳钢和不锈钢材质的电阻率差异性,以及304不锈钢软接触电磁连铸的中试试验结果,证实了不锈钢软接触电磁连铸的可行性。进而,在商业级规模铸机上分别开发了不锈钢圆坯和方坯软接触电磁连铸系统,进行了不同钢种、不同保护渣条件下的相关工业生产试验。结果表明,不锈钢圆坯和方坯软接触电磁连铸在不超过150 k W的电源输出功率条件下,均能获得较佳的振痕去除效果,改善铸坯表面质量。对获得的铸坯进行免修磨轧制成?8 mm线材,并经过固溶热处理以及酸洗等工序,使线材成品的综合成材率提高3%以上。多次生产试验采用不间断连浇方式,期间,软接触电磁连铸设备系统生产稳定可靠,未发现液面异常波动以及铸坯低倍组织卷渣等缺陷,使软接触电磁连铸技术向商业化生产运营迈出了关键一步。最后,讨论了软接触电磁连铸技术拓展至不锈钢板坯断面的可行性。