The ineluctable introduction of lithium salt to polymer solid-state electrolytes incurs a compromise between strength,ionic conductivity,and thickness.Here,we propose Al_(2)O_(3)-coated polyimide(AO/PI)porous film as ...The ineluctable introduction of lithium salt to polymer solid-state electrolytes incurs a compromise between strength,ionic conductivity,and thickness.Here,we propose Al_(2)O_(3)-coated polyimide(AO/PI)porous film as a high-strength substrate to support fast-ion-conducting polymer-in-salt(PIS)solid-state electrolytes,aiming to suppress lithium dendrite growth and improve full-cell performance.The Al_(2)O_(3)coating layer not only refines the wettability of polyimide porous film to PIS,but also performs as a high modulus protective layer to suppress the growth of lithium dendrites.The resulting PI/AO@PIS exhibits a small thickness of only 35μm with an outstanding tensile strength of 11.3 MPa and Young's modulus of 537.6 MPa.In addition,the PI/AO@PIS delivers a high ionic conductivity of 0.1 m S/cm at 25°C.As a result,the PI/AO@PIS enables symmetric Li cells to achieve exceptional cyclability for over 1000 h at 0.1 m A/cm2without noticeable lithium dendrite formation.Moreover,the PI/AO@PIS-based LiFePO4||Li full cells demonstrate outstanding rate performance(125.7 m Ah/g at 5 C)and impressive cycling stability(96.1%capacity retention at 1 C after 200 cycles).This work highlights the efficacy of enhancing the mechanical properties of polymer matrices and extending cell performance through the incorporation of a dense inorganic interface layer.展开更多
Aluminum recovery is a key issue for the overall recycling of valuable metals from spent catalysts. This paper focuses on the recovery and regeneration of alumina with high additional value from the spent hydrodesulfu...Aluminum recovery is a key issue for the overall recycling of valuable metals from spent catalysts. This paper focuses on the recovery and regeneration of alumina with high additional value from the spent hydrodesulfurization catalyst CoMo/Al_2O_3. The results indicate that 98.13% alumina is successfully leached from the treated spent catalysts by an alkaline leaching process under the conditions of 5 mol·L^(-1) sodium hydroxide,a liquid/solid ratio of 20 ml·g^(-1),a temperature of 160 0 C and a reaction time of 4 h. In the leaching residue, no difficult leaching compound is found and cobalt and nickel are enriched,both of which are conducive to the subsequent metal recovery step. The reaction order of aluminum leaching is 0.99. This reaction fits well with the interfacial chemical reaction model, and its apparent activation energy is calculated as 45.50 kJ mol^(-1). Subsequently, y-Al_2O_3 with a high specific surface area of 278.3 m^2·g^(-1), a mean size of 2.2 μm and an average pore size of 3.10 nm is then regenerated from the lixivium, indicating its suitability for use as a catalyst carrier. The recovery and regeneration of alumina from spent catalysts can not only significantly contribute to the total recycling of such hazardous spent catalysts but also provide a new approach for the preparation of y-Al_2O_3 with a high specific surface area using spent catalysts as the aluminum sources.展开更多
Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub&...Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> was determined by nano-particle size analyzer, and the effects of nano-α-Al<sub>2</sub>O<sub>3</sub> content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al<sub>2</sub>O<sub>3</sub> dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al<sub>2</sub>O<sub>3</sub> increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al<sub>2</sub>O<sub>3</sub>.展开更多
基金the financial support from the 261Project of MIIT and Natural Science Foundation of Jiangsu Province(No.BK20240179)。
文摘The ineluctable introduction of lithium salt to polymer solid-state electrolytes incurs a compromise between strength,ionic conductivity,and thickness.Here,we propose Al_(2)O_(3)-coated polyimide(AO/PI)porous film as a high-strength substrate to support fast-ion-conducting polymer-in-salt(PIS)solid-state electrolytes,aiming to suppress lithium dendrite growth and improve full-cell performance.The Al_(2)O_(3)coating layer not only refines the wettability of polyimide porous film to PIS,but also performs as a high modulus protective layer to suppress the growth of lithium dendrites.The resulting PI/AO@PIS exhibits a small thickness of only 35μm with an outstanding tensile strength of 11.3 MPa and Young's modulus of 537.6 MPa.In addition,the PI/AO@PIS delivers a high ionic conductivity of 0.1 m S/cm at 25°C.As a result,the PI/AO@PIS enables symmetric Li cells to achieve exceptional cyclability for over 1000 h at 0.1 m A/cm2without noticeable lithium dendrite formation.Moreover,the PI/AO@PIS-based LiFePO4||Li full cells demonstrate outstanding rate performance(125.7 m Ah/g at 5 C)and impressive cycling stability(96.1%capacity retention at 1 C after 200 cycles).This work highlights the efficacy of enhancing the mechanical properties of polymer matrices and extending cell performance through the incorporation of a dense inorganic interface layer.
基金financially supported by the National Natural Science Commission-Yunnan Joint Fund Project (No.U1402274)
文摘Aluminum recovery is a key issue for the overall recycling of valuable metals from spent catalysts. This paper focuses on the recovery and regeneration of alumina with high additional value from the spent hydrodesulfurization catalyst CoMo/Al_2O_3. The results indicate that 98.13% alumina is successfully leached from the treated spent catalysts by an alkaline leaching process under the conditions of 5 mol·L^(-1) sodium hydroxide,a liquid/solid ratio of 20 ml·g^(-1),a temperature of 160 0 C and a reaction time of 4 h. In the leaching residue, no difficult leaching compound is found and cobalt and nickel are enriched,both of which are conducive to the subsequent metal recovery step. The reaction order of aluminum leaching is 0.99. This reaction fits well with the interfacial chemical reaction model, and its apparent activation energy is calculated as 45.50 kJ mol^(-1). Subsequently, y-Al_2O_3 with a high specific surface area of 278.3 m^2·g^(-1), a mean size of 2.2 μm and an average pore size of 3.10 nm is then regenerated from the lixivium, indicating its suitability for use as a catalyst carrier. The recovery and regeneration of alumina from spent catalysts can not only significantly contribute to the total recycling of such hazardous spent catalysts but also provide a new approach for the preparation of y-Al_2O_3 with a high specific surface area using spent catalysts as the aluminum sources.
文摘Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> was determined by nano-particle size analyzer, and the effects of nano-α-Al<sub>2</sub>O<sub>3</sub> content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al<sub>2</sub>O<sub>3</sub> dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al<sub>2</sub>O<sub>3</sub> increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al<sub>2</sub>O<sub>3</sub>.