Ba\-\{0.5\}Sr\-\{0.5\}Co\-\{0.8\}Fe\-\{0.2\}O\-\{3-\%δ\%\} and Ba\-\{0.5\}Sr\-\{0.5\}Co\-\{0.8\}Ti\-\{0.2\}O\-\{3-\%δ\%\} oxides were synthesized by a combined EDTA\|citrate complexing method. The catalytic behavior...Ba\-\{0.5\}Sr\-\{0.5\}Co\-\{0.8\}Fe\-\{0.2\}O\-\{3-\%δ\%\} and Ba\-\{0.5\}Sr\-\{0.5\}Co\-\{0.8\}Ti\-\{0.2\}O\-\{3-\%δ\%\} oxides were synthesized by a combined EDTA\|citrate complexing method. The catalytic behavior of these two oxides with the perovskite structure was studied during the reaction of methane oxidation. The pre\|treatment with methane has different effect on the catalytic activities of both the oxides. The methane pre\|treatment has not resulted in the change of the catalytic activity of BSCFO owing to its excellent reversibility of the perovskite structure resulting from the excellent synergistic interaction between Co and Fe in the oxide. However, the substitution with Ti on Fe\|site in the lattice makes the methane pre\|treatment have an obvious influence on the activity of the formed BSCTO oxide.展开更多
The yttrium iron garnet（YIG） thin films prepared by the sol-gel method and rapid thermal annealing（RTA） process for integrated inductor are investigated. The X-ray diffraction（XRD） results indicate that the YIG ...The yttrium iron garnet（YIG） thin films prepared by the sol-gel method and rapid thermal annealing（RTA） process for integrated inductor are investigated. The X-ray diffraction（XRD） results indicate that the YIG film annealed above 650 ℃ is poly-crystalline with single-phase garnet structure. Moreover, it can be found that the initial permeability μi, saturation magnetization MS and coercivity Hc of these YIG films increase with increasing RTA temperature. Low temperature annealing after crystallization can further improve the magnetic properties of YIG film. Thereby, a planar integrated inductor in the presence of Si substrate/SiO2 layer/Y2.8Bi0.2Fe5O12 thin film/Cu spiral coil structure is fabricated successfully by the standard IC processes. Due to the magnetic enhancement originated from YIG film, the inductance L and quality factor Q of the inductor with YIG film are improved in a certain frequency range.展开更多
Superparamagnetic monodisperse Mg0.8Mn0.2Fe2O4 nanoparticles have been successfully synthesized in liquid polyol at elevated temperature of 200 °C. Diethylene glycol（DEG） used here plays dual role in synthesis ...Superparamagnetic monodisperse Mg0.8Mn0.2Fe2O4 nanoparticles have been successfully synthesized in liquid polyol at elevated temperature of 200 °C. Diethylene glycol（DEG） used here plays dual role in synthesis as it acts as reducing agent and alternatively coats the surface of nanoparticles while synthesis and thereby maintaining uniform size and dispersibility. Powder X-ray diffraction（XRD） and magnetic measurements showed that the sample is cubic spinel and superparamagnetic at room temperature. Raman spectra confirmed the formation of the Mg0.8Mn0.2Fe2O4 nanoparticles.The nanoparticles exhibit very good stability in water due to in situ coating with DEG molecules.展开更多
Ni0.4Cu0.2Zn0.4Fe2O4 thin films were fabricated on Si substrates by using the sol-gel method and rapid thermal annealing （RTA）, and their magnetic properties and crystalline structures were investigated. The samples...Ni0.4Cu0.2Zn0.4Fe2O4 thin films were fabricated on Si substrates by using the sol-gel method and rapid thermal annealing （RTA）, and their magnetic properties and crystalline structures were investigated. The samples calcined at and above 600 ℃ have a single-phase spinel structure and the average grain size of the sample calcined at 600 ℃ is about 20 nm. The initial permeability μi, saturation magnetization M and coercivity H of the samples increase with the increasing calcination temperature. The sample calcined at 600 ℃ exhibits an excellent soft magnetic performance, which has μi=33.97 （10 MHz）, Hc=15.62 Oe and Ms=228.877 emu/cm^3. Low-temperature annealing can enhance the magnetic properties of the samples. The work shows that using the sol-gel method in conjunction with RTA is a promising way to fabricate integrated thin-film devices.展开更多
文摘Ba\-\{0.5\}Sr\-\{0.5\}Co\-\{0.8\}Fe\-\{0.2\}O\-\{3-\%δ\%\} and Ba\-\{0.5\}Sr\-\{0.5\}Co\-\{0.8\}Ti\-\{0.2\}O\-\{3-\%δ\%\} oxides were synthesized by a combined EDTA\|citrate complexing method. The catalytic behavior of these two oxides with the perovskite structure was studied during the reaction of methane oxidation. The pre\|treatment with methane has different effect on the catalytic activities of both the oxides. The methane pre\|treatment has not resulted in the change of the catalytic activity of BSCFO owing to its excellent reversibility of the perovskite structure resulting from the excellent synergistic interaction between Co and Fe in the oxide. However, the substitution with Ti on Fe\|site in the lattice makes the methane pre\|treatment have an obvious influence on the activity of the formed BSCTO oxide.
基金Funded by the National Natural Science Foundation of China(No.11174226)
文摘The yttrium iron garnet（YIG） thin films prepared by the sol-gel method and rapid thermal annealing（RTA） process for integrated inductor are investigated. The X-ray diffraction（XRD） results indicate that the YIG film annealed above 650 ℃ is poly-crystalline with single-phase garnet structure. Moreover, it can be found that the initial permeability μi, saturation magnetization MS and coercivity Hc of these YIG films increase with increasing RTA temperature. Low temperature annealing after crystallization can further improve the magnetic properties of YIG film. Thereby, a planar integrated inductor in the presence of Si substrate/SiO2 layer/Y2.8Bi0.2Fe5O12 thin film/Cu spiral coil structure is fabricated successfully by the standard IC processes. Due to the magnetic enhancement originated from YIG film, the inductance L and quality factor Q of the inductor with YIG film are improved in a certain frequency range.
基金the Council of Scientific and Industrial Research, India for the award of senior research fellowship (File. 09/1077/(0001)/ 2012/EMR-1)
文摘Superparamagnetic monodisperse Mg0.8Mn0.2Fe2O4 nanoparticles have been successfully synthesized in liquid polyol at elevated temperature of 200 °C. Diethylene glycol（DEG） used here plays dual role in synthesis as it acts as reducing agent and alternatively coats the surface of nanoparticles while synthesis and thereby maintaining uniform size and dispersibility. Powder X-ray diffraction（XRD） and magnetic measurements showed that the sample is cubic spinel and superparamagnetic at room temperature. Raman spectra confirmed the formation of the Mg0.8Mn0.2Fe2O4 nanoparticles.The nanoparticles exhibit very good stability in water due to in situ coating with DEG molecules.
基金the National Natural Science Foundation of China (No. 90607021).
文摘Ni0.4Cu0.2Zn0.4Fe2O4 thin films were fabricated on Si substrates by using the sol-gel method and rapid thermal annealing （RTA）, and their magnetic properties and crystalline structures were investigated. The samples calcined at and above 600 ℃ have a single-phase spinel structure and the average grain size of the sample calcined at 600 ℃ is about 20 nm. The initial permeability μi, saturation magnetization M and coercivity H of the samples increase with the increasing calcination temperature. The sample calcined at 600 ℃ exhibits an excellent soft magnetic performance, which has μi=33.97 （10 MHz）, Hc=15.62 Oe and Ms=228.877 emu/cm^3. Low-temperature annealing can enhance the magnetic properties of the samples. The work shows that using the sol-gel method in conjunction with RTA is a promising way to fabricate integrated thin-film devices.