The high-entropy alloy composite coatings AlCu_(2)Ti(NiCr)_(2)-(WC)_(x)(x denotes powder feeding speeds,including 0,25,50,and 75 r/min)were prepared by plasma cladding using a hybrid mode of AlCu_(2)(NiCr)_(2)Ti cable...The high-entropy alloy composite coatings AlCu_(2)Ti(NiCr)_(2)-(WC)_(x)(x denotes powder feeding speeds,including 0,25,50,and 75 r/min)were prepared by plasma cladding using a hybrid mode of AlCu_(2)(NiCr)_(2)Ti cable-type welding wire(CWW)and tungsten carbide(WC)powder.The effect of WC powder feeding speed on the microstructure,hardness,and wear properties of the prepared coatings was investigated.The results show that the coatings consist of body-centered cubic main phases and face-centered cubic secondary phases,with carbide reinforcement phases formed due to the addition of WC.The hardness and wear resistance of the coatings are significantly improved compared to the TC11 substrate.When WC powder feeding speed is set at 50 r/min,the coating exhibits optimal wear resistance,with a minimum volume wear rate of 8.5869×10^(-6)mm^(3)·N^(-1)·m^(-1),greatly improving the wear properties of TC11 surface.The coincident CWW-powder plasma cladding provides a viable method for the preparation of highentropy alloy composite coatings with enhanced wear resistance.展开更多
Co-based alloy coating was prepared on Zr alloy using laser melting and cladding technique to study the difference in the high-temperature oxidation behavior between pure metal Co coatings and Co-T800 alloy coatings,a...Co-based alloy coating was prepared on Zr alloy using laser melting and cladding technique to study the difference in the high-temperature oxidation behavior between pure metal Co coatings and Co-T800 alloy coatings,as well as the wear resistance of the coatings.Besides,the effect of changing the laser melting process on the coatings was also investigated.The oxidation mass gain at 800–1200℃and the high-temperature oxidation behavior during high-temperature treatment for 1 h of two coated Zr alloy samples were studied.Results show that the Co coating and the Co-T800 coating have better resistance against high-temperature oxidation.After oxidizing at 1000℃for 1 h,the thickness of the oxide layer of the uncoated sample was 241.0μm,whereas that of the sample with Co-based coating is only 11.8–35.5μm.The friction wear test shows that the depth of the abrasion mark of the coated sample is only 1/2 of that of the substrate,indicating that the hardness and wear resistance of the Zr substrate are greatly improved.The disadvantage of Co-based coatings is the inferior corrosion resistance in 3.5wt%NaCl solution.展开更多
To solve the problems of deformation,micro-cracks,and residual tensile stress in laser cladding coatings,the technique of laser cladding with Fe-based memory alloy can be considered.However,the process of in-situ synt...To solve the problems of deformation,micro-cracks,and residual tensile stress in laser cladding coatings,the technique of laser cladding with Fe-based memory alloy can be considered.However,the process of in-situ synthesis of Fe-based memory alloy coatings is extremely complex.At present,there is no clear guidance scheme for its preparation process,which limits its promotion and application to some extent.Therefore,in this study,response surface methodology(RSM)was used to model the response surface between the target values and the cladding process parameters.The NSGA-2 algorithm was employed to optimize the process parameters.The results indicate that the composite optimization method consisting of RSM and the NSGA-2 algorithm can establish a more accurate model,with an error of less than 4.5%between the predicted and actual values.Based on this established model,the optimal scheme for process parameters corresponding to different target results can be rapidly obtained.The prepared coating exhibits a uniform structure,with no defects such as pores,cracks,and deformation.The surface roughness and microhardness of the coating are enhanced,the shaping quality of the coating is effectively improved,and the electrochemical corrosion performance of the coating in 3.5%NaCl solution is obviously better than that of the substrate,providing an important guide for engineering applications.展开更多
Conventional Fe-C alloy parts used in mechanical transmission and braking systems exposed to the external environment often suffer from wear and corrosion failures.Surface coating strengthening technologies have been ...Conventional Fe-C alloy parts used in mechanical transmission and braking systems exposed to the external environment often suffer from wear and corrosion failures.Surface coating strengthening technologies have been explored to improve the surface performance and prolong service life of these parts.Among these technologies,laser cladding has shown promise in producing Fe-based alloy coatings with superior interfacial bonding properties to the Fe-C alloy substrate.Additionally,the microstructure of the Fe-based alloy coating is more uniform and the grain size is finer than that of surfacing welding,thermal spraying,and plasma cladding,and the oxide film of alloying elements on the coating surface can improve the coating performance.However,Fe-based alloy coatings produced by laser cladding typically exhibit lower hardness,lower wear resistance,corrosion resistance,and oxidation resistance compared to coatings based on Co and Ni alloys.Moreover,these coatings are susceptible to defects such as pores and cracks.To address these limitations,the incorporation of rare-earth oxides through doping in the laser cladding process has garnered significant attention.This approach has demonstrated substantial improvements in the microstructure and properties of Fe-based alloy coatings.This paper reviewed recent research on the structure and properties of laser-cladded Fe-based alloy coatings doped with various rare earth oxides,including La_(2)O_(3),CeO_(2),and Y_(2)O_(3).Specifically,it discussed the effects of rare earth oxides and their concentrations on the structure,hardness,friction,wear,corrosion,and oxidation characteristics of these coatings.Furthermore,the mechanisms by which rare earth oxides influence the coating’s structure and properties were summarized.This review aimed to serve as a valuable reference for the application and advancement of laser cladding technology for rare earth modified Fe-based alloy coatings.展开更多
The effects of Y_(2)O_(3) on the microstructure, microhardness, wear resistance, high-temperature oxidation resistance, hot corrosion resistance, and electrochemical corrosion behaviour of CoCrFeNiTiNb high entropy al...The effects of Y_(2)O_(3) on the microstructure, microhardness, wear resistance, high-temperature oxidation resistance, hot corrosion resistance, and electrochemical corrosion behaviour of CoCrFeNiTiNb high entropy alloy coatings formed on Ti-6Al-4V alloy surfaces were studied. The results show that the addition of Y_(2)O_(3) changes the proportion of the phase but does not change its type. The average grain size is only 1/4.7 of that of the high entropy alloy(HEA) coating, and the fine-grained strengthening leads to increases in the microhardness and wear resistance of 21.8% and 26.9%, respectively. The addition of Y_(2)O_(3) enhances the denseness and bonding properties of the oxide and corrosion product layers, reducing the oxidation and hot corrosion rates by 60.3% and 40.3%, respectively. The addition of Y_(2)O_(3) doubles the corrosion resistance which is attributed to the refinement of the grains, the increased proportion of HCP and TiN, and the weakening of galvanic coupling corrosion.展开更多
(Zr_(0.53)Al_(0.1)Ni_(0.05)Cu_(0.3)Ti_(0.02))_(99)Y_1(at%)coating with amorphous layer of about 180μm thick was prepared on a steel substrate by using laser cladding method.The coating is compact and shows good metal...(Zr_(0.53)Al_(0.1)Ni_(0.05)Cu_(0.3)Ti_(0.02))_(99)Y_1(at%)coating with amorphous layer of about 180μm thick was prepared on a steel substrate by using laser cladding method.The coating is compact and shows good metallurgical bonding with substrate.The microstructure,microhardness and corrosion behavior along the depth from the coating surface to the substrate were investigated.It is found that a gradient structure consisted of amorphous surface layer,amorphous-crystalline transitional layer and substrate is formed after the laser cladding.The microhardness and corrosion behavior exhibit variation with the microstructural evolution at different depths from the coating surface.The microhardness and corrosion resistance in 3.5 wt%NaCl solution of the amorphous surface layer are comparable to those of the as-cast Zr-based BMG with the same composition,and higher than those of the steel substrate.展开更多
The effect of the gradient content of Co element on the solidification process of Cu-based alloy under deep under cooling conditions was explored.The non-equilibrium solidification structure of the under cooled alloy ...The effect of the gradient content of Co element on the solidification process of Cu-based alloy under deep under cooling conditions was explored.The non-equilibrium solidification structure of the under cooled alloy samples were analyzed.It is found that the rapidly solidified alloy has undergone twice grain refinement during the undercooling process.Characterization and significance of the maximum undercooling refinement structure of Cu60Ni35Co5 at T=253 K were analyzed.High-density defects were observed,such as dislocations,stacking faults networks,and twinning structures.The standard FCC diffraction pattern represents that it is still a single-phase structure.Based on the metallographic diagram,EBSD and TEM data analysis,it is illustrated that the occurrence of grain refinement under high undercooling is due to stress induced recrystallization.In addition,the laser cladding technology is used to coat Co-based alloy(Stellite12) coating on 304 stainless steel substrate;the microstructure of the coating cross-section was analyzed.It was found that the microstructure of the cross-section is presented as columnar crystals,planar crystals,and disordered growth direction,so that the coating has better hardness and wear resistance.By electrochemical corrosion of the substrate and coating,it can be seen that the Co and Cr elements present in the coating are more likely to form a dense passivation film,which improved the corrosion resistance of the coating.展开更多
21-4N(5Cr21Mn9Ni4N)is extensively employed in the production of engine valves,operating under severe conditions.Apart from withstanding high-temperature gas corrosion,it must also endure the impact of cylinder explosi...21-4N(5Cr21Mn9Ni4N)is extensively employed in the production of engine valves,operating under severe conditions.Apart from withstanding high-temperature gas corrosion,it must also endure the impact of cylinder explosion pressure.The predominant failure mode of 21-4N valves is abrasive wear.Surface coatings serve as an effective approach to prevent such failures.In this investigation,Laser cladding technology was utilized to fabricate AlCoCrFeNiTi high entropy alloy coatings onto the surfaces of 21-4N valves.According to the findings,the cladding zone has a normal dendritic microstructure,a good substrate-to-cladding layer interaction,and no obvious flaws.In terms of hardness,the cladding demonstrates an average hardness of 620 HV.The hardness has increased by 140%compared to the substrate.The average hardness of the cladding remains at approximately 520 HV even at elevated temperatures.Regarding frictional wear performance,between 400℃and 800℃,the cladding layer exhibits an average friction coefficient of 0.4,with the primary wear mechanisms being abrasive wear,adhesive wear,and a minor degree of plastic deformation.展开更多
The key components of engineering machinery frequently failed due to working in the high load and high wear operating envir-onment.And the performance of the Fe-based alloy coatings typically employed need to be impro...The key components of engineering machinery frequently failed due to working in the high load and high wear operating envir-onment.And the performance of the Fe-based alloy coatings typically employed need to be improved for fulfilling the service requirements.Herein,a TiC strengthened Fe-based alloy cladding layer,named TiC-Fe coating,was designed and prepared by plasma cladding technology.The frictional wear performance of coating under various loads was tested.The wear morphology of the coating was observed,and its wear mechanism was examined.The results indicated that the TiC-Fe coating was well formed and metallurgically bonded to the Q345C substrate.Its microstructure mainly consisted of Fe-Cr solid solution,α-Fe phase,(Fe,Cr)_(7)C_(3) phase and TiC phase.The coating exhibited an average microhardness of 980 HV0.2,which was about 5.4 times that of the Q345C substrate.The wear mass loss of the TiC-Fe coatings was much smaller than that of the Q345C substrate,which indicated that the wear resistance of the Q345C coating was superior to the substrate,and the wear mechanism of the coating was mainly attributed to the abrasive wear.展开更多
The MCrAlY coating has been potential candidate for the parts applied in friction and corrosion conditions, and CNTs (carbon nanotubes) are expected to improve the service performance of coatings owing to high lubrica...The MCrAlY coating has been potential candidate for the parts applied in friction and corrosion conditions, and CNTs (carbon nanotubes) are expected to improve the service performance of coatings owing to high lubrication and low chemical reactivity. In this work, a systematic investigation on the tribological and corrosion properties of CoCrAlYTaSiC-xCNTs coatings deposited by laser melting was analyzed. Results showed that the coatings had good-quality without typical metallurgical defects. The CNTs addition homogenized and refined the microstructure of coating, and also improved the tribological and corrosion properties. As the CNTs content changed from 0 to 4 wt%, the wear rate of coating decreased from 16.23 × 10^(-3) to 7.58 × 10^(-3) mg m^(−1), the jcorr of coating decreased from 4.13 × 10^(-4) to 1.23 × 10^(-4) A cm^(−2), and the Rct values increased from 12.69 to 25.07 Ω cm2.展开更多
To improve the wear performance of CoCrAlYTa coating,part of the carbon nanotubes(CNTs)chemically reacted with Ta to form reinforcement phase(TaC),while the other CNTs were retained as lubrication phase.Subsequently,t...To improve the wear performance of CoCrAlYTa coating,part of the carbon nanotubes(CNTs)chemically reacted with Ta to form reinforcement phase(TaC),while the other CNTs were retained as lubrication phase.Subsequently,the CoCrAlYTa-xCNTs(x=0,1,2,and 4;wt%)composite coatings were prepared by laserinduction hybrid cladding(LIHC),and the microstructure and wear resistance of coatings were systematically analyzed.Results show that the coatings are mainly composed of TaC,y-(Co,Cr)andβ-(Co,Cr)Al.As the CNTs content increases from 0 wt%to 4 wt%,the volume fraction of TaC increases from 13.11 vol%to 16.12 vol%.Meanwhile,the nano-hardness ofγ-(Co,Cr)andβ-(Co,Cr)Al are improved from 7.49 and 9.72 to 9.36 and 11.19 GPa,respectively.As a result,the microhardness of coating increases from HV536.25 to HV 738.16,the wear rate decreases from32.4×10^(-3)to 6.1×10^(-3)mg·m^(-1),and the average friction coefficient decreases from 0.55 to 0.44.The good wear performance of the coating is attributed to the formation of TaC and the existence of remained CNTs lubricant film.展开更多
The atmospheric corrosion monitoring(ACM)technique has been widely employed to track the real-time corrosion behavior of metal materials.However,limited studies have applied ACM to the corrosion protection properties ...The atmospheric corrosion monitoring(ACM)technique has been widely employed to track the real-time corrosion behavior of metal materials.However,limited studies have applied ACM to the corrosion protection properties of organic coatings.This study compared a bare epoxy coating with one containing zinc phosphate corrosion inhibitors,both applied on ACM sensors,to observe their corrosion protection properties over time.Coatings with artificial damage via scratches were exposed to immersion and alternating dry and wet environments,which allowed for monitoring galvanic corrosion currents in real-time.Throughout the corrosion tests,the ACM currents of the zinc phosphate/epoxy coating were considerably lower than those of the blank epoxy coating.The trend in ACM current variations closely matched the results obtained from regular electrochemical tests and surface analysis.This alignment highlights the potential of the ACM technique in evaluating the corrosion protection capabilities of organic coatings.Compared with the blank epoxy coating,the zinc phosphate/epoxy coating showed much-decreased ACM current values that confirmed the effective inhibition of zinc phosphate against steel corrosion beneath the damaged coating.展开更多
In order to improve the sealing surface performance of gray cast iron gas gate valves and achieve precise molding control of the cladding layer,as well as to reveal the influence of laser cladding process parameters o...In order to improve the sealing surface performance of gray cast iron gas gate valves and achieve precise molding control of the cladding layer,as well as to reveal the influence of laser cladding process parameters on the morphology and structure of the cladding layer,we prepared the 316L coating on HT 200 by using Design-Expert software central composite design(CCD)based on response surface analysis.We built a regression prediction model and analyzed the ANOVA with the inspection results.With a target cladding layer width of 3.5 mm and height of 1.3 mm,the process parameters were optimized to obtain the best combination of process parameters.The microstructure,phases,and hardness variations of the cladding layer from experiments with optimal parameters were analyzed by the metallographic microscope,confocal microscope,and microhardness instrument.The experimental results indicate that laser power has a significant impact on the cladding layer width,followed by powder feed rate;scan speed has a significant impact on the cladding layer height,followed by powder feed rate.The HT200 substrate and 316L can metallurgically bond well,and the cladding layer structure consists of dendritic crystals,columnar crystals,and equiaxed crystals in sequence.The optimal process parameter combination satisfying the morphology requirements is laser power(A)of 1993 W,scan speed(B)of 8.949 mm/s,powder feed rate(C)of 1.408 r/min,with a maximum hardness of 1564.3 HV0.5,significantly higher than the hardness of the HT200 substrate.展开更多
WC particles reinforced CoCrFeNiMo high-entropy alloy(HEA)composite coatings were prepared on Cr12MoV steel successfully by laser cladding technology to improve the wear resistance of substrates.Effect of WC content o...WC particles reinforced CoCrFeNiMo high-entropy alloy(HEA)composite coatings were prepared on Cr12MoV steel successfully by laser cladding technology to improve the wear resistance of substrates.Effect of WC content on microstructure and wear property of the composite coatings was studied in detail.Large numbers of carbides with four main types:primary carbide crystals,eutectic structures,massive crystals growing along the periphery of the remaining WC particles and incompletely fused WC particles,were found to exist in the WC/CoCrFeNiMo composite coatings.With increasing WC content,the microhardness of coatings is gradually improved while the average friction coefficients follow the opposite trend due to solid solution strengthening and second phase strengthening effect.The maximum microhardness and minimum friction coefficient are HV_(0.2)689.7 and 0.72,respectively,for the composite coating with 30 wt.%WC,the wear resistance of the substrate is improved significantly,the wear mechanisms are spalling wear and abrasive wear due to their high microhardness.展开更多
Proton exchange membrane water electrolysis(PEMWE)is one of the most promising strategies to pro-duce green hydrogen energy,and it is crucial to exploit highly conductive and good corrosion-resistant coatings on bipol...Proton exchange membrane water electrolysis(PEMWE)is one of the most promising strategies to pro-duce green hydrogen energy,and it is crucial to exploit highly conductive and good corrosion-resistant coatings on bipolar plates(BPs),one of the core components in PEMWE cells.In this work,NbN coatings are deposited on Ti BPs by magnetron sputtering to improve the corrosion resistance and conductivity,for which the critical process parameters,such as the working pressure,partial nitrogen pressure and de-position temperature are well optimized.It is found that the compact microstructure,highly conductive δ-NbN and uniform nanoparticles play a dominant role in the synergistic improvement of the corrosion resistance and electrical conductivity of NbN coatings.The optimized NbN coatings exhibit excellent cor-rosion resistance with the low corrosion current density of 1.1×10^(-8) A cm^(-2),a high potential value of-0.005 V vs.SCE and a low ICR value of 15.8 mΩcm2@1.5 MPa.Accordingly,NbN coatings can be a promising candidate for the development of the low-cost and high-anti-corrosion Ti BPs of PEMWE.展开更多
Corrosion activities and related accidents are significant issues for marine facilities,leading to considerable economic losses.Waterborne epoxy(EP)coating has been seen as one of the optimal options for corrosion pro...Corrosion activities and related accidents are significant issues for marine facilities,leading to considerable economic losses.Waterborne epoxy(EP)coating has been seen as one of the optimal options for corrosion protection due to its stable properties and eco-friendliness(0 g/L volatile organic compounds).Nevertheless,several intrinsic deficiencies require improvement,such as fragile mechanical properties and defects(macro and micro),resulting in the continuous deterioration of comprehensive coating performances.In this work,a novel nanocomposite coating with mechanical enhancement,intelligent self-reporting,and active protection is fabricated by integrating the functionalized and compatible graphene oxide/cerium based metal-organic framework multiscale structure(GO-CeMOF-P/M).Notably,the homogenous dispersion of GO-CeMOF-P/M and its chemical interaction with the polymer matrix effectively reduces the defects resulting from solution volatilizing and enhances the compactness,which boosts the tensile strength(32.1 MPa/8.5%)and dry adhesion force(5.8 MPa)of the coating.Additionally,the controllable responsiveness and release of multiscale nanocomposite within external environments endow intelligent active protection and self-reporting characteristics for the GO-CeMOF-P/M-EP coating,making it especially suitable for a variety of practical marine applications.Furthermore,following immersion of 80 d in the aggressive environment,Zf=0.01 Hz value of GO-CeMOF-P/M-EP coating is 1.2×10^(10)Ωcm^(2),which is 164.4 times larger than that of EP coating(7.3×10^(7)Ωcm^(2)),demonstrating remarkably strengthened anti-corrosion ability.Consequently,by offering an intriguing design strategy,the current work anticipates addressing the inherent deficiencies of EP coating and facilitating its practicality and feasibility in real sea environments.展开更多
In this work,a novel surface strengthening strategy for Mg-Li alloys was proposed,called cold spraying assisted high-speed laser cladding.CuAl9 aluminum bronze coating was firstly deposited on Mg-Li alloy by cold spra...In this work,a novel surface strengthening strategy for Mg-Li alloys was proposed,called cold spraying assisted high-speed laser cladding.CuAl9 aluminum bronze coating was firstly deposited on Mg-Li alloy by cold spraying,and then CoCrFe_(0.5)Ni_(1.5)Mo_(0.1)Nb_(0.68)eutectic highentropy alloy(EHEA)coating was prepared on the CuAl9 coating utilizing high-speed laser cladding.A gradient coating consisted of in-situ transition region and EHEA layer formed by bidirectional diffusion.The in-situ transition region was composed ofβ-Li,Cu_(2)Mg and Cu_(3)Al_(2)phases.TEM analysis indicated that Cu_(2)Mg and Cu_(3)Al_(2)phases were well matched with theβ-Li matrix phase.The EHEA coating had a nano-lamellar eutectic microstructure with relatively small lamellar-spacing(<100 nm).Metallurgical bonding interfaces formed between the EHEA coating,transition region and Mg-Li substrate.The evolution mechanism of the coating was revealed from the perspectives of mixing enthalpy,atomic radius difference and laser energy distribution.In 3.5 wt.%NaCl solution,the corrosion potential of the EHEA coating(-24 m VSHE)was 1345 m VSHEhigher than that of Mg-Li alloy(-1369 m VSHE),while the corrosion current density of the EHEA coating(3.13×10^(-7)A·cm^(-2))was almost three orders of magnitude lower than that of Mg-Li alloy(1.25×10^(-4)A·cm^(-2)).The wear rate of Mg-Li alloy(1.11×10^(-3)mm^(3)/N·m)was about 36 times higher than that of the EHEA coating(3.05×10^(-5)mm^(3)/N·m).展开更多
The present work aims to stabilize the room temperature allotropic transition of ammonium nitrate(AN)particles utilizing a microencapsulation technique,which involves solvent/non-solvent in which nitrocellulose(NC)has...The present work aims to stabilize the room temperature allotropic transition of ammonium nitrate(AN)particles utilizing a microencapsulation technique,which involves solvent/non-solvent in which nitrocellulose(NC)has been employed as a coating agent.The SEM micrographs revealed distinct features of both pure AN and NC,contrasting with the irregular granular surface topography of the coated AN particles,demonstrating the adherence of NC on the AN surface.Structural analysis via infrared spectroscopy(IR)demonstrated a successful association of AN and NC,with slight shifts observed in IR bands indicating interfacial interactions.Powder X-ray Diffraction(PXRD)analysis further elucidated the structural changes induced by the coating process,revealing that the NC coating altered the crystallization pattern of its pure form.Thermal analysis demonstrates distinct profiles for pure and coated AN,for which the coated sample exhibits a temperature increase and an enthalpy decrease of the room temperature allotropic transition by 6℃,and 36%,respectively.Furthermore,the presence of NC coating alters the intermolecular forces within the composite system,leading to a reduction in melting enthalpy of coated AN by~39%compared to pure AN.The thermal decomposition analysis shows a two-step thermolysis process for coated AN,with a significant increase in the released heat by about 78%accompanied by an increase in the activation barrier of NC and AN thermolysis,demonstrating a stabilized reactivity of the AN-NC particles.These findings highlight the synergistic effect of NC coating on AN particles,which contributed to a structural and reactive stabilization of both AN and NC,proving the potential application of NC-coated AN as a strategically advantageous oxidizer in composite solid propellant formulations.展开更多
Polyurethane-fluorinated polysiloxane(PU-^(F)PDMS)with high-strength,high-bonding and low surface en-ergy is synthesized as the matrix,and the PU-^(F)PDMS/MCs/Ag marine anti-fouling coating on the sur-face of imitatio...Polyurethane-fluorinated polysiloxane(PU-^(F)PDMS)with high-strength,high-bonding and low surface en-ergy is synthesized as the matrix,and the PU-^(F)PDMS/MCs/Ag marine anti-fouling coating on the sur-face of imitation crab shells is constructed by assembling butenolide@1,1-stilbene-modified hydrolyzed polyglycidyl methacrylate/graphene oxide microcapsules(Bu@PGMAm/GO MCs)with compact multi-shell structure and Ag nanoparticles(AgNPs)step by step on the PU-^(F)PDMS matrix.The PU-^(F)PDMS/MCs/Ag bionic anti-fouling coatings achieve long-term and stable anti-fouling effect under the combination of robust low-surface-energy PU-^(F)PDMS matrix,steady-state sustained release of butenolide encapsulated by the compact multi-shell,bionic surface formed by the microcapsules and AgNPs,and the release of Ag^(+).The shear strength,tensile strength,and elongation at break of the PU-^(F)PDMS/MCs/Ag are 3.53 MPa,6.7 MPa,and 192.83%,respectively.Its static contact angle and sliding angle are 161.8°and 3.6°,respectively.The antibacterial rate of PU-^(F)PDMS/MCs/Ag against Escherichia coli,Staphylococcus aureus,and Candida albicans can reach 100%.Compared with glass blank,PU,PU-^(F)PDMS,PU-^(F)PDMS/Ag,and PU-^(F)PDMS/MCs,both the adhesion number and coverage percentage of chlorella adhere to PU-^(F)PDMS/MCs/Ag are the minimum values,which are 600 cell mm^(-2) and 1.53%,respectively.After 6 months of marine field test,the primer blank,PU,PU-^(F)PDMS all show different degrees of attachment by shellfish,spirorbis,al-gae and other biofouling,while the PU-^(F)PDMS/MCs/Ag coating is still not covered with biofouling,while the PU-^(F)PDMS/MCs/Ag coatings still exhibit little attachment of marine fouling.The PU-^(F)PDMS/MCs/Ag bionic anti-fouling coatings are expected to be widely used in the fields of anti-fouling,anti-icing,anti-fogging,drag reduction,self-cleaning,and antibacterial.展开更多
Diamond coatings possess numerous excellent properties,making them desirable materials for high-performance surface applications.However,without a revolutionary surface modification method,the surface roughness and fr...Diamond coatings possess numerous excellent properties,making them desirable materials for high-performance surface applications.However,without a revolutionary surface modification method,the surface roughness and friction behavior of diamond coatings can impede their ability to meet the demanding requirements of advanced engineering surfaces.This study proposed the thermal stress control at coating interfaces and demonstrated a novel process of precise graphenization on conventional diamond coatings surface through laser induction and mechanical cleavage,without causing damage to the metal substrate.Through experiments and simulations,the influence mechanism of surface graphitization and interfacial thermal stress was elucidated,ultimately enabling rapid conversion of the diamond coating surface to graphene while controlling the coating’s thickness and roughness.Compared to the original diamond coatings,the obtained surfaces exhibited a 63%-72%reduction in friction coefficients,all of which were below 0.1,with a minimum of 0.06,and a 59%-67%decrease in specific wear rates.Moreover,adhesive wear in the friction counterpart was significantly inhibited,resulting in a reduction in wear by 49%-83%.This demonstrated a significant improvement in lubrication and inhibition of mechanochemical wear properties.This study provides an effective and cost-efficient avenue to overcome the application bottleneck of engineered diamond surfaces,with the potential to significantly enhance the performance and expand the application range of diamond-coated components.展开更多
基金National Natural Science Foundation of China(51764038)Gansu Science and Technology Planning Project(2022JR5RA314,22YF7WA151,22YF7GA138,23CXGA0151)+1 种基金Gansu Provincial Department of Education:Industrial Support Plan Project(2022CYZC-31)Gansu Provincial Association of Science and Technology Innovation Driving Force Project(GXH20230817-10)。
文摘The high-entropy alloy composite coatings AlCu_(2)Ti(NiCr)_(2)-(WC)_(x)(x denotes powder feeding speeds,including 0,25,50,and 75 r/min)were prepared by plasma cladding using a hybrid mode of AlCu_(2)(NiCr)_(2)Ti cable-type welding wire(CWW)and tungsten carbide(WC)powder.The effect of WC powder feeding speed on the microstructure,hardness,and wear properties of the prepared coatings was investigated.The results show that the coatings consist of body-centered cubic main phases and face-centered cubic secondary phases,with carbide reinforcement phases formed due to the addition of WC.The hardness and wear resistance of the coatings are significantly improved compared to the TC11 substrate.When WC powder feeding speed is set at 50 r/min,the coating exhibits optimal wear resistance,with a minimum volume wear rate of 8.5869×10^(-6)mm^(3)·N^(-1)·m^(-1),greatly improving the wear properties of TC11 surface.The coincident CWW-powder plasma cladding provides a viable method for the preparation of highentropy alloy composite coatings with enhanced wear resistance.
基金National Natural Science Foundation of China(52071126)Natural Science Foundation of Tianjin City,China(22JCQNJC01240)+2 种基金Central Guidance on Local Science and Technology Development Fund of Hebei Province(226Z1009G)Special Funds for Science and Technology Innovation in Hebei(2022X19)Anhui Provincial Natural Science Foundation(2308085ME135)。
文摘Co-based alloy coating was prepared on Zr alloy using laser melting and cladding technique to study the difference in the high-temperature oxidation behavior between pure metal Co coatings and Co-T800 alloy coatings,as well as the wear resistance of the coatings.Besides,the effect of changing the laser melting process on the coatings was also investigated.The oxidation mass gain at 800–1200℃and the high-temperature oxidation behavior during high-temperature treatment for 1 h of two coated Zr alloy samples were studied.Results show that the Co coating and the Co-T800 coating have better resistance against high-temperature oxidation.After oxidizing at 1000℃for 1 h,the thickness of the oxide layer of the uncoated sample was 241.0μm,whereas that of the sample with Co-based coating is only 11.8–35.5μm.The friction wear test shows that the depth of the abrasion mark of the coated sample is only 1/2 of that of the substrate,indicating that the hardness and wear resistance of the Zr substrate are greatly improved.The disadvantage of Co-based coatings is the inferior corrosion resistance in 3.5wt%NaCl solution.
基金financial supports from the National Natural Science Foundation of China-Youth Project(51801076)the Provincial Colleges and Universities Natural Science Research Project of Jiangsu Province(18KJB430009)+1 种基金the Postdoctoral Research Support Project of Jiangsu Province(1601055C)the Senior Talents Research Startup of Jiangsu University(14JDG126)。
文摘To solve the problems of deformation,micro-cracks,and residual tensile stress in laser cladding coatings,the technique of laser cladding with Fe-based memory alloy can be considered.However,the process of in-situ synthesis of Fe-based memory alloy coatings is extremely complex.At present,there is no clear guidance scheme for its preparation process,which limits its promotion and application to some extent.Therefore,in this study,response surface methodology(RSM)was used to model the response surface between the target values and the cladding process parameters.The NSGA-2 algorithm was employed to optimize the process parameters.The results indicate that the composite optimization method consisting of RSM and the NSGA-2 algorithm can establish a more accurate model,with an error of less than 4.5%between the predicted and actual values.Based on this established model,the optimal scheme for process parameters corresponding to different target results can be rapidly obtained.The prepared coating exhibits a uniform structure,with no defects such as pores,cracks,and deformation.The surface roughness and microhardness of the coating are enhanced,the shaping quality of the coating is effectively improved,and the electrochemical corrosion performance of the coating in 3.5%NaCl solution is obviously better than that of the substrate,providing an important guide for engineering applications.
基金supported by the Jiangxi Provincial Natural Science Foundation of China(Grant number 20224BAB204049)the National Natural Science Foundation of China(Grant number 52205194)the Fund Project of Jiangxi Provincial Department of Education(Grant number GJJ2200602)。
文摘Conventional Fe-C alloy parts used in mechanical transmission and braking systems exposed to the external environment often suffer from wear and corrosion failures.Surface coating strengthening technologies have been explored to improve the surface performance and prolong service life of these parts.Among these technologies,laser cladding has shown promise in producing Fe-based alloy coatings with superior interfacial bonding properties to the Fe-C alloy substrate.Additionally,the microstructure of the Fe-based alloy coating is more uniform and the grain size is finer than that of surfacing welding,thermal spraying,and plasma cladding,and the oxide film of alloying elements on the coating surface can improve the coating performance.However,Fe-based alloy coatings produced by laser cladding typically exhibit lower hardness,lower wear resistance,corrosion resistance,and oxidation resistance compared to coatings based on Co and Ni alloys.Moreover,these coatings are susceptible to defects such as pores and cracks.To address these limitations,the incorporation of rare-earth oxides through doping in the laser cladding process has garnered significant attention.This approach has demonstrated substantial improvements in the microstructure and properties of Fe-based alloy coatings.This paper reviewed recent research on the structure and properties of laser-cladded Fe-based alloy coatings doped with various rare earth oxides,including La_(2)O_(3),CeO_(2),and Y_(2)O_(3).Specifically,it discussed the effects of rare earth oxides and their concentrations on the structure,hardness,friction,wear,corrosion,and oxidation characteristics of these coatings.Furthermore,the mechanisms by which rare earth oxides influence the coating’s structure and properties were summarized.This review aimed to serve as a valuable reference for the application and advancement of laser cladding technology for rare earth modified Fe-based alloy coatings.
基金Project supported by the National Natural Science Foundation of China(51805285,51605237)the projects of Shandong Province"Youth Innovation Science and Technology Support Plan"(2021KJ026)+1 种基金the Key Research and Development Project of Shandong Province(2018GGX103031)the Natural Science Foundation of Shandong Province(ZR2021ME023)。
文摘The effects of Y_(2)O_(3) on the microstructure, microhardness, wear resistance, high-temperature oxidation resistance, hot corrosion resistance, and electrochemical corrosion behaviour of CoCrFeNiTiNb high entropy alloy coatings formed on Ti-6Al-4V alloy surfaces were studied. The results show that the addition of Y_(2)O_(3) changes the proportion of the phase but does not change its type. The average grain size is only 1/4.7 of that of the high entropy alloy(HEA) coating, and the fine-grained strengthening leads to increases in the microhardness and wear resistance of 21.8% and 26.9%, respectively. The addition of Y_(2)O_(3) enhances the denseness and bonding properties of the oxide and corrosion product layers, reducing the oxidation and hot corrosion rates by 60.3% and 40.3%, respectively. The addition of Y_(2)O_(3) doubles the corrosion resistance which is attributed to the refinement of the grains, the increased proportion of HCP and TiN, and the weakening of galvanic coupling corrosion.
基金financially supported by the National Natural Science Foundation of China(No.51271008)。
文摘(Zr_(0.53)Al_(0.1)Ni_(0.05)Cu_(0.3)Ti_(0.02))_(99)Y_1(at%)coating with amorphous layer of about 180μm thick was prepared on a steel substrate by using laser cladding method.The coating is compact and shows good metallurgical bonding with substrate.The microstructure,microhardness and corrosion behavior along the depth from the coating surface to the substrate were investigated.It is found that a gradient structure consisted of amorphous surface layer,amorphous-crystalline transitional layer and substrate is formed after the laser cladding.The microhardness and corrosion behavior exhibit variation with the microstructural evolution at different depths from the coating surface.The microhardness and corrosion resistance in 3.5 wt%NaCl solution of the amorphous surface layer are comparable to those of the as-cast Zr-based BMG with the same composition,and higher than those of the steel substrate.
基金Funded by the Basic Research Projects in Shanxi Province(No.202103021224183)。
文摘The effect of the gradient content of Co element on the solidification process of Cu-based alloy under deep under cooling conditions was explored.The non-equilibrium solidification structure of the under cooled alloy samples were analyzed.It is found that the rapidly solidified alloy has undergone twice grain refinement during the undercooling process.Characterization and significance of the maximum undercooling refinement structure of Cu60Ni35Co5 at T=253 K were analyzed.High-density defects were observed,such as dislocations,stacking faults networks,and twinning structures.The standard FCC diffraction pattern represents that it is still a single-phase structure.Based on the metallographic diagram,EBSD and TEM data analysis,it is illustrated that the occurrence of grain refinement under high undercooling is due to stress induced recrystallization.In addition,the laser cladding technology is used to coat Co-based alloy(Stellite12) coating on 304 stainless steel substrate;the microstructure of the coating cross-section was analyzed.It was found that the microstructure of the cross-section is presented as columnar crystals,planar crystals,and disordered growth direction,so that the coating has better hardness and wear resistance.By electrochemical corrosion of the substrate and coating,it can be seen that the Co and Cr elements present in the coating are more likely to form a dense passivation film,which improved the corrosion resistance of the coating.
基金Sponsored by the Project to Enhance the Innovative Capabilities of Science and Technology SMEs of Shandong Province(Grant No.2023TSGC0531).
文摘21-4N(5Cr21Mn9Ni4N)is extensively employed in the production of engine valves,operating under severe conditions.Apart from withstanding high-temperature gas corrosion,it must also endure the impact of cylinder explosion pressure.The predominant failure mode of 21-4N valves is abrasive wear.Surface coatings serve as an effective approach to prevent such failures.In this investigation,Laser cladding technology was utilized to fabricate AlCoCrFeNiTi high entropy alloy coatings onto the surfaces of 21-4N valves.According to the findings,the cladding zone has a normal dendritic microstructure,a good substrate-to-cladding layer interaction,and no obvious flaws.In terms of hardness,the cladding demonstrates an average hardness of 620 HV.The hardness has increased by 140%compared to the substrate.The average hardness of the cladding remains at approximately 520 HV even at elevated temperatures.Regarding frictional wear performance,between 400℃and 800℃,the cladding layer exhibits an average friction coefficient of 0.4,with the primary wear mechanisms being abrasive wear,adhesive wear,and a minor degree of plastic deformation.
基金supported by National Natural Science Foundation of China(No.52130509,92166105)the Science and Technology Innovation Program of Hunan Province(No.2021RC3096)145 project and Natural Science Foundation of Hunan Province(No.2023JJ30038).
文摘The key components of engineering machinery frequently failed due to working in the high load and high wear operating envir-onment.And the performance of the Fe-based alloy coatings typically employed need to be improved for fulfilling the service requirements.Herein,a TiC strengthened Fe-based alloy cladding layer,named TiC-Fe coating,was designed and prepared by plasma cladding technology.The frictional wear performance of coating under various loads was tested.The wear morphology of the coating was observed,and its wear mechanism was examined.The results indicated that the TiC-Fe coating was well formed and metallurgically bonded to the Q345C substrate.Its microstructure mainly consisted of Fe-Cr solid solution,α-Fe phase,(Fe,Cr)_(7)C_(3) phase and TiC phase.The coating exhibited an average microhardness of 980 HV0.2,which was about 5.4 times that of the Q345C substrate.The wear mass loss of the TiC-Fe coatings was much smaller than that of the Q345C substrate,which indicated that the wear resistance of the Q345C coating was superior to the substrate,and the wear mechanism of the coating was mainly attributed to the abrasive wear.
文摘The MCrAlY coating has been potential candidate for the parts applied in friction and corrosion conditions, and CNTs (carbon nanotubes) are expected to improve the service performance of coatings owing to high lubrication and low chemical reactivity. In this work, a systematic investigation on the tribological and corrosion properties of CoCrAlYTaSiC-xCNTs coatings deposited by laser melting was analyzed. Results showed that the coatings had good-quality without typical metallurgical defects. The CNTs addition homogenized and refined the microstructure of coating, and also improved the tribological and corrosion properties. As the CNTs content changed from 0 to 4 wt%, the wear rate of coating decreased from 16.23 × 10^(-3) to 7.58 × 10^(-3) mg m^(−1), the jcorr of coating decreased from 4.13 × 10^(-4) to 1.23 × 10^(-4) A cm^(−2), and the Rct values increased from 12.69 to 25.07 Ω cm2.
基金financially supported by the National Natural Science Foundation of China(Nos.52005217 and 51261026)the Basic and Applied Basic Research Fund Project of Guangdong Province in China(Nos.2023A1515012684,2021A1515010523 and 2020A1515110020)+4 种基金the University Research Platform and Research Projects of Guangdong Education Department(No.2022ZDZX3003)the Open Foundation of Guangxi Key Laboratory of Processing for Non-ferrous Metals and Featured Materials(No.2022GXYSOF18)Guanxi Key Laboratory of Information Materials(No.221012-K)the Open Project Program of Wuhan National Laboratory for Optoelectronics(No.2021WNLOKF010)the Fundamental Research Funds for the Central Universities(No.21622110)。
文摘To improve the wear performance of CoCrAlYTa coating,part of the carbon nanotubes(CNTs)chemically reacted with Ta to form reinforcement phase(TaC),while the other CNTs were retained as lubrication phase.Subsequently,the CoCrAlYTa-xCNTs(x=0,1,2,and 4;wt%)composite coatings were prepared by laserinduction hybrid cladding(LIHC),and the microstructure and wear resistance of coatings were systematically analyzed.Results show that the coatings are mainly composed of TaC,y-(Co,Cr)andβ-(Co,Cr)Al.As the CNTs content increases from 0 wt%to 4 wt%,the volume fraction of TaC increases from 13.11 vol%to 16.12 vol%.Meanwhile,the nano-hardness ofγ-(Co,Cr)andβ-(Co,Cr)Al are improved from 7.49 and 9.72 to 9.36 and 11.19 GPa,respectively.As a result,the microhardness of coating increases from HV536.25 to HV 738.16,the wear rate decreases from32.4×10^(-3)to 6.1×10^(-3)mg·m^(-1),and the average friction coefficient decreases from 0.55 to 0.44.The good wear performance of the coating is attributed to the formation of TaC and the existence of remained CNTs lubricant film.
基金financially supported by the National Natural Science Foundation of China(No.52371049)the Young Elite Scientists Sponsorship Program by the China Association for Science and Technology(YESS,No.2020QNRC001)the National Science and Technology Resources Investigation Program of China(Nos.2021FY100603 and 2019FY101404)。
文摘The atmospheric corrosion monitoring(ACM)technique has been widely employed to track the real-time corrosion behavior of metal materials.However,limited studies have applied ACM to the corrosion protection properties of organic coatings.This study compared a bare epoxy coating with one containing zinc phosphate corrosion inhibitors,both applied on ACM sensors,to observe their corrosion protection properties over time.Coatings with artificial damage via scratches were exposed to immersion and alternating dry and wet environments,which allowed for monitoring galvanic corrosion currents in real-time.Throughout the corrosion tests,the ACM currents of the zinc phosphate/epoxy coating were considerably lower than those of the blank epoxy coating.The trend in ACM current variations closely matched the results obtained from regular electrochemical tests and surface analysis.This alignment highlights the potential of the ACM technique in evaluating the corrosion protection capabilities of organic coatings.Compared with the blank epoxy coating,the zinc phosphate/epoxy coating showed much-decreased ACM current values that confirmed the effective inhibition of zinc phosphate against steel corrosion beneath the damaged coating.
基金Funded by the National Natural Science Foundation of China(No.51975540)。
文摘In order to improve the sealing surface performance of gray cast iron gas gate valves and achieve precise molding control of the cladding layer,as well as to reveal the influence of laser cladding process parameters on the morphology and structure of the cladding layer,we prepared the 316L coating on HT 200 by using Design-Expert software central composite design(CCD)based on response surface analysis.We built a regression prediction model and analyzed the ANOVA with the inspection results.With a target cladding layer width of 3.5 mm and height of 1.3 mm,the process parameters were optimized to obtain the best combination of process parameters.The microstructure,phases,and hardness variations of the cladding layer from experiments with optimal parameters were analyzed by the metallographic microscope,confocal microscope,and microhardness instrument.The experimental results indicate that laser power has a significant impact on the cladding layer width,followed by powder feed rate;scan speed has a significant impact on the cladding layer height,followed by powder feed rate.The HT200 substrate and 316L can metallurgically bond well,and the cladding layer structure consists of dendritic crystals,columnar crystals,and equiaxed crystals in sequence.The optimal process parameter combination satisfying the morphology requirements is laser power(A)of 1993 W,scan speed(B)of 8.949 mm/s,powder feed rate(C)of 1.408 r/min,with a maximum hardness of 1564.3 HV0.5,significantly higher than the hardness of the HT200 substrate.
基金Project(2021YFC2801904)supported by the National Key R&D Program of ChinaProject(KY10100230067)supported by the Basic Product Innovation Research Project,China+3 种基金Projects(52271130,52305344)supported by the National Natural Science Foundation of ChinaProjects(ZR2020ME017,ZR2020QE186)supported by the Natural Science Foundation of Shandong Province,ChinaProjects(AMGM2024F11,AMGM2021F10,AMGM2023F06)supported by the Science Fund of Shandong Laboratory of Advanced Materials and Green Manufacturing at Yantai,ChinaProject(KY90200210015)supported by Leading Scientific Research Project of China National Nuclear Corporation(CNNC),China。
文摘WC particles reinforced CoCrFeNiMo high-entropy alloy(HEA)composite coatings were prepared on Cr12MoV steel successfully by laser cladding technology to improve the wear resistance of substrates.Effect of WC content on microstructure and wear property of the composite coatings was studied in detail.Large numbers of carbides with four main types:primary carbide crystals,eutectic structures,massive crystals growing along the periphery of the remaining WC particles and incompletely fused WC particles,were found to exist in the WC/CoCrFeNiMo composite coatings.With increasing WC content,the microhardness of coatings is gradually improved while the average friction coefficients follow the opposite trend due to solid solution strengthening and second phase strengthening effect.The maximum microhardness and minimum friction coefficient are HV_(0.2)689.7 and 0.72,respectively,for the composite coating with 30 wt.%WC,the wear resistance of the substrate is improved significantly,the wear mechanisms are spalling wear and abrasive wear due to their high microhardness.
基金supported by the National Key Re-search and Development Program of China(No.2022YFB4002100)the National Natural Science Foundation of China(No.52271136)the Natural Science Foundation of Shaanxi Province(Nos.2019TD-020 and 2021JC-06).
文摘Proton exchange membrane water electrolysis(PEMWE)is one of the most promising strategies to pro-duce green hydrogen energy,and it is crucial to exploit highly conductive and good corrosion-resistant coatings on bipolar plates(BPs),one of the core components in PEMWE cells.In this work,NbN coatings are deposited on Ti BPs by magnetron sputtering to improve the corrosion resistance and conductivity,for which the critical process parameters,such as the working pressure,partial nitrogen pressure and de-position temperature are well optimized.It is found that the compact microstructure,highly conductive δ-NbN and uniform nanoparticles play a dominant role in the synergistic improvement of the corrosion resistance and electrical conductivity of NbN coatings.The optimized NbN coatings exhibit excellent cor-rosion resistance with the low corrosion current density of 1.1×10^(-8) A cm^(-2),a high potential value of-0.005 V vs.SCE and a low ICR value of 15.8 mΩcm2@1.5 MPa.Accordingly,NbN coatings can be a promising candidate for the development of the low-cost and high-anti-corrosion Ti BPs of PEMWE.
基金financially supported by the National Natural Science Foundation of China(Nos.52371088,52071347,and U20A20233)Guangdong Basic and Applied Basic Research Foundation(No.2023A1515240007)Shenzhen Science and Technology Program(No.KJZD20230923114819041).
文摘Corrosion activities and related accidents are significant issues for marine facilities,leading to considerable economic losses.Waterborne epoxy(EP)coating has been seen as one of the optimal options for corrosion protection due to its stable properties and eco-friendliness(0 g/L volatile organic compounds).Nevertheless,several intrinsic deficiencies require improvement,such as fragile mechanical properties and defects(macro and micro),resulting in the continuous deterioration of comprehensive coating performances.In this work,a novel nanocomposite coating with mechanical enhancement,intelligent self-reporting,and active protection is fabricated by integrating the functionalized and compatible graphene oxide/cerium based metal-organic framework multiscale structure(GO-CeMOF-P/M).Notably,the homogenous dispersion of GO-CeMOF-P/M and its chemical interaction with the polymer matrix effectively reduces the defects resulting from solution volatilizing and enhances the compactness,which boosts the tensile strength(32.1 MPa/8.5%)and dry adhesion force(5.8 MPa)of the coating.Additionally,the controllable responsiveness and release of multiscale nanocomposite within external environments endow intelligent active protection and self-reporting characteristics for the GO-CeMOF-P/M-EP coating,making it especially suitable for a variety of practical marine applications.Furthermore,following immersion of 80 d in the aggressive environment,Zf=0.01 Hz value of GO-CeMOF-P/M-EP coating is 1.2×10^(10)Ωcm^(2),which is 164.4 times larger than that of EP coating(7.3×10^(7)Ωcm^(2)),demonstrating remarkably strengthened anti-corrosion ability.Consequently,by offering an intriguing design strategy,the current work anticipates addressing the inherent deficiencies of EP coating and facilitating its practicality and feasibility in real sea environments.
基金financially supported by the National Natural Science Foundation of China(No.51975137,52205189)。
文摘In this work,a novel surface strengthening strategy for Mg-Li alloys was proposed,called cold spraying assisted high-speed laser cladding.CuAl9 aluminum bronze coating was firstly deposited on Mg-Li alloy by cold spraying,and then CoCrFe_(0.5)Ni_(1.5)Mo_(0.1)Nb_(0.68)eutectic highentropy alloy(EHEA)coating was prepared on the CuAl9 coating utilizing high-speed laser cladding.A gradient coating consisted of in-situ transition region and EHEA layer formed by bidirectional diffusion.The in-situ transition region was composed ofβ-Li,Cu_(2)Mg and Cu_(3)Al_(2)phases.TEM analysis indicated that Cu_(2)Mg and Cu_(3)Al_(2)phases were well matched with theβ-Li matrix phase.The EHEA coating had a nano-lamellar eutectic microstructure with relatively small lamellar-spacing(<100 nm).Metallurgical bonding interfaces formed between the EHEA coating,transition region and Mg-Li substrate.The evolution mechanism of the coating was revealed from the perspectives of mixing enthalpy,atomic radius difference and laser energy distribution.In 3.5 wt.%NaCl solution,the corrosion potential of the EHEA coating(-24 m VSHE)was 1345 m VSHEhigher than that of Mg-Li alloy(-1369 m VSHE),while the corrosion current density of the EHEA coating(3.13×10^(-7)A·cm^(-2))was almost three orders of magnitude lower than that of Mg-Li alloy(1.25×10^(-4)A·cm^(-2)).The wear rate of Mg-Li alloy(1.11×10^(-3)mm^(3)/N·m)was about 36 times higher than that of the EHEA coating(3.05×10^(-5)mm^(3)/N·m).
文摘The present work aims to stabilize the room temperature allotropic transition of ammonium nitrate(AN)particles utilizing a microencapsulation technique,which involves solvent/non-solvent in which nitrocellulose(NC)has been employed as a coating agent.The SEM micrographs revealed distinct features of both pure AN and NC,contrasting with the irregular granular surface topography of the coated AN particles,demonstrating the adherence of NC on the AN surface.Structural analysis via infrared spectroscopy(IR)demonstrated a successful association of AN and NC,with slight shifts observed in IR bands indicating interfacial interactions.Powder X-ray Diffraction(PXRD)analysis further elucidated the structural changes induced by the coating process,revealing that the NC coating altered the crystallization pattern of its pure form.Thermal analysis demonstrates distinct profiles for pure and coated AN,for which the coated sample exhibits a temperature increase and an enthalpy decrease of the room temperature allotropic transition by 6℃,and 36%,respectively.Furthermore,the presence of NC coating alters the intermolecular forces within the composite system,leading to a reduction in melting enthalpy of coated AN by~39%compared to pure AN.The thermal decomposition analysis shows a two-step thermolysis process for coated AN,with a significant increase in the released heat by about 78%accompanied by an increase in the activation barrier of NC and AN thermolysis,demonstrating a stabilized reactivity of the AN-NC particles.These findings highlight the synergistic effect of NC coating on AN particles,which contributed to a structural and reactive stabilization of both AN and NC,proving the potential application of NC-coated AN as a strategically advantageous oxidizer in composite solid propellant formulations.
基金supported by the National Natural Science Foundation of China(Nos.52003148 and 52261045)the State Key Laboratory of Marine Resource Utilization in South China Sea,Hainan University(No.MRUKF2021023)+3 种基金the Key Research and Development Project of Shaanxi Province(No.2023-YBGY-475)the Key Scientific Research Project of Education Department of Shaanxi Province(No.22JS003)the Industrialization Project of the State Key Laboratory of Biological Resources and Ecological Environment(Cultivation)of Qinba Region(No.SXC-2310)the key cultivation project funds of Shaanxi University of Technology(No.SLGKYXM2201).
文摘Polyurethane-fluorinated polysiloxane(PU-^(F)PDMS)with high-strength,high-bonding and low surface en-ergy is synthesized as the matrix,and the PU-^(F)PDMS/MCs/Ag marine anti-fouling coating on the sur-face of imitation crab shells is constructed by assembling butenolide@1,1-stilbene-modified hydrolyzed polyglycidyl methacrylate/graphene oxide microcapsules(Bu@PGMAm/GO MCs)with compact multi-shell structure and Ag nanoparticles(AgNPs)step by step on the PU-^(F)PDMS matrix.The PU-^(F)PDMS/MCs/Ag bionic anti-fouling coatings achieve long-term and stable anti-fouling effect under the combination of robust low-surface-energy PU-^(F)PDMS matrix,steady-state sustained release of butenolide encapsulated by the compact multi-shell,bionic surface formed by the microcapsules and AgNPs,and the release of Ag^(+).The shear strength,tensile strength,and elongation at break of the PU-^(F)PDMS/MCs/Ag are 3.53 MPa,6.7 MPa,and 192.83%,respectively.Its static contact angle and sliding angle are 161.8°and 3.6°,respectively.The antibacterial rate of PU-^(F)PDMS/MCs/Ag against Escherichia coli,Staphylococcus aureus,and Candida albicans can reach 100%.Compared with glass blank,PU,PU-^(F)PDMS,PU-^(F)PDMS/Ag,and PU-^(F)PDMS/MCs,both the adhesion number and coverage percentage of chlorella adhere to PU-^(F)PDMS/MCs/Ag are the minimum values,which are 600 cell mm^(-2) and 1.53%,respectively.After 6 months of marine field test,the primer blank,PU,PU-^(F)PDMS all show different degrees of attachment by shellfish,spirorbis,al-gae and other biofouling,while the PU-^(F)PDMS/MCs/Ag coating is still not covered with biofouling,while the PU-^(F)PDMS/MCs/Ag coatings still exhibit little attachment of marine fouling.The PU-^(F)PDMS/MCs/Ag bionic anti-fouling coatings are expected to be widely used in the fields of anti-fouling,anti-icing,anti-fogging,drag reduction,self-cleaning,and antibacterial.
基金support from the National Natural Science Foundation of China(NSFC)[No.52475464,52475463]National Natural Science Foundation of Jiangsu Province(No.BK20231442)+4 种基金the Fundamental Research Funds for the Central Universities(No.NS2024032)the International Joint Laboratory of Sustainable Manufacturing,Ministry of Education and the Fundamental Research Funds for the Central Universities(No.NG2024007)China Scholarship Council(No.202206830048)the Foundation of the Graduate Innovation Center,Nanjing University of Aeronautics and Astronautics(No.kfjj20200510)Funding for Outstanding Doctoral Dissertation in NUAA(No.BCXJ23-09)。
文摘Diamond coatings possess numerous excellent properties,making them desirable materials for high-performance surface applications.However,without a revolutionary surface modification method,the surface roughness and friction behavior of diamond coatings can impede their ability to meet the demanding requirements of advanced engineering surfaces.This study proposed the thermal stress control at coating interfaces and demonstrated a novel process of precise graphenization on conventional diamond coatings surface through laser induction and mechanical cleavage,without causing damage to the metal substrate.Through experiments and simulations,the influence mechanism of surface graphitization and interfacial thermal stress was elucidated,ultimately enabling rapid conversion of the diamond coating surface to graphene while controlling the coating’s thickness and roughness.Compared to the original diamond coatings,the obtained surfaces exhibited a 63%-72%reduction in friction coefficients,all of which were below 0.1,with a minimum of 0.06,and a 59%-67%decrease in specific wear rates.Moreover,adhesive wear in the friction counterpart was significantly inhibited,resulting in a reduction in wear by 49%-83%.This demonstrated a significant improvement in lubrication and inhibition of mechanochemical wear properties.This study provides an effective and cost-efficient avenue to overcome the application bottleneck of engineered diamond surfaces,with the potential to significantly enhance the performance and expand the application range of diamond-coated components.